An investigation of the size distribution and phase composition as well an analysis of the Al–Mg–B powder system are performed as a function of the time of mechanical activation in a planetary mill and heat treatment regimes. It is found out that the largest content of the AlMgB14 phase is observed in the materials manufactured from a powder mixture subjected to a 4-hour mechanical treatment and sintered at the temperature 1130°С.
Similar content being viewed by others
References
V. B. Shipilo, et al, Production, Properties and Applications of Diamond and Cubic Boron Nitride Powders (Ed. P. A. Vityaz' [in Russian], Minsk (2003).
J. Haines, J. M. Leger, and G. Bocquillon, Annu. Rev. Mater. Res., 31, No. 1, 1– 23, (2001).
V. I. Ivashchenko et al., J. Appl. Phys., 119, No. 20, 205105 (2016).
J. Chen et al. , Ceramics. Int. 43, No. 15, 12362–12371 (2017).
B. A. Cook et al., Scripta Mater., 42, No. 6, 597–602 (2000).
A. Ahmed et al., Tribology Int., 39, No. 2, 129–137 (2006).
I. A. Zhukov G. V. Garkushin, S. A. Vorozhtsov, et al., Russ. Phys. J., 58, No. 9, 1358–1361 (2015).
A. P. Surzhikov, E. N. Lysenko, A. V. Malyshev, et al., Russ. Phys. J., 55, No. 6, 672–677 (2012).
C. Sauter et al., Ultrason. Sonochem., 15, No. 4, 517–523 (2008).
J. L. Murra, J. Phase Equilibria, 3, No. 1, 60 (1982).
M. L. Whittaker et al., Ceram. Eng. Sci. Proc., 31, No. 5, 239–250 (2010).
V. F. Komarov, M. V. Komarova, A. B. Vorozhtsov, M. I. Lerner, Russ. Phys. J., 55, No. 10, 1117–1122 (2012).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Izvestiya Vysshikh Uchebnykh Zavedenii, Fizika, No. 8, pp. 87–92, August, 2018.
Rights and permissions
About this article
Cite this article
Zhukov, I.A., Ziatdinov, M.K., Dubkova, Y.A. et al. Synthesis of AlMgB14: Influence of Mechanical Activation of Al–Mg–B Powder Mixture on Phase Composition of Sintered Materials. Russ Phys J 61, 1466–1471 (2018). https://doi.org/10.1007/s11182-018-1557-5
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11182-018-1557-5