Styrene-acrylate latex with high glass transition temperature (T g), low minimum film forming temperature(MFT) and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T g of 20.57 °, MFT of 5.0 °, and good stability, had good stability of film forming.
Similar content being viewed by others
References
Jie Jiang-bin, Liu Yan-hua. VOC Content in the Latex Paint and Indoor Health[J]. China Paint,2004(1):22–23(in Chinese)
Liebscher H. Economic Solutions for Compliance to the New European VOC Directive[J]. Progress in Organic Coatings, 2000,40:75–83
Chen Li-jun, Chen Huan-qin. Approach to Prepare Low VOC Polyurethane(PUR) Coating and Its Application[J].Chemical Materials for Construction, 2004(6):1–4(in Chinese)
Liu Yong-zhen, Chen Peng, Ren Xiu-quan, et al. Emulsion Blending Technology-Formulation of Latex Coatings with Ultra-low VOC Content[J]. Chemical Materials for Construction, 2003(1):10–13( in Chinese)
Sanjani N S, Mahdavian A R, Bataile P. Emulsion Polymerization of Styrene and DEAEMA with a Core-shell Structure[J]. Journal of Applied Polymer Science,2000,78(11):1 977–1 985
Kim S H, Son W K, Kim Y J, et al. Synthesis of Polystyrene/poly(butyl acrylate) Core-shell Latex and Its Surface Morphology[J]. Journal of Applied Polymer Science, 2003, 88(3): 595–601
Zou M X, Wang S J, Huang F Z, et al. Preparation and Characterization of Core-shell Polystyrene and Polymethylsilsesquioxane Structure Latex Particles by Seeded Polymerization[J]. Polymer International, 2006, 55(3): 305–311
Zhang Xin-ya, Tu Wei-ping, Yang Zhuo-ru, et al. Influence of Emulsifying Agent on Stability of Polymeric Latex in Emulsion Polymerization[J]. Technology on Adhesion and Sealing, 2002,23(3):16–19(in Chinese)
Cao Tong-yu, Liu Qing-pu, Hu Jin-sheng. Synthetic Mechanism, Performance and Application of Polymer Latex[M]. Beijing: Chemical Industry Press,1997:199–203( in Chinese)
Okubo M, Yamada A M. Preparation of Composite Particles with Core-shell Structure[J]. Journal of Polymer Science, 1980,203(6): 3 219–3 220
Morguchi N, Tsugaru T, Amiya S. Molecular Design of the Polymer Forming the Complex with MetalI. Design of the Hard-segments of Thermoplastic Elastomers by Using Model Compounds [J]. Journal of Molecular Structure,1999,477: 191–199
Devon M J, Gardon J L, Robert G, et al. Effects of Core-shell Latex Morphology on Film Forming Behavior[J]. Journal of Applied Polymer Science,1990, 39(10): 2 119–2 128
Li Z M, Yang J H, Yu Y Z,et al. Morphological Characterization of the Core-shell Latex Particle by Transmission Electron Microscopy and Image Analysis[J]. Journal of Applied Polymer Science,2003,89(3):855–861
Chen Jie. Analysis of Organic Spectrum[M]. Beijing: Beijing University of Science and Technology Press, 1996:35–37(in Chinese)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, L., Wu, F., Zhuang, X. et al. Preparation of styrene-acrylate latex used in ultralow VOC building internal wall coating. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 23, 65–70 (2008). https://doi.org/10.1007/s11595-006-1065-2
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11595-006-1065-2