Abstract
The hot corrosion behaviors of a single crystal (SC) Ni-base superalloy coated with Na2SO4 and 75 wt.% Na2SO4-25 wt.% NaCl mixture were studied in air at 900°C. The results showed that the corrosion productions were laminar structure, porous and easily spalled. And sulfides formed quickly in the deep SC superalloy under the corrosion production. The addition of NaCl into Na2SO4 considerably accelerated the corrosion of the SC superalloy, and the corrosion scale became more porous. The hot corrosion process was explained based on sulfide formation and its subsequent oxidation.
Similar content being viewed by others
References
Li M.H., Sun X.F., Gong S.K., Zhang Z.Y., Guan H.R., Hu Z.Q. (2004). Surface Coatings Technology 176:209
Li M.H., Zhang Z.Y., Sun X.F., Guan H.R., Hu W.Y., Hu Z.Q. (2002). Oxidation of Metals 58:499
Bernier J.S., Levan G., Maniruzzaman M., Sisson R.D. Jr., Bose S. (2003). Surface Coatings Technology 163–164:95
Li M.H., Sun X.F., Gong S.K., Zhang Z.Y., Guan H.R., Hu Z.Q. (2003). Surface Coatings Technology 165:241
Tolpygo V.K., Clarke D.R. (2003). Surface Coating Technology 163–164:81
Li M.H., Sun X.F., Li J.G., Zhang Z.Y., Jin T., Guan H.R., Hu Z.Q. (2003). Oxidation of Metals 59:591
Li M.H., Sun X.F., Jin T., Guan H.R., Hu Z.Q. (2003). Oxidation of Metals 60:195
Deb D., Ramakrishna S. Iyer, Radhakrishnan V.M. (1996). Materials Letters 29:19
Bornstein N.S., Decrescent M.A. (1969). Transactions of the Metallurgical society of AIME 245:1947
Luthra K.L., Worrell W.L. (1978). Metallurgical Transactions A9:1055
Stringer J., Wilcox B.A., Jaffee R.I. (1972). Oxidation of Metals 5:11
Taniguchi S., Shibata T. (1988) Transactions of the Japan Institute Metals 29:658
Goebel J.A., Pettit F.S., Goward G.W. (1973) Metallugical Transactions 4:261
Ting J.M., Lin R.Y. (1989). Oxidation of Metals 32(3/4):225
Reese E., Grabke H.J. (1993). Materials and Corrosion 44:44
Kim A.S., McNallan M.J. (1990). Corrosion 46:746
Nicholls J.R., Leggett J., Andrews P. (1997). Materials Corrosion 48:56
Jianting B., Ranucci D., Picco E., Strocchi P.M. (1982). Proc. Symp. On High Temperature Alloys for Gas Turbines. Reidel, Dordrecht, pp. 805
Elliot P., Tyreman C.J., Prescot R. (1985). Journal of Meterology 37:20
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, M., Sun, X., Hu, W. et al. Hot Corrosion of a Single Crystal Ni-Base Superalloy by Na-Salts at 900°C. Oxid Met 65, 137–150 (2006). https://doi.org/10.1007/s11085-006-9004-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11085-006-9004-3