Abstract
The present investigation aims to find the combined effect of coarse and fine size particle reinforcement of zircon sand in aluminum alloy LM13 on the wear behavior. The composites are fabricated by varying the reinforcement of fine and coarse size zircon sand particles and compared with the single size reinforcement. Coarse and fine particle zircon sand of 106–125 and 20–32-μm size, respectively, are used in this study. The wear test was carried out on pin-on-disc machine. Microhardness measurement was done for developed composites. Wear track and debris are analyzed by SEM to study the wear mechanism. Line profile and EDS analysis is also done to validate the microstructural results. Study reveals that a combination of 3 % fine and 12 % coarse particle reinforced composite exhibits better wear resistance while 3 % coarse and 12 % fine particle reinforcement decreases the wear resistance. It is also observed that zircon sand particles provide effective nucleation site for the eutectic silicon. Microstructural examination shows globular and finely distributed eutectic silicon in the vicinity of the reinforced particles.
Similar content being viewed by others
References
Kaur, K., Pandey, O.P.: Dry sliding wear behavior of zircon sand reinforced Al–Si alloy. Tribol. Lett. 38, 377–387 (2010)
Das, S., Das, S., Das, K.: Abrasive wear of zircon sand and alumina reinforced Al–4.5 wt% Cu alloy matrix composites—a comparative study. Compos. Sci. Technol. 67, 746–751 (2007)
Roy, R.S., Guchhait, H., Chanda, A., Basu, D., Mitra, M.K.: Improved sliding wear-resistance of alumina with sub-micron grain size: a comparison with coarser grained material. J. Eur.Ceram. Soc. 27, 4737–4743 (2007)
Kaur, K., Pandey, O.P.: Microstructural characteristics of spray formed zircon sand reinforced LM13 composite. J. Alloy. Compd. 503, 410–415 (2010)
Hashim, J., Looney, L., Hashmi, M.S.J.: Metal matrix composites: production by the stir casting method. J. Mater. Process. Technol. 92–93, 1–7 (1999)
Bindumadhavan, P.N., Wah, H.K., Prabhakar, O.: Dual particle size (DPS) composites: effect on wear and mechanical properties of particulate metal matrix composites. Wear 248, 112–120 (2001)
Zhang, Q., Wu, G., Sun, D., Chen, G., Jiang, L.: Microstructure and thermal conduction properties of an Al–12Si matrix composite reinforced with dual sized SiC particles. J. Mater. Sci. 39, 303–305 (2004)
Ahmad, K.R., Jamaludin, S.B., Hussain, L.B., Ahmad, Z.A.: The influence of alumina particle size on sintered density and hardness of discontinuous reinforced aluminum metal matrix composite. J. Teknol. 42(A), 49–57 (2005)
Ozdemir, N., Yakuphanoglu, F.: The effects of particle size and volume fraction of Al2O3 on electronic thermal conductivity of α-Al2O3 particulate reinforced aluminum composites (Al/Al2O3-MMC). Int. J. Adv. Manuf. Technol. 29, 226–229 (2006)
Yılmaz, O., Buytoz, S.: Abrasive wear of Al2O3-reinforced aluminium-based MMCs. Compos. Sci. Technol. 61, 2381–2392 (2001)
Zou, X.G., Miyahara, H., Yamamoto, K., Ogi, K.: Sliding wear behavior of Al–Si–Cu composites reinforced with SiC particles. Mater. Sci. Technol. 19, 1519–1526 (2003)
Surappa, M.K.: Aluminium matrix composites: challenges and opportunities. Sadhana 28, 319–334 (2003)
Amirkhanlou, S., Niroumand, B.: Synthesis and characterization of 356-SiCp composites by stir casting and compocasting methods. Trans. Nonferrous Met. Soc. China 20, 788–793 (2010)
Hashim, J., Looney, L., Hashmi, M.S.J.: Particle distribution in cast metal matrix composites—part I. J. Mater. Process. Technol. 123, 251–257 (2002)
Hashim, J., Looney, L., Hashmi, M.S.J.: Particle distribution in cast metal matrix composites—part II. J. Mater. Process. Technol. 12, 258–263 (2002)
Youssef, Y.M., Dashwood, R.J., Lee, P.D.: Effect of clustering on particle pushing and solidification behavior in TiB2 reinforced aluminium PMMCs. Compos. A 36, 747–763 (2005)
Nakae, H., Wu, S.: Engulfment of Al2O3 particles during solidification of aluminum matrix composites. Mater. Sci. Eng., A 252, 232–238 (1998)
Segurado, J., González, C., Lorca, J.L.: A numerical investigation of the effect of particle clustering on the mechanical properties of composites. Acta Mater. 51, 2355–2369 (2003)
Cruz, K.S., Meza, E.S., Fernandes, F.A.P., Quaresma, J.M.V., Casteletti, L.C., Garcia, A.: Dendritic arm spacing affecting mechanical properties and wear behavior of Al–Sn and Al–Si alloys directionally solidified under unsteady–state conditions. Metall. Mater. Trans. A 41, 973 (2010)
Kaur, K.O., Pandey, P.: Wear and microstructural characteristics of spray atomized zircon sand reinforced LM13 alloy. Mat. Wiss. Werkst. 41(7), 21 (2010)
Chaudhury, S.K., Singh, A.K., Sivaramakrishnan, C.S., Panigrahi, S.C.: Wear and friction behavior of spray formed and stir cast Al–2Mg–11TiO2 composites. Wear 258, 759–767 (2005)
Das, S., Mondal, D.P., Dixit, G.: Correlation of abrasive wear with microstructure and mechanical properties of pressure die-cast aluminum hard-particle composite. Metall. Mater. Trans. A 32, 633–642 (2001)
Das, S., Udhayabanu, V., Das, S., Das, K.: Synthesis and characterization of zircon sand/Al-4.5 wt% Cu composite produced by stir casting route. J. Mater. Sci. 41, 4668–4677 (2006)
Sharma, S.C., Girish, B.M., Somashekar, D.R., Satish, B.M., Kamath, Rathnakar.: Sliding wear behaviour of zircon particles reinforced ZA-27 alloy composite materials. Wear 224, 89–94 (1999)
Bakshi, S.R., Wang, D., Price, T., Zhang, D., Keshri, A.K., Chen, Y., McCartney, P., Graham, D., Shipway, H., Agarwal, A.: Microstructure and wear properties of aluminum/aluminum-silicon composite coatings prepared by cold spraying. Surf. Coat. Technol. 204, 503–551 (2009)
Zhang, J., Alpas, A.T.: Transition between mild and severe wear in aluminium alloys. Acta Mater. 45, 513–528 (1997)
Acknowledgments
The authors are thankful to Armament Research Board (ARMREB), Defence Research and Development Organization (DRDO), India for providing financial support under the letter no. ARMREB/MAA/2008/105 for this study.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, S., Sharma, V., Panwar, R.S. et al. Wear Behavior of Dual Particle Size (DPS) Zircon Sand Reinforced Aluminum Alloy. Tribol Lett 47, 231–251 (2012). https://doi.org/10.1007/s11249-012-9983-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11249-012-9983-y