Abstract
Zirconium is commonly used as a cladding material for nuclear reactors. The purity of the zirconium material seeks to control reactor efficiency. A novel composite of reduced graphene oxide–grafted polyacrylic acid, malic acid, and trioctylamine (rGO-g-PAA-MA/TOA) was prepared using in situ radical polymerization with gamma radiation at a dose of 25 KGy from a 60Co cell to preconcentrate zirconium Zr(IV) from zircon raffinate. Five distinct rGO-g-PAA-MA/TOA composite compositions were created and evaluated. The best composite composition was 62.95% acrylic acid, 15.8% malic acid, and 15.8% trioctylamine. After 60 min, the sorption reaction reached equilibrium at pH 0.35 and 20 °C. The pseudo nth order indicated that the order of the sorption reaction was 1.8476. The Elovich model and Dubinin-Radushkevich model controlled the kinetic mechanism and adsorption isotherm of the sorption reaction, respectively; based on estimated regression plots and quantitatively with three different error functions: coefficient of determination (R2), chi-square statistic (χ2), and corrected Akaike information (AICc). The adsorption capacity of rGO-g-PAA-MA/TOA was 75.06 mg g−1. Exothermic reaction and spontaneous sorption took place. Using 2 M H2SO4, 98% of the zirconium was efficiently desorbed. The separation of contaminated Ti(IV) from desorbed Zr(IV) by raising pH to 2.5 through hydrolysis and ZrO2 formation.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Zirconium is only found in its compounds in the IV oxidation state, and its properties are similar to those of titanium (IV). Zr(IV) and ZrO2+ ions exist in HNO3 and HC1O4 solutions and polymerize as zirconium can be formed with the fluoride ion, ethylene diamine tetraacetic acid, and hydroxy acids (Ali 2022). Zirconium has excellent thermal and mechanical properties, which make it suitable for many different applications like painting, glazes, dyes in the ceramic industry, refractory materials, smelting molds, and organic catalysts (Biswas et al. 2012; Rajmane et al. 2006). In addition to its application in the nuclear industry as a covering material for the fuel rods in nuclear reactors due to its low neutron capture cross-section, some zirconium compounds, such as zirconium phosphate and zirconium silico-tungstate, could be used to remove uranium from nuclear waste solutions (Ali 2018; Eliwa and Mubark 2021). Due to all of these applications in various fields, scientists are looking for various chemical techniques for extracting zirconium from its concentrates.
In nature, zirconium metal exists in two minerals: zircon (ZrSiO4) and baddeleyite (ZrO2) (Wang and Lee 2016; Wang et al. 2013). The zircon mineral is widely found in the ground along with igneous, metamorphic, and sedimentary rocks, as well as heavy residual rocks or beach sand. It should be separated from these admixtures using wet gravity concentration, followed by magnetic and electrostatic separation (Abdel-Rehim and Bakr 2016). For extracting ZrO2 from zircon minerals, the bonds between ZrO2 and SiO2 must be broken either chemically or thermally. Numerous methods were used to separate ZrO2 such as alkaline dissociation (Ma et al. 2020; Lötter et al. 2012), chlorination (Pechishcheva et al. 2018), reduction (Choi and Yoon 2013), hydrothermal treatments (Ianos and Barvinschi 2010; Taylor and Meyer 2005), spray pyrolysis (Rainer et al. 2022), zirconium oxychloride separation by crystallization (Poernomo et al. 2020), and precipitation (Ma et al. 2020; Chen et al. 2015; Ao et al. 2020; Gibot et al. 2020).
Numerous solvent extraction studies were carried out to investigate zirconium extraction from various solutions, such as organic phosphorus compounds such as TBP (Aliakbari et al. 2014), TOPO (Banda et al. 2013), TRPO (trialkylphosphine oxide) (Xu et al. 2012), CYANEX 301 and 302 (Saberyan et al. 2008, 2010), CYANEX 272 (Taghizadeh et al. 2009), CYANEX 923 (Taghizadeh et al. 2011), CYANEX 921 (El Shafie et al. 2014), amines (Lakshmanan et al. 2014), and D2EHPA (Taghizadeh et al. 2009; De Beer et al.2016). All these mentioned solvents showed good results for zirconium recovery. TOA (trioctylamine) especially has been used successfully to extract zirconium (Rajmane et al. 2006; Bhatta et al. 2013). However, the higher TOA concentration consumed, in addition to the contamination of Zr with Hf, is regarded as a weakness in this method. Organic acid media are known to provide better metal separation, possibly due to the high stability of metal–organic acid complexes (Rajmane et al. 2006; Van der Westhuizen et al. 2015). As a result, the authors are forced to look for a more cost-effective technique, such as adsorption to extract zirconium in pure form.
Until now, no papers have been published on the use of organic acids and TOA in a polymeric matrix to extract zirconium from its ore. Scientists became more interested in graphene, nanomaterials and carbon nanotubes as sorbent materials over the last decade (Valcárcel et al. 2008). Among them, graphene is preferred due to its low cost of preparation. Adding graphene to polymeric materials could improve their mechanical, thermal, and chemical properties, as well as their specific surface area (Trikkaliotis et al. 2021; Rostamnia and Pourhassan 2013; Alamgholiloo et al. 2021, 2020).
The current study focuses on the synthesis of a novel polymeric composite reduced graphene oxide–grafted poly acrylic acid, malic acid, and trioctylamine (rGO-g-PAA-MA/TOA) using gamma radiation for zirconium preconcentration and separation from zircon raffinate solution (the remained aqueous solution after solvent extraction). Following Egyptian zircon alkaline fusion and solvent extraction, the investigated composite was contacted with raffinate. The dimensions controlling the preconcentration and separation processes, like acidic media type, pH, adsorbent dose (V/m), zirconium initial concentration, shaking time, and temperature, were investigated. Elution studies were carried out to assess the feasibility of using this composite for zirconium preconcentration and separation. Other factors influencing zirconium elution from loaded adsorbents, such as eluant agent type and concentration, were investigated to choose the optimum parameters for zirconium elution, separation, and refining.
Methodology
The Egyptian Nuclear Materials Authority provides zircon raffinate solution. HCl acid, NaOH, HNO3 acid, and H2SO4 acid were purchased from Merck, Germany. Acrylic acid (AA) with 99% purity was obtained from Elf Chem. Co, France. Loba Chemie India provided 99% pure malic acid (MA). Methylene bis-acrylamide (DAM) and extra-pure graphite powders were provided by Merck, Germany. BDH Chemicals, Ltd., England, produced potassium permanganate (KMnO4) and sodium nitrate (NaNO3). Alpha Co., India, also delivered hydrogen peroxide, while ascorbic acid was obtained from Bratachem Co., Egypt.
Fusion of zircon mineral
S.1 represents the elementary analysis of the zircon ore (Ali 2018). About 250 g of zircon is heated to 650 °C in a stainless steel melting pot with 312 g of NaOH pellets; the resulting smelt is composed of water-soluble sodium silicate (Na2SiO3) and water-insoluble sodium zirconate (Na2ZrO3); this step is demonstrated by Eq. (1) (Ali 2022)
After cooling, sodium silicate was dissolved by mixing the smelt with 4 times its weight with double distilled water and stirred at 60 °C for 2 h. In this step, a large amount of Na2SiO3 was dissolved, and a small amount of Na2ZrO3 was hydrolyzed to hydrated zirconia species Eq. (2). (Ali 2022)
The mixture was filtered on hot, and about 20 g from the solid residual precipitate (Na2ZrO3) was then solubilized in excess conc. HCl to keep pH lower than 1 to avoid zirconium hydrolysis at 90 °C for 2 h as given in following Eq. (3) (Ali 2022) and then directly filtered, yielding zirconium chloride solution with the concentration (12.01 gL−1) and the solid residual, which mainly consisted of unreacted zircon, HfO2, TiO2, Al2O3, ThO2, and H2SiO3 (Mohamed and Daher 2002).
Preparation of zirconium working solutions
Previously (Ali 2022; Bhatta et al. 2013), the prepared chloride solution was solvent extracted, the raffinate (aqueous remained solutions from a previous work) about 1 L was collected, and its zirconium content was determined and precipitated by ammonia solution. To prepare the required working concentrations, the precipitate was dried and divided before being dissolved in various acids such as conc. HCl and HNO3 to determine the best suitable working media.
Preparation of (rGO-g-PAA-MA/TOA) sorbent
The prepared graphene oxide by the Hummers process (Zaaba 2017) was used as a precursor for the production of reduced graphene oxide (rGO). One gram of GO was reduced by 10 g of ascorbic acid to produce rGO (Andrijanto et al. 2016). Five different monomer compositions of rGO-g-PAA-MA/TOA composites are prepared (Table 1). A total of 0.1 g of rGO was dispersed in 20 mL distilled water and acrylic acid (AA) and magnetically stirred for 2 h at 20 °C, labeled mixture 1. Acrylic acid and 1 mL of trioctylamine were mixed in another 20 mL of distilled water and labeled mixture 2 after stirring for 2 h. Another 10 mL of distilled water was labeled solution 3; mixture of acrylic acid and L-malic acid was mixed and magnetically stirred for 2 h. Finally, with vigorous stirring, mixture 1 was added dropwisely to mixture 2 and then to mixture 3. MBA, a cross-linker was added, and the entire mixture was ultrasonically treated to form a homogeneous solution. S.2 illustrates a suggested mechanism of the polymerization process of rGO-g-PAA-MA/TOA.
Instruments
A Bomen Miclson FT-IR spectrophotometer, model MB157 from Canada, was used to identify the active functional groups in rGO-g-PAA-MA/TOA composites. The crystalline phase structure was examined using Shimadzu X-ray diffraction (XRD) (model XD-Dl, Kyoto, Japan) with a diffraction angle (θ) range of 4–70°. For SEM and EDX mapping, a JEOL JSM-5400 (SEM, FEI Quanta FEG-250, and EDX) was used. Transmission electron micrograph image (TEM), type JEM2100, Jeol.s.b (Japan), is used to recognize the surface morphology and grain size of the prepared samples. A pore-size chromatech 9320 from the USA was used to calculate pore size distribution and porosity. The particle size is measured by Zetasizer Nano Zs, Malvern (UK), through the dynamic light scattering (DLS) method. BET surface area was measured according to the nitrogen BET (Brunauer–Emmett–Teller) adsorption technique in a surface area analyzer (Nova 3200 series, Micrometrics) (USA). Samples were degassed under a vacuum at 40 °C/4 h using the alizarin red S method; zirconium was analyzed in all aqueous phases (Pechishcheva et al. 2018; Elshehy 2011). The absorbance of the formed zirconium alizarin complex was measured at 520 nm against appropriate standard solutions using a Lambda 3 UV/VIS spectrophotometer (PerkinElmer, USA). The elementary concentration of leach liquor of zircon raffinate before, after sorption, and after desorption was measured by optical emission spectrometer with inductive coupled plasma (Prodigy Axial high dispersion ICP-OES model, USA).
Batch experiments
Several influencing factors on the adsorption process were investigated. Media selection, solution pH, shaking time, initial zirconium concentration, adsorbent dose (V/m), and temperature were all considered. The adsorption experiments were repeated twice and sometimes three times by shaking 0.1 g sample portions of the prepared composite with 10 mL of zirconium concentrations ranging from 200–2000 mg L−1, pH ranging from 0.1 to 0.5, and at different temperatures [(20–60) ± 2] °C, and the samples were taken at predetermined intervals. Following treatment, the solid phases were separated using Whatmann filter paper (no. 40), and the amount of zirconium in the filtrate was determined using the alizarin red method. The adsorbed zirconium or uptake was calculated by dividing the difference between the initial and the residual concentrations in the solution by the mass of the adsorbent. The adsorption efficiency (% A) is determined as Zr(IV) adsorption percentage relative to its initial concentration of the system using Eq. (4) (Dakroury et al. 2021; Dolatyari et al. 2016).
Amount sorbed qe (mg g−1) was calculated using Eq. (5)
where qe (mg g−1) is the amount of the zirconium adsorbed per unit mass of adsorbent. Co and Ce are the initial and equilibrium (or at any time) ion concentration (mg L−1), respectively, V is the volume of the solution per liter, and m is the mass (g) of the adsorbent.
Zirconium desorption from loaded composite
Elution experiments were performed on loaded composite, in a 50-mL beaker, and 20 mL of eluant and 0.1 g of loaded composite were shaken vigorously using a magnetic stirrer for 24 h at 20 °C. A test portion of the aqueous samples was removed by pipette for analysis. The controlling factors of the elution process were investigated in detail, including eluant type and eluant concentration. The elution efficiency (%) was calculated using Eq. (6) (Ali et al.2022).
where Caq is related to the concentration of zirconium within the aqueous phase and Cs is the concentration of zirconium within the composite.
Kinetic and isothermal modeling
The interaction between rGO-g-PAA/MA/TOA and zirconium could be discussed through studying time transient models and equilibrium adsorption models. Pseudo-1st order, pseudo-2nd order, the Elovich, intraparticle diffusion models, and pseudo-nth order were chosen for time transient models. Langmuir, Freundlich, and Dubinin-Radushkevich were selected for adsorption isotherm models. The non-linear regression was used to examine the selected applied models. S.3 includes non linear equations for the selected models. The best fit models were recognized qualitatively by residual error plots and quantitatively by three error functions: coefficient of determination (R2), chi-square statistic (χ2), and corrected akaike information (AICc). S.4 includes the equation formula for the quantitative applied error functions. The best fitting model was accompanied by a maximum value of R2 or minimum values of χ2 and AICc.
Thermodynamic studies
Thermodynamic studies for zirconium sorption onto rGO-g-PAA-MA/TOA composite were conducted by considering four different temperatures (293, 303, 313, and 323 K), where all other key parameters (e.g., solution pH, sorbent concentration, and V/m ratio) were kept constant. Thermodynamic parameters, such as change in Gibbs energy (ΔG, kJ·mol−1), change in enthalpy (ΔH, kJ·mol−1), and change in entropy (ΔS, kJ mol−1·K−1), at the selected temperatures were calculated applying following Eqs. (7) and (8):
where R represents the general gas constant (8.314 JK−1 mol−1), T represents the absolute temperature (K), and Kc represents the sorption equilibrium constant.
Results and discussion
Characterization of rGO-g-PAA/MA/TOA Sorbent
FTIR analysis
The graphene oxide (GO) FTIR spectrum in Fig. 1a investigates various oxygen derivative functional groups of GO such as O–H, C = O and C–O–C, as assigned by a strong wide peak at 3427 cm−1,1720 cm−1, and C–O–C, deformation by vibrations in epoxy groups (El-Shazly et al. 2022). After reduction of GO into rGO, the same functional groups were present, but the intensity of the oxygen derivatives functional groups decreased. Figure 1b depicts rGO-g-PAA/MA/TOA composite and loaded rGO-g-PAA/MA/TOA with Zr(IV), with the functional groups assigned. The integration of the O–H stretching vibrations of the grafted PAA with the N–H stretching vibrations of the TOA matrix results in a broadened absorption band at 3435 cm−1. The peak at 1733 cm−1 belongs to stretching, vibration of COO−. The two bands at 1461 cm−1 and 1386 cm−1 correspond to scissors and bending vibrations of CH2 and CHCO (Alvarez-Gayosso et al. 2015), respectively. The bands at 1633 cm−1 and 1230 cm−1 were related to the − OH bending of the neighboring carboxyl group. The peaks of C–H symmetrical and asymmetrical stretching of CH2 and CH3 composite are obtained at 2960 cm−1 and 2929 cm−1, where the vibration band at 884 cm−1 related to C–O–C deformation vibrations in the epoxy groups of rGO (Sieradzka et al. 2021). After Zr loading onto rGO-g-PAA/MA/TOA composite, some noticeable differences have been observed in the intensity of bands. Namely, the peak at 3437 cm−1, corresponding to the stretching vibrations of –OH and –NH2, became broader and of lower intensity, indicating these groups were involved in coordination of Zr(IV) ions. Disappearing of OH band at 1633 cm−1 and 1230 cm−1 and COO− at 1730 cm−1 with a new high sharp intense band at 1403 cm−1 belongs to binding of Zr(IV) to OH− and COO− (Mizuguchi et al. 1997).
FT-IR of a GO (El-Shazly et al.2022) and rGO and b rGO-g-PAA-MA/TOA composite and Zr(IV) loaded onto rGO-g-PAA-MA/TOA composite
Morphology investigations
Figure 2a reveals a rough, fractured, and randomly aggregated structure due to high cross-linking density of the rGO-g-PAA-MA/TOA composite (Czarnecka and Nowaczyk 2020). The surface particles are irregular in size as the hydrogen bonds between grafted AA and TOA lead to roughness in the surface (Li et al. 2021). The roughness surface guarantees reasonable sorption efficiency (Leiva et al. 2021). After Zr(IV) loading, Fig. 2b, the surface morphology became compactly packed and accumulated, with no discernible voids, indicating that Zr(IV) cations were entrapped via the active sites of rGO-g-PAA-MA/TOA. This was confirmed by the EDX mapping of loaded rGO-g-PAA-MA/TOA investigated in Fig. 2c where Zr, Ti was existed in addition to C, O the main elementary constituent of the composite. The presence of Ti is owed to the impurities in zircon raffinates (Ahmed et al. 2021). Figure 2d, e shows the TEM of rGO-g-PAA-MA/TOA and loaded rGO-g-PAA-MA/TOA where the nano-character was investigated before and after loading due to graphene content.
Porosity measurements and particle size distribution
Regarding to Fig. 3a–c, the BET adsorption isotherm of rGO, rGO-g-PAA-MA/TOA composite, and loaded rGO-g-PAA-MA/TOA composite suggesting type IV isotherm means mono-Zr(IV) molecule sorption. The hysteresis loops of type H3, characteristics of the mesoporous material with slit-shape pores or wedge-shaped pores according to IUPAC classification (Xu et al. 2020; Andrianainarivelo 2020) and monolayer formation, is beginning at low pressures, and multilayer formation occurs at medium pressure. The BET surface area was measured for rGO, rGO-g-PAA-MA/TOA composite, and loaded rGO-g-PAA-MA/TOA composite (0.2 g of the sample degassed at 40 °C). The BET surface area of rGO-g-PAA-MA/TOA composite was 4.56 m2 g−1 with meso-pore size. After loading, the specific surface area decreases to 3.76 m2 g−1 with meso-pore size due to the diffusion of Zr(IV) ions to pores. Pore size of rGO decrease after grafting to the polymeric matrix means that the composite material is much more selective (Andrianainarivelo 2020), while both the pore size and monolayer coverage (Vm) of rGO-g-PAA-MA/TOA composite decrease after loading of Zr(IV) as shown in Table 2 and depicted in Fig. 3d, e, g confirming sorption process.
Porosity measurements provide information about sorption efficiency. The average pore diameter of 139.5 nm represents macropore size (> 50 nm). These macropores enhance sorption and desorption efficiencies (Dakroury et al. 2022).
Only open pores play a role in the sorption process. Comparing apparent density and bulk density can provide insight into the extent of the open pores in the composite. All porosity measurements of the rGO and rGO-g-PAA-MA/TOA composite are shown in Table 2. A high percentage of porosity is compatible with roughness structure in the surface investigation of SEM results. After Zr(IV) loading onto rGO-g-PAA-MA/TOA composite, a decrease in total pore area, average pore diameter, and porosity was observed due to pore blockage with the larger Zr size species (Ali et al. 2011). The particle size of rGO, rGO-g-PAA-MA/TOA composite, and Zr loading onto rGO-g-PAA-MA/TOA composite is depicted in Fig. 3h–j where the average particle size increased after sorption of Zr onto rGO-g-PAA-MA/TOA.
X-ray diffraction
The structural phases of GO, rGO, rGO-g-PAA-MA/TOA composite, and Zr-loaded rGO-g-PAA-MA/TOA composite are depicted in Fig. 3k. A characteristic wide diffraction peak at 2 θ = 14.4° increasing the distance between fields in the graphene oxide (6.146 A°) is due to the presence of oxygen functional groups and water molecules into the carbon layer structure. After reduction of GO by ascorbic acid, the rGO structure became more regular. The characteristic diffraction peak of rGO at 2 θ = 24.3° with decreasing distance between layers (3.659 A°) referred to remaining oxygen functional groups (Johra et al. 2014). An amorphous structure assigned for rGO-g-PAA-MA/TOA composite is with a weak and broad diffraction characteristic peak of rGO at 2θ = 25–30° (Cao and Zhang 2015). Famous poor crystalline characteristic peaks for Zr(IV) appeared after Zr loading,at 2θ = 28.71, 31.76°, 35° (Devi and Jayashree 2013) confirming its sorption on the surface of rGO-g-PAA-MA/TOA composite.
Sorption studies
Using the nitrate media and the chloride media, the sorption efficiency (%) and the sorbed amounts (mg g−1) for the five different compositions of the prepared composites were determined. The sorption efficiencies for all the prepared composites in the nitrate media were higher than those in the chloride media. The hard acid Zr(IV) (high charge density) binds to the hard base (Cl−) in the chloride media more than (NO3−) in the nitrate media, according to the (Pearson 1963) rule. So the sorption of Zr(IV) onto rGO-g-PAA-MA/TOA in the nitrate media was easier and higher than that in the chloride media. Table 3 demonstrates that rGO-g-PAA-MA-TOA with composition 62.95% AA had high sorption efficiency toward Zr(IV) when compared to the other prepared composite compositions. So the (rGO-g-PAA-MA/TOA) composite was selected for all sorption experimental studies during this work.
pH impact
In the nitrate media with pH ranging from 0.1 to 0.5, Zr(IV) sorption from zirconium raffinate is shown in Fig. 4a. The results revealed that increasing the pH value from 0.1 to 0.3 resulted in an increase in sorption efficiency, which was slightly affected by varying the pH within 0.3–0.5 range. Figure 4b depicts the speciation diagram for Zr at pH ranges 1–12 using Hydra/Medusa chemical equilibrium software (Puigdomenech 2013). At pH less than 2, complexion species such as [Zr(OH)3]+, [Zr(OH)2]2+, and [Zr(OH)]3+ and polymeric species [Zr4 (OH)8]8+ and [Zr2(OH)6]2+ predominate. An ionic species, Zr (OH)5, predominates at pH 5. Furthermore, Zr(IV) predominates at pH less than 1 (Christoph et al. 2017).
The stability of the rGO-g-PAA-MA/TOA composite was studied by measuring its solubility in HNO3, HCl, and H2SO4 (Fig. 4c). The results showed that the rGO-g-PAA-MA/TOA composite is chemically stable up to 2 M for all the examined mineral acids; the solubility of rGO-g-PAA-MA/TOA is less than 1%. The rGO-g-PAA-MA/TOA composite is soluble in HCl < HNO3 < H2SO4 at concentrations greater than 2 M. This is in agreement with the order of increasing the strength of acids, HCl < HNO3 < H2SO4. According to Fig. 4d, Zr(IV) began to precipitate at pH greater than 0.4. Thus, pH 0.35 is optimal for Zr(IV) sorption onto rGO-g-PAA-MA/TOA. Zr(IV) of high grade could be adsorbed onto rGO-g-PAA-MA/TOA at pH 0.35 and separated from Hf due to the formation of hafnium-polymeric species that inhibit its sorption onto the organic polymeric composite (Luo et al. 2016).
Time impact
The impact of time within the 5–90-min range and the equilibrium sorption time of zirconium onto rGO-g-PAA-MA/TOA composite at pH 0.35, with an initial zirconium concentration of 1424.7 mg L−1, are shown in Fig. 5a. Because of the presence of free active sites in the rGO-g-PAA-MA/TOA composite, the sorbed amount and sorption efficiency increase rapidly from 5 to 30 min. As these active sites occupied, the rate of sorption reaction slowed down at 30 min and reached equilibrium at 60 min. After the equilibrium time, there is almost no difference in sorption efficiency. A total of 75.06 mg g−1 of zirconium sorbed onto rGO-g-PAA-MA/TOA composite.
Concentration impact
The effect of concentration of zirconium on the extent of the sorption reaction is shown in Fig. 5b. The study of the effect of concentration performed within the range 93–2200 mg g−1 of zirconium. The sorption efficiency decreases with the increase in concentration due to the decrease in the available free active sites (Alghamdi et al. 2019) and the increase in the number of zirconium ions at composite surface due to driving force movement (Igberase et al. 2017). The sorbed efficiency of rGO-g-PAA-MA/TOA toward Zr(IV) decreased from 78.5% at initial concentration 93 mg L−1 to 37% at initial concentration 2200 mg L−1.
Temperature impact
Figure 5c implies a negative effect of the temperature on the sorption reaction at pH 0.35 for the initial concentration of 1424.7 mg L−1. As the temperature increased from 293 to 323 K, the sorption efficiency decreased from 52.7 to 44.5%. This behavior indicated that the Zr(IV) sorption reaction onto the rGO-g-PAA-MA/TOA composite was exothermic.
V/m ratio impact
A total of 0.1 g of rGO-g-PAA-MA/TOA composite is contacted with 10, 20, 25, and 30 mL of zirconium solutions to determine the optimum V/m ratio (Fig. 5d). The sorbed amount of zirconium and sorption efficiency decreased by increasing V/m ratio; this is because the number of free active sites on the rGO-g-PAA-MA/TOA composite is constant, while the number of zirconium ions increased with increasing the solution volume (Igberase and Osifo 2015).
Time transient models
S.5a depicts the non-linear regression fitting plots of pseudo-1st order, pseudo-2nd order, the Elovich, and intraparticle diffusion models. The intraparticle diffusion clarified the external mass transfer of Zr(IV) to the external surface of rGO-g-PAA-MA/TOA composite as well as the internal diffusion of Zr(IV) to active sites. The calculated parameters and the applied error functions for the selected models are listed in Table 4. R2 for the Elovich was the highest one. As a result, the Elovich model provided the best fit model of Zr(IV) sorption onto the rGO-g-PAA-MA/TOA composite. The adsorption rate of the Elovich is higher than the desorption constant. A chemical adsorption or ion exchange mechanism of zirconium onto the rGO-g-PAA-MA/TOA composite was expected. Comparing pseudo-1st-order and pseudo-2nd-order parameters, the qt calculated from pseudo-2nd order was 77.859 mg g−1 and closer to qt (75.06 mg g−1) experiment, confirming that the sorption reaction is regulated by chemisorptions mechanism.
S.5b showed the plot of pseudo-nth order applying Eq. (11), which allows to describe the adsorption processes more accurately than using traditional pseudo-1st-order and pseudo-2nd-order equations. The calculated n order was 1.848; the order of the sorption of Zr(IV) onto rGO-g-PAA-MA/TOA composite was between 1 and 2; this pointed to multiple steps of the sorption reaction mechanism. The lowest values for χ2 and AICC were for pseudo-nth order.
Regarding the residual error in S.5c for the qualitative error function, positive deviations at the initial time are followed by negative ones at intermediate sorption time intervals and positive ones near equilibrium time for the Elovich model. Pseudo-nth-order model gives fairly lowest residuals.
Isotherm modeling
Three famous isotherm models were examined: Langmuir, Freundlich, and Dubinin-Radushkevich. S.5d illustrated the predictive performance for non-linear regression of the examined isotherm models. The calculated parameters and quantitative error functions of the examined models are listed in Table 5. The D-R model has the highest R2 (0.894) and the lowest χ2 and AICC (0.0093 and − 30.696, respectively). Furthermore, the mean free energy E calculated from the parameter in Eq. 16 equals 8.168, confirming that the sorption process was chemisorption in accordance with the time transient results. For S.5e, the residual error of the fitting isotherm model showed that D-R has fairly low error residuals.
Thermodynamic studies
Plotting ln Kc against 1/T gave a straight line. The slope and intercept is used to calculate ∆H° and ∆S° at the selected temperatures. Figure 6a depicts the linear relation between ln Kc against 1/T. The calculated parameters are represented in Table 6. The negative value of the change in enthalpy indicates that the process is exothermic in nature, which can be substantiated by the decrease in sorption efficiency with an increase in temperature. On the other hand, the affinity and the increased randomness or disorders at the adsorbent-adsorbate interface during the period of sorption were corroborated by the positive value of ΔS (Sahmoune 2018). The ∆G° negativity increases with an increase in temperatures which indicates the spontaneity of the sorption reaction at higher temperatures.
a Plot against ln Kc to 1/T for the sorption of Zr(IV) onto rGO-g-PAA-MA/TOA composite. b Speciation diagram of Zr(IV) contaminated with Ti(IV). c Desorption study of Zr(IV) sorbed onto rGO-g-PAA-MA/TOA composite using different eluents. d Desorption study of Zr(IV) sorbed onto rGO-g-PAA-MA/TOA using different concentrations of H2SO4
Separation of zirconium from zircon raffinate
The prepared composite rGO-g-PAA/MA/TOA was used to separate Zr(IV) from zircon raffinate in the nitrate media at pH 0.35 by conducting 0.1 g of the composite with 10 mL of the raffinate liquor for an hour. The initial concentration of the elemental analysis of the zircon raffinate, after sorption onto rGO-g-PAA-MA/TOA composite and after desorption with 2 M H2SO4, was measured by ICP technique, and the results are listed in Table 7.
The result showed that Ti(IV) was contaminated with desorbed Zr(IV), and to separate Ti(IV), the pH was raised to 2.5 where Zr(IV) and soluble cationic species of Zr hydrolyzed with the formation of ZrO2 (Fig. 6b) (Ahmed et al. 2021).
Desorption studies
Desorption experiments were conducted to investigate the possibility of recovering adsorbed zirconium onto rGO-g-PAA-MA/TOA (Fig. 6c). To select the best desorbing agent, different eluents such as H2SO4, HNO3, HCl, and H2O were tested. The desorbing efficiency of zirconium using various eluents was in the order H2SO4 > HNO3 > HCl > H2O. So H2SO4 was selected as an efficient desorbing agent. Despite the fact that the order of Ka was in the order HCl > H2SO4 > HNO3 > H2O, the desorption efficiency order shows that H2SO4 is the best desorbing agent as discussed by Saberyan et al. (2010), while HCl and HNO3 were poor desorbing agents due to the common ion effect of Cl− and NO3−, as HCl and HNO3 were used in fusion of Zircon minerals (Ali et al. 2022) and as pH media, respectively. Figure 6d shows the desorption efficiency of the different concentrations of H2SO4. As the concentration of H2SO4 increased from 0.25 to 2 M, the desorption efficiency increased from 51.81% H2SO4 to 98.6% at H2SO4.
Reusability and mechanism of the sorption reaction
To determine the ability of rGO-g-PAA-MA/TOA for recycling, four adsorption–desorption-adsorption cycles were carried out. The results of this study are investigated in Fig. 7a. The Zr(IV) sorption amount was 75 0.06 mg g−1 after the 1st cycle and decreased to 7.11 mg g−1 after the 4th cycle. It can be inferred that ion exchange or chemisorptions of Zr(IV) onto rGO-g-PAA-MA/TOA play a role in the sorption process (Ali et al. 2022).rGO-g-PAA-MA/TOA composite contains amine (− NH), hydroxyl (− OH), carbonyl (C = O), ether O–C–O, and ester (COO–) active groups, which can bind to Zr(IV) as shown in Fig. 7b for the predication of the sorption mechanism reaction where an electrostatic attraction between these groups and Zr(IV) has already been proposed. Furthermore, in addition to the electrostatic attraction force between Zr(IV) and active site functional groups, the intraparticle diffusion model plot of Zr(IV) into rGO-g-PAA-MA/TOA has a positive intercept of 44.651 mg g−1; thus, the diffusion process may be governed by both film diffusion and intraparticle diffusion together. Regarding to the above findings, the sorption mechanism of Zr(IV) onto rGO-g-PAA-MA/TOA, the preconcentration of Zr(IV) from zircon raffinate mechanism takes place through three routes: (i) movement of Zr(IV) from the solution bulk to rGO-g-PAA-MA/TOA surface, (ii) diffusion of Zr(IV) from boundary layer inside the pores of rGO-g-PAA-MA/TOA, and (iii) sorption of Zr(IV) onto active mentioned functional groups through electrostatic attraction force.
Conclusion
Zirconium ions could be preconcentrated from zircon raffinate by sorption techmique, using a reduced graphene oxide–grafted polyacrylic-malic acid trioctylamine (rGO-g-PAA-MA/TOA) composite. Reduced graphene (rGO), acrylic acid (AA), malic acid (MA), and trioctylamine (TOA) monomers were co-polymerized by exposing the monomers to 25 KGy of cobalt 60 gamma-ray radiations. The sorption parameters were optimized to select pH 0.35, and sorption equilibrium was achieved after 1 h. The sorption efficiency decreased as the temperature increased, resulting in an exothermic sorption reaction. To achieve the sorption mechanism, kinetic modeling and isotherm modeling were used. Non-linear regression and three error functions were used to reduce fitting errors and select the best fitting mechanism for the sorption reaction. Coefficient of determination (R2), chi-square statistic (χ2), and corrected Akaike information (AICc) were used as quantitative error functions, and residual plots were used as qualitative error functions. Thus, the Elovich regulated the reaction kinetic mechanism for kinetic models and the Dubinin-Radushkevich controlled the adsorption isotherms. The capacity for sorption was 75.06 mg g−1. Thermodynamic calculations clarified that the spontaneity of the sorption reaction produced positive entropy. Ninety-eight percent of the sorbed zirconium recovered using 2 M H2SO4 as an efficient desorbing eluent. The research demonstrated the potential of rGO-g-PAA-MA/TOA as a promising composite for the separation of Zr(IV) from Hf(IV) from zircon raffinate.
Data availability
All the data used for this work are publicly available.
References
Abdel-Rehim AM, Bakr MY (2016) Mechanical activation of processing of Egyptian wolframite. In: Neelameggham NR, Alam S, Oosterhof H, Jha A, Dreisinger D, Wang S (eds) Rare metal technology 2015. Springer, Cham. https://doi.org/10.1007/978-3-319-48188-3_22
Ahmed A, Attallah MF, Elsayed A, Hoda R, Massod A (2021) Extraction chromatography and fractional precipitation procedures for production various zirconium grades for industrial and nuclear interest from Egyptian zircon ore. Arab J Nucl Sci Appl 54:63–72. https://doi.org/10.21608/ajnsa.2021.48409.1413
Alamgholiloo H, Rostamnia S, Zhang K, Lee TH, Lee Y-S, Varma RS, Jang HW, Shokouhimehr M (2020) Boosting aerobic oxidation of alcohols via synergistic effect between TEMPO and a composite Fe3O4/Cu-BDC/GO nanocatalyst. ACS Omega. https://doi.org/10.1021/acsomega.9b04209
Alamgholiloo H, Pesyan NN, Mohammadi R, Rostamnia S, Shokouhimehr M (2021) Synergistic advanced oxidation process for the fast degradation of ciprofloxacin antibiotics using a GO/CuMOF-magnetic ternary nanocomposite. J Environ Chem Eng 9(4):105486. https://doi.org/10.1016/j.jece.2021.105486
Alghamdi AA, Al-Odayni A-B, Saeed WS, Al-Kahtani A, Alharthi FA, Aouak T (2019) Efficient adsorption of lead (II) from aqueous phase solutions using polypyrrole-based activated carbon. Materials 12(12):2020. https://doi.org/10.3390/ma12122020
Ali AH (2018) Potentiality of zirconium phosphate synthesized from zircon mineral for uptaking uranium. Sep Sci Technol 53:2284–2296. https://doi.org/10.1080/01496395.2018.1445115
Ali AH (2022) Production of highly purified zirconium oxide from zircon mineral leach liquor using bis-(2-ethylhexyl) phosphate as a promising extractant. Chem Pap 76:6723–6734. https://doi.org/10.1007/s11696-022-02339-1
Ali AH, Dakroury GA, Hagag MS et al (2022) Sorption of some rare earth elements from acidic solution onto poly(acrylic acid–co-acrylamide/16, 16-dimethylheptadecan-1-amine) composite. J Polym Environ 30:1170–1188. https://doi.org/10.1007/s10924-021-02271-7
Ali SS, Zabidi NM, Duvvuri S (2011) Effect of loading on the physicochemical properties of alumina supported Co/Mo bimetallic nanocatalysts. J Appl Sci 11(8):421–1425. https://doi.org/10.3923/jas.2011.1421.1425
Aliakbari M, Saberyan K, Noaparast M, Abdollahi H, Akcil A (2014) Separation of hafnium and zirconium using TBP modified ferromagnetic nanoparticles: effects of acid and metals concentrations. Hydrometallurgy 146:72–75
Alvarez-Gayosso C, Carlos, Canseco A, Estrada M, Palacios-Alquisira R, Hinojosa J, Castaño V (2015) Preparation and microstructure of cobalt (III) poly (acrylate) hybrid materials. Int J Basic Appl Sci 4:255–263. https://doi.org/10.14419/ijbas.v4i3.4172
Andrianainarivelo M (2020) Analysis of specific surfaces of composite material:clays of Madagascar and TiO2. Int J Mater Chem 10(1):1–4. https://doi.org/10.5923/j.ijmc.20201001.01
Andrijanto E, Shoelarta S, Subiyanto G, Rifki S (2016) Facile synthesis of graphene from graphite using ascorbic acid as reducing agent. AIP Conference Proceedings 1725(1). https://doi.org/10.1063/1.4945457
Ao H, Cao W, Hong Y, Wu J, Wei L (2020) Adsorption of sulfate ion from water by zirconium oxide-modified biochar derived from pomelo peel. Sci Total Environ 708:135092
Banda R, Lee H, Lee M (2013) Separation of Zr from Hf in acidic chloride solutions by using TOPO and its mixture with other extractants. J Radioanal Nucl Chem 298:259–264
Bhatta BC, Panda N, Mishra S (2013) Extraction of Zr(IV) from hydrochloric acid with tri-octyl amine and CYANEX 921 in kerosene. Int J Miner Metall Mater 20:823–828. https://doi.org/10.1007/s12613-013-0802-8
Biswas RK, Habib MA, Karmakar AK, Islam MR (2012) Preparation of some useful compounds of zirconium from Bangladeshi zircon. Ind Eng Chem Res 51:13552–13561. https://doi.org/10.1021/ie301412b
Cao N, Zhang Y (2015) Study of reduced graphene oxide preparation by Hummers’ method and related characterization. J Nanomater 2015. https://doi.org/10.1155/2015/168125
Chen L, Zhao X, Pan B, Zhang W, Hua M, Lv L, Zhang W (2015) Preferable removal of phosphate from water using hydrous zirconium oxide-based nanocomposite of high stability. J Hazard Mater 284:35–42
Choi M, Yoon B (2013) Study for production of zirconium sponge by separated-reduction process. In: Marquis F (eds) Proceedings of the 8th Pacific Rim International Congress on Advanced Materials and Processing. Springer, Cham, pp 2313–2316. https://doi.org/10.1007/978-3-319-48764-9_287
Christoph H, Stephan W, Werner K, Jerome K, Andreas CS (2017) Solution species and crystal structure of Zr(IV) acetate. Inorg Chem 56:2473–2480. https://doi.org/10.1021/acs.inorgchem.6b01624
Czarnecka E, Nowaczyk J (2020) Semi-natural superabsorbents based on starch-g-poly (acrylic acid): modification, synthesis and application. Polymers 12(8):1794. https://doi.org/10.3390/polym12081794
Dakroury GA, El-Shazly EAA, Hassan HS (2021) Preparation and characterization of ZnO/chitosan nanocomposite for Cs(I) and Sr(II) sorption from aqueous solutions. J Radioanal Nucl Chem 330:159–174. https://doi.org/10.1007/s10967-021-07935-1
Dakroury GA, Maree RM, El-Shazly EAA et al (2022) Synthesize of poly (acrylamide-co-itaconic/TiO2) nanocomposite for Ce(III) sorption from monazite leachate. J Polym Environ 30:1942–1958. https://doi.org/10.1007/s10924-021-02320-1
De Beer L, Van der Westhuizen DJ, Krieg HM (2016) Solvent extraction and separation of hafnium from zirconium using Ionquest 801. J S Afr Inst Min Metall 116:93–99. https://doi.org/10.17159/2411-9717/2016/v116n1a14
Devi KRS, Jayashree S (2013) Eco friendly nitration of toluene using modified zirconia. Bull Chem React Eng Catal. https://doi.org/10.9767/bcrec.7.3.4154.205-214
Dolatyari L, Yaftian MR, Rostamnia S (2016) Removal of uranium(VI) ions from aqueous solutions using Schiff base functionalized SBA-15 mesoporous silica materials. J Environ Manage 169:8–17. https://doi.org/10.1016/j.jenvman.2015.12.005
El Shafie AS, Daher AM, Ahmed IS, Sheta ME, Moustafa MM (2014) Extraction and separation of nano-sized zirconia from nitrate medium using CYANEX921. Int J Adv Res 2:647–659
Eliwa AA, Mubark AE (2021) Effective sorption of U (VI) from chloride solutions using zirconium silico-tungstate matrix. Int J Environ Anal Chem. https://doi.org/10.1080/03067319.2021.1921762
El-Shazly EAA, Moussa SI, Dakroury GA (2022) Recovery of some rare-earth elements by sorption technique onto graphene oxide. J Sustain Metall 8:715–731. https://doi.org/10.1007/s40831-022-00520-0
Elshehy EA (2011) Extraction of some transition elements using modified silica produced from the leaching wastes of zircon mineral, Ph.D. Thesis
Gibot P, Vidal L, Laffont L, Mory J (2020) Zirconia nanopowder synthesis via detonation of trinitrotoluene. Ceram Int 46:27057–27062. https://doi.org/10.1016/s0304-386x(02)00042-7
Ianos R, Barvinschi P (2010) Solution combustion synthesis of calcium zirconate, CaZrO3, powders. J Solid State Chem 183:491–496. https://doi.org/10.1016/j.jssc.2009.12.015
Igberase E, Osifo P (2015) Equilibrium, kinetic, thermodynamic and desorption studies of cadmium and lead by polyaniline grafted cross-linked chitosan beads from aqueous solution. J Ind Eng Chem 26:340–347. https://doi.org/10.1016/j.jiec.2014.12.007
Igberase E, Osifo P, Ofomaja A (2017) The adsorption of Pb, Zn, Cu, Ni, and Cd by modified ligand in a single component aqueous solution: equilibrium, kinetic, thermodynamic, and desorption studies. Int J Anal Chem 2017:1–15. https://doi.org/10.1155/2017/6150209
Johra FT, Lee J-W, Jung WG (2014) Facile and safe graphene preparation on solution based platform. J Ind Eng Chem 20(5):2883–2887. https://doi.org/10.1016/j.jiec.2013.11.022
Lakshmanan VI, Sridhar R, Jankovic Z, Halim MA (2014) Separation and purification of zirconium with amines from sulphuric acid system: a review. Int Solvent Extract Conf
Leiva E, Tapia C, Rodríguez C (2021) Highly efficient removal of Cu(II) ions from acidic aqueous solution using ZnO nanoparticles as nano-adsorbents. Water 13(21):2960. https://doi.org/10.3390/w13212960
Li B, Wu C, Han Y, Ma X, Luo Z (2021) Preparation of poly (acrylic acid) grafted reduced graphene oxide/polyacrylamide composite hydrogels with good electronic and mechanical properties by in-situ polymerization. J Macromol Sci, Part B: Phys 60:589–602. https://doi.org/10.1080/00222348.2021.1887602
Lötter SJ, Purcelll W, Nel JT, Snyders E (2012) Alternative dissolution of zircon samples and simultaneous analysis of major and trace components. J South Afr Inst Min Metall 112(1):69–76. http://www.scielo.org.za/scielo.php?script=sci_arttext&pid=S2225-62532012000100014&lng=en&tlng=en
Luo X, Wang X, Bao S, Liu X, Zhang W, Fang T (2016) Adsorption of phosphate in water using one-step synthesized zirconium-loaded reduced graphene oxide. Sci Rep 6:39108. https://doi.org/10.1038/srep39108
Ma Y, Stopic S, Wang X, Forsberg K, Friedrich B (2020) Basic sulfate precipitation of zirconium from sulfuric acid leach solution. Metals 10:1099. https://doi.org/10.3390/met10081099
Mizuguchi M, Nara M, Kawano K, Nitta K (1997) FT-IR study of the Ca2+-binding to bovine α-lactalbumin. FEBS Lett 417:153–156. https://doi.org/10.1016/s0014-5793(97)01274-x
Mohammed NA, Daher AM (2002) Preparation of high-purity zirconia from Egyptian zircon: an anion-exchange purification process. Hydrometallurgy 65(2–3):103–107
Pearson RG (1963) Hard and soft acid and bases. J Am Chem Soc 85:3533–3539
Pechishcheva NV, Shunyaev KY, Melchakova OV (2018) Zirconium in modern analytical chemistry. Rev Anal Chem 37(2):20170016. https://doi.org/10.1515/revac-2017-0016
Poernomo H, Sajima, Pusporini ND (2020) Synthesis of zirconium oxychloride and zirconia low TENORM by zircon sand from Landak West Kalimantan. J Phys: Conf Ser 1436:012106. https://doi.org/10.1088/1742-6596/1436/1/012106
Puigdomenech I (2013) Make equilibrium diagrams using sophisticated algorithms (MEDUSA). Inorganic Chemistry. Royal Institute of Technology, Stockholm Sweden. http://www.kemi.kth.se/medusa. https://sites.google.com/site/chemdiagr/
Rainer G, Valery IA, Alexey GK, Leonid VV, Maxim DL, Yuliya EM (2022) Synthesis of submicron, nanostructured spherical powders of Y3Al5O12-phases by the method by ultrasonic spray pyrolysis and investigation of their structure and properties. Ceramics 5:201–209. https://doi.org/10.3390/ceramics5020017
Rajmane MM, Sargar BM, Mahamuni SV, Anuse MA (2006) Solvent extraction separation of zirconium(IV) from succinate media with N-n-octylaniline. J Serb Chem Soc 71:223–234. https://doi.org/10.2298/JSC0603223R
Rostamnia S, Pourhassan F (2013) The SBA-15/SO3H nanoreactor as a highly efficient and reusable catalyst for diketene-based, four-component synthesis of polyhydroquinolines and dihydropyridines under neat conditions. Chin Chem Lett 24(5):401–403. https://doi.org/10.1016/j.cclet.2013.03.020
Saberyan K, Meysami AH, Rashchi F, Zolfonoun E (2008) Proposal of a new Hf(IV)/Zr(IV) separation system by the solvent extraction method. Chin J Chem 26:2067–2072
Saberyan K, Vahedian-Donyaparast P, Noparast M, Zolfonoun E, Nemati A (2010) Solvent extraction of zirconium from zircon leach liquor using triphenylphosphine oxide. Miner Metall Process 27:129–132
Sahmoune M (2018) Evaluation of thermodynamic parameters for adsorption of heavy metals by green adsorbents. Environ Chem Lett 17:697–704. https://doi.org/10.1007/s10311-018-00819-z
Sieradzka M, Ślusarczyk C, Biniaś W, Fryczkowski R (2021) The role of the oxidation and reduction parameters on the properties of the reduced graphene oxide. Coatings 11:166–183. https://doi.org/10.3390/coatings11020166
Taghizadeh M, Ghasemzadeh R, Ashrafizadeh SN, Ghannadi M (2009) Stoichiometric relation for extraction of zirconium and hafnium from acidic nitrate solutions with CYANEX 272. Hydrometallurgy 96:77–80
Taghizadeh M, Ghanadi M, Zolfonoun E (2011) Separation of zirconium and hafnium by solvent extraction using mixture of TBP and CYANEX 923. J Nucl Mater 412:334–337
Taylor DJ, Meyer HM (2005) Wet-chemical synthesis of zirconium oxyfluoride. J Mater Sci 40:2655–2658. https://doi.org/10.1007/s10853-005-2098-1
Trikkaliotis DG, Christoforidis AK, Mitropoulos AC, Kyzas GZ (2021) Graphene oxide synthesis, properties and characterization techniques: a comprehensive review. ChemEngineering 5(3):64. https://doi.org/10.3390/chemengineering5030064
Valcárcel M, Cárdenas S, Simonet BM, Moliner-Martínez Y, Lucena R (2008) Carbon nanostructures as sorbent materials in analytical processes. TrAC - Trends Anal Chem 27:34–43. https://doi.org/10.1016/j.trac.2007.10.012
Van der Westhuizen D, Lachmann G, Krieg H (2015) Solvent extraction separation of zirconium (IV) and hafnium (IV) as chloride and fluoride feedstock solutions using amine extractants. S Afr J Chem Eng 20:31–55
Wang LY, Lee MS (2016) Solvent extraction of Zr(IV) and Hf(IV) from sulfuric acid solutions by acidic extractants and their mixtures with TBP. J Korean Inst Resour Recycl. https://doi.org/10.7844/kirr.2016.25.2.3
Wang LY, Lee HY, Lee MS (2013) Solvent extraction of zirconium and hafnium from hydrochloric acid solutions using acidic organophosphorus extractants and their mixtures with TOPO. Mater Trans 54:1460–1466
Xu C, Wang C, Wang J, Chen J (2012) Third phase formation in the extraction of zirconium(IV) by TRPO in kerosene. Sep Sci Technol 48:183–191
Xu L, Zhang J, Ding J, Liu T, Shi G, Li X, Dang W, Cheng Y, Guo R (2020) Pore structure and fractal characteristics of different shale lithofacies in the Dalong formation in the western area of the Lower Yangtze platform. Minerals 10(1):72. https://doi.org/10.3390/min10010072
Zaaba N (2017) Synthesis of graphene oxide using modified hummers method: solvent influence. Procedia Eng 184:469–477
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
Amr Hamdi Ali, Shaimaa Mohammed Abdo, and Gehan Abel Raman Sadek Dakroury were involved in the initial conception and design of the study. Amr Hamdi Ali, Shaimaa Mohammed Abdo, Gehan and Abel Raman Sadek Dakroury were involved in the data collection. Amr Hamdi Ali, Shaimaa Mohammed Abdo, and Gehan Abel Raman Sadek Dakroury contributed to the methodology and analysis. Amr Hamdi Ali and Shaimaa Mohammed Abdo performed the analysis. Gehan Abel Raman Sadek Dakroury wrote the original draft. All authors have substantially contributed to the study and revision of the paper.
Corresponding author
Ethics declarations
Ethical approval
The authors confirm that this material is the own original work which has not been published elsewhere.
Consent to participate
All of the authors consented to participate in the drafting of this manuscript.
Consent for publication
All of the authors consent to publish this manuscript.
Competing interest
The authors declare no competing interests.
Research involving human participants and/or animals:
Not applicable.
Additional information
Responsible Editor: George Z. Kyzas
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
The authors declare that this manuscript has not been published and not under consideration for publication elsewhere.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ali, A.H., Abdo, S.M. & Dakroury, G.A.R.S. Zirconium preconcentration from zircon raffinate using gamma radiation–induced polymerization of reduced graphene oxide composite. Environ Sci Pollut Res 30, 58330–58345 (2023). https://doi.org/10.1007/s11356-023-26485-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-023-26485-5