Abstract
A series of cationic polymers containing quaternary ammonium groups turned out to be powerful catalysts for the CO2-fixation of epoxides under an atmospheric pressure of CO2 at elevated temperature. A variety of differently substituted aromatic and aliphatic epoxides were well tolerated and the polymeric catalysts could easily be recovered by a simple filtration and reused without any loss in catalytic activity.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
1 Introduction
Polyelectrolytes are of fundamental and practical importance since many of them play critical biological functions in nature [1,2,3]. An important subgroup, also known as ionenes, refers to polycations carrying quaternary ammonium groups in the backbone [1, 4,5,6,7,8,9,10]. These polymers are typically synthesized by (1) chain or step polymerization of suitable monomers (e.g. Menshutkin reaction between bis-tertiary amines and activated dihalides, self-polyaddition of aminoalkylhalides) or (2) cationic functionalization of reactive precursor polymers [11, 12]. The practical importance of these macromolecules lies on the large number of applications in daily life, biosciences and industrial processes (e.g. as antibacterial agents or building blocks for the preparation of chromatography stationary phases, symplexes or gels, among other uses) [4, 13, 14].
Recently, we have reported a series of ionene polymers based on N,N′-(p-phenylene)dibenzamide and α,ω-tertiary diamines, where the substitution pattern on the central benzene ring (i.e. ortho-, meta-, para-) in some of these polymers was found to play a key role on the hydrogelation [15], dye uptake [16] and antimicrobial properties [17]. In addition, our groups and others have shown that these versatile polymers can also serve as easily recoverable and reusable phase-transfer catalysts for a variety of different transformations [18,19,20].
Intrigued by the catalytic potential of these highly-functionalized polymers and in continuation of our research focus on multifunctional (chiral) ammonium salt catalysis (for two recent contributions please see Ref. [21, 22]), we became interested in elucidating the catalytic potential of ionenes for more challenging reactions. One transformation that has attracted considerable attention over the last years is the incorporation of CO2 into epoxides to access cyclic carbonates (for selected rather recent reports with different catalyst systems please see Ref. [23,24,25,26,27,28,29,30,31,32,33,34,35,36,37,38,39,40]). This transformation is not only interesting because of the importance of the hereby obtained dioxolanes [41, 42], but it also provides a powerful approach for the utilization of CO2 as a simple one carbon-source for organic transformations [43, 44]. Accordingly, there is a strong interest in the development of new and alternative catalyst systems to carry out such reactions under operationally simple and mild conditions. Some rather recent reports describing the use of functionalized polymers to catalyze the CO2 fixation with epoxides caught our interest [45,46,47]. Considering the previously described potential of ionenes as catalysts [18], we thus now started a program with the focusing on investigating a variety of structurally different polycations bearing ammonium groups A–F for their potential to catalyze the CO2 incorporation into epoxides 1 under an atmospheric pressure of CO2 (Scheme 1).
2 Results and Discussion
It has been well documented that the nature of the halide counter anion can play a crucial role in such ammonium salt catalyzed CO2-incorporation reactions [48, 49] and we thus tested Cl and I-containing polymers A–F for this study. Our investigations started by using simple styrene oxide 1a (R = Ph, Scheme 1) as the epoxide component and carrying out the CO2 fixation under solvent free conditions with an atmospheric pressure of CO2 (by using a simple balloon) (Table 1).
As the developed ionene synthesis provides the chloride salts directly we tested these compounds as catalysts in the beginning (entries 1–15). The first results obtained when using the 1,4-diazabicyclo[2.2.2]octane (DABCO)-based ionenes A were rather disappointing as no dioxolane 2a was formed at 60 °C (entries 1 and 2) and only small amounts were formed after 4 h at 120 °C (entries 3–5). The same rather low reactivity was then observed by using the B-chloride series with a C2 ammonium group linker, (entries 6–8). By using the other polymers C–F under these conditions however, some very interesting observations were made (entries 9–15). With increasing linker length the catalytic performance of the ionene chlorides improved significantly, especially for the 1,4-regioisomers like compound C1,4 (entry 11) and compound D1,4 (entry 13). In both cases catalyst quantities of 0.5–1 mol% allowed us to reach conversions of more than 50% after 4 h reaction time (120 °C), and almost complete conversion when doubling the reaction time in the presence of 0.5 mol% D1,4 (entry 14). In addition, also the cyclohexyl-based polymer E and the pyridinium-based F showed some promising initial catalytic potential (entries 15, 16).
To investigate the influence of the counter anion we next tested the corresponding iodide-based polymers (entries 17–24). These salts were prepared by carrying out a chloride to iodide exchange of the initially used salts (see the supporting information for details). Very interestingly, this lead to a significant improvement in case of the A and B series (entries 17–20), which performed rather slow with chlorides only. On the other hand, those polymers that performed well for the chloride salts already (i.e. C1,4 and D1,4) performed less satisfactory when using the iodides instead (entries 21,22). According to mechanistic studies by others [48, 49], the nucleophilic counter anion plays a crucial role in the initial epoxide opening. The results obtained in our experiments may thus be rationalized by different halide-binding affinities of the different polymers. While for the shorter ionenes it seems reasonable (based on the observed trends in reactivity) that chlorides are more closely bound to the polymer backbone and thus less readily available for the nucleophilic attack of the epoxide (compared to the bigger and more easily polarizable iodide), it seems that iodides are on the other hand more tightly attached to the polymers in those cases where longer linkers between the ammonium groups are present (thus explaining the different trend in reactivity in these cases). Finally, we tested the use of chloride-based ionenes and adding additional NaI to the reaction mixture (entries 25–30). Interestingly, in these experiments again the A and B series performed clearly superior compared to the sole use of the Cl-ionenes (compare entries 25 vs. 4, 26 vs. 5, 27 vs. 3, and 28 vs. 8). It should be noted that NaI alone allows for approximately 10% conversion under these conditions in the absence of any catalyst, thus a synergistic effect of the use of NaI together with the cationic polymers was clearly proven herein. The results are again not that much better for the C and D series (entries 29,30) which is in accordance to the observations made when using the isolated salts alone (the slightly higher yields may be rationalized by some minor catalytic contribution of the excess NaI). Finally, it was also shown that addition of NaBr has more or less no positive effect (entry 31).
Altogether this screening of different cationic polymers revealed a rather complex structure-catalytic activity relationship and with respect to ease of operation we thus decided to carry out further studies (i.e. investigation of the application scope) with the chloride-containing ionene D1,4 under the conditions shown in entry 14. It was also clearly shown that the catalyst can easily be recycled by a simple filtration from the crude reaction mixture and reused for at least four further reactions without any significant loss in activity. As shown in Table 2, the application scope of this reaction is relatively broad and a variety of differently substituted aliphatic and aromatic epoxides performed very well under the catalysis of ionene D1,4. For comparison, the reactions were all run at 120 °C with 0.5 mol% of the catalyst for either 1, 4, or 10 h. The only real limitation was observed when using nitro-styrene oxide (entry 14), which gave almost no cyclic carbonate but instead decomposed totally under the reaction conditions.
![](http://media.springernature.com/full/springer-static/image/art%3A10.1007%2Fs11244-018-0996-0/MediaObjects/11244_2018_996_Figa_HTML.gif)
Mechanistically, the CO2 fixation with epoxides in the presence of nucleophilic catalysts has been discussed and investigated in much detail [23, 40, 48,49,50]. It is commonly believed that the epoxide is activated towards nucleophilic attack by the Lewis- or Bronsted-acidic catalyst and that the nucleophilic source opens the epoxide by addition to the less substituted carbon (for two recent mechanistic investigations see Ref. [40, 49]). As a simple test to investigate whether epoxide opening really occurs preferably via nucleophilic addition to the less-substituted carbon or if maybe a more SN1-type mechanism proceeding via attack to the benzylic position is likely we tested the CO2-fixation with the deuterium-labelled styrene oxides 1a–D2 and 1a–D1 (Scheme 2). It was clearly shown that the di-deuterated 1a–D2 reacts measurably slower than the parent non-deuterated 1a and the epoxide deuterated in the benzylic position (1a–D1). This kinetic isotope effect is therefore a clear hint that nucleophilic attack indeed occurs at the less-substituted carbon, as proposed by others for different catalyst systems [40, 49].
3 Conclusion
A detailed screening of different ionene polymers showed that these cationic polymers are powerful catalysts for the CO2-fixation of epoxides under an atmospheric pressure of CO2. Depending on the polymer backbone, either the corresponding iodides or chlorides turned out to be best-suited for this transformation, illustrating that both, the nature of the multifunctional polymer backbone, and the nucleophilic counter anion play an important role in this transformation. A variety of different epoxides were well tolerated and the polymeric catalysts could easily be recycled by a simple filtration. Some mechanistic insights in this reaction were obtained by using deuterated starting materials, as the observed kinetic isotope effect provides evidence for a mechanism in which the nucleophile preferentially adds to the less hindered epoxide carbon.
4 Experimental
4.1 General Information
1H-, 13C-, and 19F-NMR spectra were recorded on a Bruker Avance III 300 MHz spectrometer, a Bruker Avance 500 MHz spectrometer, and on a Bruker Avance III 700 MHz spectrometer with TCI cryoprobe. All NMR spectra were referenced on the solvent peak. High resolution mass spectra were obtained using a Thermo Fisher Scientific LTQ Orbitrap XL with an Ion Max API Source. MALDI-TOF measurements were collected with a Bruker Autoflex III Smartbeam spectrometer and on an Agilent atmospheric pressure photoionization (APPI) source on an Agilent 6520 quadrupole time-of-flight (QTOF) in the positive mode. The ionenes were synthesized as described recently [15, 17]. The used epoxides were purchased from commercial suppliers and used without further purification. The deuterated epoxides were synthesized as described in the online supporting information.
4.2 General CO2-Fixation Procedure
The reactions were carried out using a Radleys Carousel 12 Plus Reaction Station™. A mixture of 0.2 mmol of the corresponding ionene (based on the repeating monomeric catalytically active units of the ionene) was weighed in a reaction tube (ø 16 mm). After the addition of 4 mmol epoxide and heating the mixture to 120 °C a CO2 atmosphere was provided by using a simple balloon and stirring was started (1000 rpm). After the given reaction time, the mixture was cooled down to room temperature and either filtered using a fritted glass funnel (P 4) to recover the ionenes, or directly flushed through a short column of silica gel (heptanes/EtOAc = 10:1–3:1 as eluent) to afford the literature known cyclic carbonates 2 (further details and analytical data can be found in the SI).
References
Netz RR, Andelman D (2003) Phys Rep 380:1–95
Grosberg AY, Nguyen TT, Shklovskii BI (2002) Rev Mod Phys 74:329–345
Poinsignon C (1989) Mat Sci Eng B B3:31–37
Jaeger W, Bohrisch J, Laschewsky A (2010) Prog Polym Sci 35:511–577
Werner C (2006) Advances in polymer science: polymers for regenerative medicine. Springer, Dresden
Punyani S, Singh H (2006) J Appl Polym Sci 102:1038–1044
Kourai H, Yabuhara T, Shirai A, Maeda T, Nagamune H (2006) Eur J Med Chem 41:437–444
Zelinkin AN, Putnam D, Shastri P, Langer R, Izumrudov VA (2002) Bioconjugate Chem 13:548–553
Bortel E, Kochanowski A, Siniarska B, Witek E (2001) Pol J Appl Chem 44:55–77
Noguchi H (1996) Ionene polymers. In: Salomone JC (ed) Polymeric materials encyclopedia. CRC Press, Boca Raton, pp 3392–3421
Laschewsky A (2012) Curr Opin Colloid Interface Sci 17:56–63
Williams SR, Long TE (2009) Prog Polym Sci 34:762–782
Friedman M (2003) J Agric Food Chem 51:4504–4526
Oha JK, Drumright R, Siegwart DJ, Matyjaszewski K (2008) Prog Polym Sci 33:448–477
Bachl J, Zanuy D, López-Pérez DE, Revilla-López G, Cativiela C, Alemán C, Díaz DD (2014) Adv Funct Mater 24:4893–4904
Dragan ES, Mayr J, Häring M, Cocarta AI, Díaz DD (2016) ACS Appl Mater Interfaces 8:30908–30919
Mayr J, Schlossmann J, Díaz DD (2017) Int J Mol Sci 18:303
Tiffner M, Zielke K, Mayr J, Häring M, Díaz Díaz D, Waser M (2016) ChemistrySelect 1:4030–4033
Morawetz H, Overberger CG, Salamone JC, Yaroslavsky S (1968) J Am Chem Soc 90:651–656
Faria AC, Mello RS, Orth ES, Nome F (2008) J Mol Cat A: 289:106–111
Di Mola A, Tiffner M, Scorzelli F, Palombi L, Filosa R, De Caprariis P, Waser M, Massa A (2015) Beilstein J Org Chem 11:2591–2599
Novacek J, Izzo JA, Vetticatt M, Waser M (2016) Chem Eur J 22:17339–17344
North M, Pasquale R, Young C (2010) Green Chem 12:1514–1539
Lu XB, Darensbourg DJ (2012) Chem Soc Rev 41:1462–1484
Ema T, Miyazaki Y, Koyama S, Yano Y, Sakai T (2012) Chem Commun 48:4489–4491
Castro-Osma JA, North M, Wu X (2016) Chem Eur J 22:2100–2107
Whiteoak CJ, Kielland N, Laserna V, Escudero-Adan EC, Martin E, Kleij AW (2013) J Am Chem Soc 135:1228–1231
Ren WM, Liu Y, Lu XB (2014) J Org Chem 79:9771–9777
Büttner H, Steinbauer J, Werner T (2015) ChemSusChem 8:2655–2669
Alves M, Grignard B, Gennen S, Mereau R, Detrembleur C, Jerome C, Tassain T (2015) Catal Sci Technol 5:4636–4643
Yang H, Wang X, Ma Y, Wang L, Zhang J (2016) Catal Sci Technol 6:7773–7782
Toda Y, Komiyama Y, Kikuchi A, Suga H (2016) ACS Catal 6:6906–6910
Liu S, Suematsu N, Maruoka K, Shirakawa S (2016) Green Chem 18:4611–4615
Tiffner M, Gonglach S, Haas M, Schöfberger W, Waser M (2017) Chem Asian J 12:1048–1051
Kumatabara Y, Okada M, Shirakawa S (2017) ACS Sustain Chem Eng 5:7295–7301
Kaneko S, Shirakawa S (2017) ACS Sustain Chem Eng 5:2836–2840
Sopena S, Martin E, Escudero-Adan EC, Kleij AW (2017) ACS Catal 7:3532–3539
Xue Z, Zhao X, Wang J, Mu T (2017) Chem Asian J 12:2271–2277
Ema T, Yokoyama M, Watanabe S, Sasaki S, Ota H, Takaishi K (2017) Org Lett 19:4070–4073
Xu F, Cheng W, Yao X, Sun J, Sun W, Zhang S (2017) Catal Lett 147:1654–1664
Trost BM, Angle SR (1985) J Am Chem Soc 107:6123–6124
Clements JH (2003) Ind Eng Chem Res 42:663–674
Aresta M, Dibenedetto A, Angelini A (2014) Chem Rev 114:1709–1742
Liu Q, Wu L, Jackstell R, Beller M (2015) Nat Commun 6:5933–5947
Kohrt C, Werner T (2015) ChemSusChem 8:2031–2034
Dai WL, Jin B, Luo SL, Yin SF, Luo XB, Au CT (2013) J CO2 Util 3–4:7–13
Zhong W, Bobbink FD, Fei Z, Dyson PJ (2017) ChemSusChem 10:2728–2735
Kihara N, Hara N, Endo T (1993) J Org Chem 58:6198–6202
Rocha CC, Onfroy T, Pilme J, Denicourt-Nowicki A, Roucoux A, Launay F (2016) J Catal 333:29–39
Calo V, Nacci A, Monopoli A, Fanizzi A (2002) Org Lett 4:2561–2563
Acknowledgements
Open access funding provided by Austrian Science Fund (FWF). This work was supported by the Austrian Science Funds (FWF): Project No. P26387-N28. The used NMR spectrometers at JKU Linz were acquired in collaboration with the University of South Bohemia (CZ) with financial support from the European Union through the EFRE INTERREG IV ETC-AT-CZ program (Project M00146, “RERI-uasb”). We are grateful to Prof. Dr. Markus Himmelsbach (JKU Linz) for support with MS and ion chromatography analysis. We thank Dr. Jürgen Bachl, Dr. Judith Mayr and Mr. Jakob Asenbauer (Universität Regensburg) for repeating the synthesis of some of the polymers. D.D.D. thanks the Deutsche Forschungsgemeinschaft (DFG) for the Heisenberg Professorship Award.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Tiffner, M., Häring, M., Díaz, D.D. et al. Cationic Polymers Bearing Quaternary Ammonium Groups-Catalyzed CO2 Fixation with Epoxides. Top Catal 61, 1545–1550 (2018). https://doi.org/10.1007/s11244-018-0996-0
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11244-018-0996-0