Melamine-assisted synthesis of atomically dispersed Fe sites anchored on crumple-rich carbon nanospheres as highly efficient electrocatalysts for oxygen reduction reaction

  • Original Paper
  • Published:
Ionics Aims and scope Submit manuscript

Abstract

Fabrication of an advanced electrocatalyst for oxygen reduction reaction (ORR) is important for the commercialization of fuel cells. Herein, we report an ORR electrocatalyst with Fe atoms evenly distributed on crumple-rich nitrogen-doped carbon (N–C) nanospheres via a simple melamine-assisted pyrolysis strategy, where crumple-rich N–C nanospheres are prepared by a dual soft template approach. The as-obtained Fe–N-C-M electrocatalyst shows a better onset potential (1.02 V vs. RHE) and half-wave potential (0.883 V vs. RHE) in alkaline solution, superior to the commercial Pt/C (0.97 and 0.860 V vs. RHE, respectively). Moreover, the Fe–N-C-M also displays outstanding stability with 80.4% of relative current remained after a 10-h stability test at 0.8 V vs. RHE and remarkable methanol tolerance with 79.2% of relative current sustained after adding 3 M methanol, outperforming the commercial Pt/C (49.4% and 48.5%, respectively). All of these excellent properties are contributed to the unique crumple-rich structure, large specific surface area, and high content of Fe-Nx and pyridinic-N active centers.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

Similar content being viewed by others

References

  1. Chen G, Liu P, Liao Z, Sun F, He Y, Zhong H, Zhang T, Zschech E, Chen M, Wu G, Zhang J, Feng X (2020) Zinc-mediated template synthesis of Fe-N-C electrocatalysts with densely accessible Fe-Nx active sites for efficient oxygen reduction. Adv Mater 32(8):1907399

    Article  CAS  Google Scholar 

  2. Wang H, Yin FX, Liu N, Kou RH, He XB, Sun CJ, Chen BH, Liu DJ, Yin HQ (2019) Engineering Fe-Fe3C@Fe-N-C active sites and hybrid structures from dual metal-organic frameworks for oxygen reduction reaction in H2–O2 fuel cell and Li-O2 battery. Adv Funct Mater 29(23):1901531

    Article  Google Scholar 

  3. Lu S, Zhuang Z (2017) Investigating the influences of the adsorbed species on catalytic activity for hydrogen oxidation reaction in alkaline electrolyte. J Am Chem Soc 139(14):5156–5163

    Article  CAS  PubMed  Google Scholar 

  4. Cong Y, Chai C, Zhao X, Yi B, Song Y (2020) Pt0.25Ru0.75/N-C as highly active and durable electrocatalysts toward alkaline hydrogen oxidation reaction. Adv Mater Interfaces 7 (11):2000310

  5. Wang J, Zhao Y, Setzler BP, Rojas-Carbonell S, Yehuda CB, Amel A, Page M, Wang L, Hu K, Shi L, Gottesfeld S, Xu B, Yan Y (2019) Poly(aryl piperidinium) membranes and ionomers for hydroxide exchange membrane fuel cells. Nat Energy 4:392–398

    Article  CAS  Google Scholar 

  6. Wang L, Peng X, Mustain WE, Varcoe JR (2019) Radiation-grafted anion-exchange membranes: the switch from low- to high-density polyethylene leads to remarkably enhanced fuel cell performance. Energy Environ Sci 12(5):1575–1579

    Article  CAS  Google Scholar 

  7. Zeng L, Peng H, Liu W, Yin J, Xiao L, Lu J, Zhuang L (2020) Extraordinary activity of mesoporous carbon supported Ru toward the hydrogen oxidation reaction in alkaline media. J Power Sources 461:228147

  8. Tatus-Portnoy Z, Kitayev A, Vineesh TV, Tal-Gutelmacher E, Page M, Zitoun D (2020) A low-loading Ru-rich anode catalyst for high-power anion exchange membrane fuel cells. Chem Commun 56(42):5669–5672

    Article  CAS  Google Scholar 

  9. Xue Y, Liu X, Fang J, Wang X, Setzler BP, Zhu W, YanY ZZ (2020) A highly-active, stable and low-cost platinum-free anode catalyst based on RuNi for hydroxide exchange membrane fuel cells. Nat Commun 11(1):5651

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  10. Cong Y, Mccrum IT, Gao X, Lv Y, Miao S, Shao Z, Yi B, Yu H, Janik MJ, Song Y (2019) Uniform Pd0.33Ir0.67 nanoparticles supported on nitrogen-doped carbon with remarkable activity toward the alkaline hydrogen oxidation reaction. J Mater Chem A 7:3161–3169

    Article  CAS  Google Scholar 

  11. Han H, Cong Y, Qin J, Zhai Z, Wang X, Gao R, Zhang G, Guo X, Song Y (2021) Pyrolysis-driven synthesis of nanoscale carambola-like carbon decorated with atomically dispersed Fe sites toward efficient oxygen reduction reaction. Catal Sci Technol 10(21):7160–7164

    Article  Google Scholar 

  12. Wang Q, Sun F, Chen G, Wang J, Peng L, Chen W, Shang L, Zhao J, Waterhouse D, Zhang T, Waterhouse GIN (2021) Molten NaCl-assisted synthesis of porous Fe-N-C electrocatalysts with a high density of catalytically accessible FeN4 active sites and outstanding oxygen reduction reaction performance. Adv Energy Mater 11(9):2100219

    Article  CAS  Google Scholar 

  13. Peng X, Omasta TJ, Magliocca E, Wang L, Varcoe JR, Mustain WE (2019) Nitrogen-doped carbon-CoOx nanohybrids: a precious metal free cathode that exceeds 1.0 W cm2 peak power and 100 h life in anion-exchange membrane fuel cells. Angew Chem Int Ed 58:1046–1051

    Article  CAS  Google Scholar 

  14. Zong L, Liu S, Fan K, Dou S, Xu J, Zhao X, Zhang W, Zhang Y, Wu W, Lu F, Cui L, Jia X, Zhang Q, Yang Y, Zhao J, Li X, Deng Y, Chen Y, Wang L (2021) Ultrafine Fe/Fe3C decorated on Fe-Nx-C as bifunctional oxygen electrocatalysts for efficient Zn-air batteries. J Energy Chem 56:72–79

    Article  Google Scholar 

  15. Rong J, Chen J, Deng T, Wang K, Wang Y (2020) In-situ growth of ZnS/FeS heterojunctions on biomass-derived porous carbon for efficient oxygen reduction reaction. J Energy Chem 47:79–85

    Article  Google Scholar 

  16. Yang W, Liu X, Lv H, Jia J (2021) Atomic Fe & FeP nanoparticles synergistically facilitate oxygen reduction reaction of hollow carbon hybrids. J Colloid Interface Sci 583:371–375

    Article  CAS  PubMed  Google Scholar 

  17. Yang Y, Wu Y, Chen X, Gao T, Zhang J, Xiao D (2020) Self-assembled Fe, N-doped chrysanthemum-like carbon microspheres for efficient oxygen reduction reaction and Zn-air battery. Energy Technol 8(7):2000145

    Article  CAS  Google Scholar 

  18. Shen H, Gracia-Espino E, Ma J, Zang K, Luo J, Wang L, Gao S, Mamat X, Hu G, Wagberg T, Guo S (2017) Synergistic effect between the atomically dispersed active site of Fe-N-C and C-S-C for ORR in acidic medium. Angew Chem Int Ed 56:13800–13804

    Article  CAS  Google Scholar 

  19. Li N, Liu L, Wang K, Niu J, Zhang Z, Dou M, Wang F (2021) Gelatin-derived 1-D carbon nanofiber architecture with simultaneous decoration of single Fe-Nx sites and Fe/Fe3C nanoparticles for efficient oxygen reduction. Chem Eur J 27:1–12

    Google Scholar 

  20. Lee J, Kim JG, Pak C (2021) Electrolyte accessibility of non-precious-metal catalysts with different spherical particle sizes under alkaline conditions for oxygen reduction reaction. J Energy Chem 52:326–331

    Article  Google Scholar 

  21. Zhou Y, Ma D, Foucher AC, Xiong L, Zhang J, Stach EA, Yue Q, Kang Y (2021) Atomic Fe dispersed hierarchical mesoporous Fe-N-C nanostructures for an efficient oxygen reduction reaction. ACS Catal 11(1):74–81

    Article  CAS  Google Scholar 

  22. Mahmood A, Xie N, Zhao B, Zhong L, Zhang Y, Niu L (2021) Optimizing surface N-doping of Fe-N-C catalysts derived from Fe/melamine-decorated polyaniline for oxygen reduction electrocatalysis. Adv Mater Interfaces 8(13):2100197

    Article  CAS  Google Scholar 

  23. Zhao S, Ban L, Zhang J, Yi W, Zhu Z (2020) Cobalt and nitrogen co-doping of porous carbon nanosphere as highly effective catalysts for oxygen reduction reaction and Zn-air battery. Chem Eng J 409(6):128171

    Google Scholar 

  24. Zhang H, Zhou W, Lu XF, Chen T, Lou XW (2020) Implanting isolated Ru atoms into edge-rich carbon matrix for efficient electrocatalytic hydrogen evolution. Adv Energy Mater 10(23):2000882

    Article  CAS  Google Scholar 

  25. Li J, Song Y, Zhang G, Liu H, Wang Y, Sun S, Guo X (2017) Pyrolysis of self-assembled iron porphyrin on carbon black as core/shell structured electrocatalysts for highly efficient oxygen reduction in both alkaline and acidic medium. Adv Funct Mater 27(3):1604356

    Article  Google Scholar 

  26. Gong X, Zhu J, Li J, Gao R, Zhou Q, Zhang Z, Dou H, Zhao L, Sui X, Cai J (2020) Self-templated hierarchically porous carbon nanorods embedded with atomic Fe-N4 active sites as efficient oxygen reduction electrocatalysts in Zn-air batteries. Adv Funct Mater 31(8):2008085

    Article  Google Scholar 

  27. Zheng L, Yu S, Lu X, Fan W, Liao S (2020) 2D bimetallic Zn/Fe-MOF-derived porous carbon nanosheets with high density of single/paired Fe atoms as high-performance oxygen reduction catalysts. ACS Appl Mater Interfaces 12(12):13878–13887

    Article  CAS  PubMed  Google Scholar 

  28. Ye S, Luo F, Xu T, Zhang P, Shi H, Qin S, Wu J, He C, Ouyang X, Zhang Q, Liu J, Sun X (2020) Boosting the alkaline hydrogen evolution of Ru nanoclusters anchored on B/N-doped graphene by accelerating water dissociation. Nano Energy 68:1043

    Article  Google Scholar 

  29. Li R, Wang X, Dong Y, Pan X, Liu X, Zhao Z, Qiu J (2018) Nitrogen-doped carbon nanotubes decorated with cobalt nanoparticles derived from zeolitic imidazolate framework-67 for highly efficient oxygen reduction reaction electrocatalysis. Carbon 132:580–588

    Article  CAS  Google Scholar 

  30. Fan H, Wang T, Gong H, Jiang C, He J, Sun Z, Zhao M, Song L, He J (2021) Heteroatom sulfur-induced defect engineering in carbon nanotubes: enhanced electrocatalytic activity of oxygen reduction reaction. Carbon 180:31–40

    Article  CAS  Google Scholar 

  31. Shi C, Liu Y, Qi R, Li J, Zhu J, Yu R, Li S, Hong X, Wu J, Xi S, Zhou L, Mai L (2021) Hierarchical N-doped carbon spheres anchored with cobalt nanocrystals and single atoms for oxygen reduction reaction. Nano Energy 87:106153

    Article  CAS  Google Scholar 

  32. Li X, Li J, Shi Y, Zhang M, Fan S, Yin Z, Qin M, Lian T, Li X (2018) Rational design of cobalt and nitrogen Co-doped carbon hollow frameworks for efficient photocatalytic degradation of gaseous toluene. J Colloid Interface Sci 528:45

    Article  CAS  PubMed  Google Scholar 

  33. Ren H, Wang Y, Yang Y, Tang X, Peng Y, Peng H, Xiao L, Lu J, Abruña HD, Zhuang L (2017) Fe/N/C nanotubes with atomic Fe sites: a highly active cathode catalyst for alkaline polymer electrolyte fuel cells. ACS Catal 7(10):6485–6492

    Article  CAS  Google Scholar 

  34. Wang Z, Jin H, Meng T, Liao K, Meng W, Yang J, He D, Xiong Y, Mu S (2018) Fe, Cu-coordinated ZIF-derived carbon framework for efficient oxygen reduction reaction and zinc-air batteries. Adv Funct Mater 28(39):1802596

    Article  Google Scholar 

  35. Wu M, Liu R (2020) Pearl necklace fibrous carbon sharing Fe-N/Fe-P dual active sites as efficient oxygen reduction catalyst in broad media and for liquid/solid-state rechargeable Zn-air battery. Energy Technol 8(3):1901263

    Article  CAS  Google Scholar 

  36. Zhu Z, Han J, Cui J, Zho P, Yang Z, Sun H, Li A (2021) Nanostructured tubular carbon materials doped with cobalt as electrocatalyst for efficient oxygen reduction reaction. J Mater Sci 56(13):8143–8158

    Article  CAS  Google Scholar 

  37. Hinokimoto A, Lee J, Izu H, Chen L, Horike S (2020) Metal-carbon composite catalysts by one-step conversion of MOF crystals in a sealed-tube reactor. ACS Appl Energy Mater 3(12):11529–11533

    Article  CAS  Google Scholar 

  38. Wu W, Liu Y, Liu D, Chen W, Song Z, Wang X, Zheng Y, Lu N, Wang C, Mao J, Li Y (2021) Single copper sites dispersed on hierarchically porous carbon for improving oxygen reduction reaction towards zinc-air battery. Nano Res 14(4):998–1003

    Article  CAS  Google Scholar 

  39. Zhou S, Zang J, Gao H, Tian X, Tian P, Song S, Wang Y (2021) Deflagration method synthesizing N, S co-doped oxygen-functionalized carbons as a bifunctional catalyst for oxygen reduction and oxygen evolution reaction. Carbon 181(26):234

    Article  CAS  Google Scholar 

  40. Xu Z, Fan M, Wang J, Zhang F, Lin W, Zhang H (2020) Trace iron-decorated nitrogen/sulfur Co-doped hierarchically porous carbon for oxygen reduction and lithium-sulfur batteries. ACS Appl Energy Mater 3(3):2719–2726

    Article  CAS  Google Scholar 

  41. Zou L, Zhong G, Nie Y, Tan Z, Liao W, Fu X, Pan Z (2021) Porous carbon nanosheets derived from ZIF-8 treated with KCl as highly efficient electrocatalysts for the oxygen reduction reaction. Energy Technol 9:2100035

    Article  CAS  Google Scholar 

  42. Vecchio CL, Serov A, Romero H, Lubers A, Zulevi B, Aricò AS, Baglio V (2019) Commercial platinum group metal-free cathodic electrocatalysts for highly performed direct methanol fuel cell applications. J Power Sources 437:226948

    Article  Google Scholar 

  43. Ou C, Chen H, Wang H, Liao Y, Li R, Liu H (2021) A novel in situ synthesis of nitrogen-doped graphene with excellent electrocatalytic performance for oxygen reduction reaction. Electrochim Acta 3380:138256

    Article  Google Scholar 

  44. Liu H, Zhu S, Cui Z, Li Z, Wu S, Liang Y (2021) Unveiling the roles of multiple active sites during oxygen reduction reaction in Cr2O3@Cr-N-C composite catalyst. J Catal 396:402–408

    Article  CAS  Google Scholar 

Download references

Funding

This work was partially supported by the National Natural Science Foundation of China (Grant No. 51962019 and 21766017), the Natural Research Fund of Gansu Province (Grant No. 20JR5RA441), and the Lanzhou University of Technology Hongliu Characteristic Dominance Major Fund.

Author information

Author notes

  1. Yuanyuan Cong and Guihui Xie contributed equally to this work

Authors and Affiliations

  1. School of Petrochemical Technology, Lanzhou University of Technology, Lanzhou, 730050, Gansu, China

    Yuanyuan Cong, Guihui Xie, Xiangzhi Meng, Haibin Wang, Fanchao Meng, Chunlei Li & Qiuping Zhao

  2. Key Laboratory of Low Carbon Energy and Chemical Engineering of Gansu Province, Lanzhou University of Technology, Lanzhou, 730050, Gansu, China

    Yuanyuan Cong, Guihui Xie, Xiangzhi Meng, Haibin Wang, Fanchao Meng, Chunlei Li & Qiuping Zhao

Authors
  1. Yuanyuan Cong
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Guihui Xie
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Xiangzhi Meng
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Haibin Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Fanchao Meng
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Chunlei Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Qiuping Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Qiuping Zhao.

Ethics declarations

Conflict of interest

The authors declare no competing interests.

Additional information

Publisher’s note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Below is the link to the electronic supplementary material.

Supplementary file1 (DOCX 10506 KB)

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Cong, Y., Xie, G., Meng, X. et al. Melamine-assisted synthesis of atomically dispersed Fe sites anchored on crumple-rich carbon nanospheres as highly efficient electrocatalysts for oxygen reduction reaction. Ionics 27, 5287–5295 (2021). https://doi.org/10.1007/s11581-021-04261-0

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11581-021-04261-0

Keywords

Search

Navigation