Abstract
Nanosized TiO2 particles were prepared by solvothermal method using tetrabutyl titanate as precursor, ethanol and water as solvents, and a facile immobilization method of nanosized TiO2 particles on woven glass fabric was developed. The samples obtained under various preparation conditions were characterized by means of thermo gravimetric analysis (TG) and differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution-transmission electron microscopy (HR-TEM), and Brunauer-Emmett-Teller (BET). The results show that the cube-shape of TiO2 prepared by solvothermal method has good crystallinity of (101) surface, higher thermal stability and large specific surface area. Scanning electron microscopy (SEM) images confirmed that the immobilized TiO2 film was uniformly distributed and clung to the substrate firmly. The photocatalytic activity of the catalysts was tested using photocatalytic oxidation of gaseous benzene. The results show that the TiO2 calcined after solvothermal treatment suffers from lower specific surface area, and hence decreases its photocatalytic activity. The photocatalytic activities of the TiO2 by solvothermal treatment with or without calcination in degradation 400 mg/m3 benzene are 3.7 and 4.1 times as high as catalyst without solvothermal treatment, respectively.
Similar content being viewed by others
References
Tayade R J, Kulkarni R G, Jasra R V. Photocatalytic degradation of aqueous nitrobenzene by nanocrystalline TiO2. Ind Eng Chem Res, 2006, 45: 922–927
Hu Y, Xu J J, Yuan C W, et al. A single TiO2-coated side-glowing optical fabric for photocatalytic wasterwater treatment. Chin Sci Bull, 2005, 50(18): 1979–1984
Feng X G, Rong F, Fu D G, et al. Photocatalytic degradation of trace-level of Microcystin-LR by nano-film of titaniumdioxide. Chin Sci Bull, 2006, 51(10): 1191–1198
Zuo G, Cheng Z, Chen H, et al. Study on photocatalytic degradation of several volatile organic compounds. J Hazard Mater, 2006, 128: 158–163
Lillo-Ródenas M A, Bouazza N, Berenguer-Murcia A, et al. Photocatalytic oxidation of propene at low concentration. Appl Catal B, 2006, 71: 298–309
Mo J H, Zhang Y P, Yang R. Novel insight into VOC removal performance of photocatalytic oxidation reactors. Indoor Air, 2005, 15(4): 291–300
Yang R, Zhang Y P, Zhao R Y. An improved model for analyzing the performance of photocatalytic oxidation reactors in removing volatile organic compounds and its applications. J Air Waste Manage, 2004, 54: 1516–1524
Zhang Y P, Yang R, Zhao R Y. A model for analyzing the performance of photocatalytic air cleaner in removing volatile organic compounds. Atmos Environ, 2003, 37: 3395–3399
Kolen’ko Y U, Churagulov B R, Kunst M, et al. Photocatalytic properties of titania powders prepared by hydrothermal method. Appl Catal B, 2004, 54: 51–58
Ovenstone J. Preparation of novel titania photocatalysts with high activity. J Mater Sci, 2001, 36: 1325–1329
Inagaki M, Nakazawa Y, Hirano M, et al. Preparation of stable anatase-type TiO2 and its photocatalytic performance. Int J Inorg Mater, 2001, 3: 809–811
Kim D S, Kwak S Y. The hydrothermal synthesis of mesoporous TiO2 with high crystallinity, thermal stability, large surface area, and enhanced photocatalytic activity. Appl Catal A, 2007, 323: 110–118
Kominami H, Kato J, Murakami S, et al. Solvothermal syntheses of semiconductor photocatalysts of ultra-high activity. Catal Today, 2003, 84: 181–189
Kontos A I, Arabatzis I M, Tsoukleris D S, et al. Efficient photocatalysts by hydrothermal treatment of TiO2. Catal Today, 2005, 11: 275–281
Yang J, Mei S, Ferreira J M F. Hydrothermal processing of nanocrystalline anatase films from tetraethylammonium hydroxide peptized titania sols. J Eur Ceram Soc, 2004, 24: 335–339
Yu J G, Zhao X J, Zhao Q N. Effect of surface structure on photocatalytic activity of TiO2 thin films prepared by sol-gel method. Thin Solid Films, 2000, 379: 7–14
Yu J C, Yu J, Ho W, et al. Effect of F doping on the photocatalytic activity and microstructures of nanocrystalline TiO2 powders. Chem Mater, 2002, 14: 3808–3816
Alapi T, Sipos P, Ilisz I, et al. Synthesis and characterization of titania photocatalysts: The influence of pretreatment on the activity. Appl Catal A, 2006, 303: 1–8
Fujihara S, Maedo T, Ohgi H, et al. Hydrothermal routes to prepare nanocrystalline mesoporous SnO2 having high thermal stability. Langmuir, 2004, 20: 6476–6481
Testino A, Bellobono I R, Buscaglia V, et al. Optimizing the photocatalytic properties of hydrothermal TiO2 by the control of phase composition and particle morphology. A systematic approach. J Am Chem Soc, 2007, 129: 3564–3575
Kudryavtaeva S M, Vertegel A A, Kalinin S V, et al. Effect of microstructure on the stability of nanocrystalline tin dioxide ceramics. J Mater Chem, 1997, 7(11): 2269–2272
Zhang J, Li M J, Feng Z C, et al. UV Raman spectroscopic study on TiO2. I. Phase trsnsformation at the surface and in the bulk. J Phys Chem B, 2006, 110: 927–935
Liao D L, Liao B Q. Shape, size and photocatalytic activity control of TiO2 nanoparticles with surfactants. J Photoch Photobio A, 2007, 187: 363–369
Cho C H, Han M H, Kim D H, et al. Morphology evolution of anatase TiO2 nanocrystals under a hydrothermal condition (pH=9.5) and their ultra-high photo-catalytic activity. Mater Chem Phys, 2005, 92: 104–111
Author information
Authors and Affiliations
Corresponding author
Additional information
Supported by the National Key Technology R&D Program of China (Grant No. 2006BAJ02A08) the Natural Science Foundation of Zhejiang Province (Grant No. Y50596) and the Hangzhou Science & Technology Development Program (Grant No. 20061133B27)
About this article
Cite this article
Wu, Z., Gu, Z., Zhao, W. et al. Photocatalytic oxidation of gaseous benzene over nanosized TiO2 prepared by solvothermal method. Chin. Sci. Bull. 52, 3061–3067 (2007). https://doi.org/10.1007/s11434-007-0456-x
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11434-007-0456-x