Abstract
Zinc oxide (ZnO) is a semiconductor compound with a potential for wide use in various applications, including biomaterials and biosensors, particularly as nanoparticles (the size range of ZnO nanoparticles is from 2 to 100 nm, with an average of about 35 nm). Here, we report isolation of novel ZnO-binding peptides, by screening of a phage display library. Interestingly, amino acid sequences of the ZnO-binding peptides reported in this paper and those described previously are significantly different. This suggests that there is a high variability in sequences of peptides which can bind particular inorganic molecules, indicating that different approaches may lead to discovery of different peptides of generally the same activity (e.g., binding of ZnO) but having various detailed properties, perhaps crucial under specific conditions of different applications.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Zinc oxide (ZnO) is a compound widely used in many applications, including construction of solar cells, luminescent materials, and acoustic devices (Goyal et al. 1992; Ezhilvalavan and Kutty 1997; Yu et al. 2005; Shinde et al. 2007). Interestingly, employment of ZnO in biosensors has also been proposed (Gerstel et al. 2006; Park et al. 2009; Tomczak et al. 2009). The possibility to obtain ZnO nanoparticles (i.e., the structures whose at least one dimension is less than 100 nm) significantly broads its practical usefulness (Fan and Lu 2005). It appears that ZnO nanoparticles (which are usually in the size range between 2 and 100 nm, with an average of about 35 nm; Meulenkamp 1998) may be of special interest in biotechnology and nanotechnology (Umetsu et al. 2005; Okochi et al. 2010). In fact, ZnO nanomaterials have been used in sensors, field emission devices, photodetectors, and optical switches (for a review, see Weintraub et al. 2010). Medical applications of ZnO nanoparticles are facilitated due to consideration of ZnO as a safe material, and include anticancer agents, antimicrobial factors, and drug delivery systems (discussed by Li et al. 2008 and Rasmussen et al. 2010). Since ZnO nanoparticles can absorb UV light, they are used in cosmetics, particularly in face or body sunscreen creams (Rasmussen et al. 2010).
The wide use of ZnO nanoparticles stimulated the search for compounds that may specifically bind such structures. In fact, agents that can bind inorganic compounds may be used to build materials with nanoscale precision. Peptides and proteins were demonstrated to be particularly useful in this approach, even when applied to substances not commonly found in biological systems (Brown et al. 2000). Therefore, knowing an extremely high variability of properties of peptides and proteins, and a potential possibility to obtain a peptide that might bind any small molecule of interest, it is reasonable to search for peptides specifically interacting with certain compounds (Seker and Demir 2011). One of the most effective methods in such a search, especially if a target material forms nanoparticles, is screening of peptide libraries (Seker and Demir 2011).
Phage display technique is a method which allows production of various peptides attached to the surface proteins of bacteriophage virions (Castel et al. 2011). This is achieved by genetic engineering of the bacteriophage genome, particularly by fusing genes coding for phage structural proteins with an appropriate DNA fragment, coding for the desired protein or peptide. This may concern either a specific peptide or protein of known functions or a putative one. In the latter case, DNA fragments of randomized sequences can be cloned, and their expression leads to formation of a peptide library, expressed on the bacteriophage surface. Derivatives of phage M13 are among the most widely used vectors in phage display systems (Georgieva and Konthur 2011).
Previously, several ZnO-binding peptides have been reported, which were isolated on the basis of various approaches, including screening of peptide libraries expressed in phage display systems (Kjærgaard et al. 2000; Umetsu et al. 2005; Okochi et al. 2010; Vreuls et al. 2010). Amino acid sequences of these peptides are listed in Table 1. We wanted to probe whether amino acid sequences of ZnO-binding peptides are strictly determined (i.e., the number of possible kinds of ZnO-binding peptides of various sequences is strictly limited) or whether there are many possibilities to form such peptides, whose sequences are significantly different. If the former alternative is true, any new attempts to obtain ZnO-binding peptides should result in obtaining results similar to those published to date. On the other hand, if the latter option is correct, new experiments, differing even slightly in details, should result in isolating peptides which bind ZnO but have amino acid sequences significantly different from those already reported.
Materials and methods
Peptide phage library
In order to isolate novel ZnO-binding peptides, we have employed a peptide phage library that displays a linear 12-mer peptide on the pIII protein of M13KE phage (Ph.D.-12 Phage Display Peptide Library Kit, New England Biolabs, NEB). This system was successfully used previously to find material-specific peptides (Whaley et al. 2000; Chen et al. 2006; Ahmad et al. 2008).
Selection and characterization of bacteriophages presenting ZnO-binding peptides
In order to select bacteriophages presenting ZnO-binding peptides on their surfaces, we have utilized synthetic, physically powdered ZnO (Sigma-Aldrich). Panning procedure was performed according to the Phage Display Manual (NEB). Briefly, 10 mg of ZnO powder were washed six times with the TBST buffer (50 mM Tris–HCl pH 7.5, 150 mM NaCl, 0.1 % Tween-20) to remove any ZnO particles that do not sediment during centrifugation at 4,000 × g for 1 min (which would negatively interfere with phage isolation at later steps of the procedure) and to establish the equilibrium of buffer conditions of the mixture (which is crucial for effective binding of phages to any surface). 10 μL of phage library was incubated with ZnO in 1 mL of the TBST buffer (at final ZnO concentration of 10 mg/mL) for 1 h at room temperature (RT). This incubation time was chosen on the basis of results of preliminary experiments, in which shorter incubation was less efficient in isolating ZnO-binding phages, while extending the time over 1 h did not change the results significantly. Unbound phages were then separated from ZnO-binding phages by centrifugation (4,000 × g, 1 min, RT) and were subsequently removed by decanting the supernatant. The pellet containing ZnO with bound phages was washed ten times with the TBST buffer. Phages which bound ZnO were eluted with 1 mL of 0.2 M glycine–HCl (pH 2.2) for 10 min, and finally neutralized with 150 μL of 1 M Tris–HCl (pH 9.1). Phages were then multiplied on Escherichia coli ER2738 (NEB) according to the NEB protocol and used in the next panning procedure (briefly, for phage multiplication, 0.2 mL of an overnight E. coli ER2738 culture were mixed with eluted phages, transferred to 20 mL of fresh LB medium in a 250 mL flask, and incubated with shaking (160 rpm) at 37 °C for 5 h). Three rounds of panning were performed. Following the last panning, the eluted phages were titrated on agar plates supplemented with IPTG/XGal as previously described (Łoś et al. 2008). Phages from individual plaques were amplified as described above, and their DNAs were isolated and purified according to Wilson (1993) and sequenced commercially using the 96 gIII sequencing primer (NEB).
Results and discussion
Experiments performed as described in Materials and methods led to detection of a huge variability (in the range of a few to several orders of magnitude) in efficiencies of binding to ZnO nanoparticles exhibited by different phage clones, as estimated by determining percentages of bound and unbound virions after 1 h incubaction. In fact, some binding (several percent of bound virions) could be observed even for phages that did not expose any foreign peptides on their capsids (data not shown). This might be explained by the fact that no chemical surface could be truly neutral in its effects on adhesion, thus, even naturally occurring phages may attach, to some extent, to any particles. Nevertheless, we have isolated 20 phage clones which were able to bind ZnO very efficiently, i.e., in which at least 99.99 % virions were able to interact with ZnO sufficiently stably to remain bound after the washing procedures.
Of the isolated 20 clones, those revealing the highest affinity to ZnO (clones no. PG-7, PG-8, PG-10, PG-12, PG-14, PG-17) were chosen for more detailed analysis, in which nucleotide sequences of the DNA inserts have been determined. As a semi-negative control, a clone revealing about ten times lower affinity to ZnO (measured as a fraction of virions able to remain bound after the washing procedures), called clone no. PG-2, was also analyzed (Fig. 1). Amino acid sequences of peptides PG-7, PG-8, PG-12, PG-14, and PG-17, exposed on the phage surface, deduced on the basis of determined nucleotide sequences, were identical and red as follows: TMGANLGLKWPV (Fig. 1; Table 1). The amino acid sequence of PG-10 was TTGANLGPKWPV, and that of PG-2 was TMGANLGLESPE. Comparison of the differences between clones binding ZnO relatively strongly (i.e., consisting of less than 1 per 105 virions unbound to ZnO, giving the efficiency of binding >99.999 %; clones PG-7, PG-8, PG-12, PG-14, and PG-17) with those binding ZnO slightly (clone PG-10) or significantly (clone PG-2) weaker indicated that the optimal amino acid sequence of ZnO-binding peptide, isolated under conditions employed in this study, was as follows: TMGANLGLKWPV (Fig. 1). Moreover, it appears that replacement of M with T at position 2 and of L with P at position 8 (as in PG-10) had a minor effect on ZnO binding, while replacement of K with E at position 9, W with S at position 10, and V with E at position 12 (as in PG-2) resulted in a considerable lower affinity of the peptide to ZnO (Fig. 1).
Characterization of selected phage clones which expose ZnO-binding peptides on their virion surfaces. Names of clones and sequences of the exposed peptides are shown, with differences in amino acid residues between peptides marked by white letters on the black background. Efficiency of ZnO binding by particular phage clones was estimated by determination of the fraction of virions unbound to ZnO after the washing procedure (see Materials and methods for details)
The clone no. PG-7 (revealing the optimal ZnO-binding sequence of the phage surface-exposed peptide), has been further characterized. We assessed the efficiency of ZnO binding according to the panning procedure (Sano and Shiba 2003). Binding efficiency was expressed as the ratio of the output phage number (phages eluted, O) to the input phage number (phages incubated with ZnO, I), called the output/input (O/I) ratio. As a control, we employed the M13KE phage with the wild-type pIII protein (NEB). The results of such experiments, presented in Fig. 2, confirmed an efficient binding of the selected peptide to ZnO. This efficiency appears to be similar to those described previously for other peptides isolated as agents that bind ZnO effectively (Kjærgaard et al. 2000; Umetsu et al. 2005; Okochi et al. 2010; Vreuls et al. 2010).
The results of experiments presented in this report indicate that by changing either experimental conditions or approach, it is possible to isolate ZnO-binding peptides of very different amino acid sequences (compare sequences of ZnO-binding peptides presented in Table 1). Therefore, it appears that variability of peptide structures that are able to bind this compound is very high. This implies potential possibilities of searching for ZnO-binding peptides revealing various properties under different reaction conditions. In this light, it is worth reminding that different applications of ZnO may require binding of this compound by peptides under various conditions of temperature, pH, ionic strength, and others (Umetsu et al. 2005).
Finally, one should note that searching for factors that can bind certain compounds, particularly when using the method of phage display-based screening of peptide libraries, is devoted to bio- and bionano-technological applications, and in no way represents processes that occur in nature. The phage display tests demonstrate a huge biological potential of organisms rather than mimic actual biological selection, at least under conditions currently occurring in natural habitats.
References
Ahmad G, Dickerson MB, Cai Y, Jones SE, Ernst EM, Vernon JP, Haluska MS, Fang Y, Wang J, Subramanyam G, Naik RR, Sandhage KH (2008) Rapid bioenabled formation of ferroelectric BaTiO3 at room temperature from an aqueous salt solution at near neutral pH. J Am Chem Soc 130:4–5. doi:10.1021/ja0744302
Brown S, Sarikaya M, Johnson E (2000) A genetic analysis of crystal growth. J Mol Biol 299:725–735. doi:10.1006/jmbi.2000.3682
Castel G, Chtéoui M, Heyd B, Tordo N (2011) Phage display of combinatorial peptide libraries: application to antiviral research. Molecules 16:3418–3499. doi:10.3390/molecules16053499
Chen H, Su X, Neoh KG, Choe WS (2006) QCM-D analysis of binding mechanism of phage particles displaying a constrained heptapeptide with specific affinity to SiO2 and TiO2. Anal Chem 78:4872–4879. doi:10.1021/ac0603025
Ezhilvalavan S, Kutty TRN (1997) Effect of antimony oxide stoichiometry on the nonlinearity of zinc oxide varistor ceramics. Mater Chem Phys 49:258–269. doi:10.1016/S0254-0584(97)80173-3
Fan Z, Lu JG (2005) Zinc oxide nanostructures: synthesis and properties. J Nanosci Nanotechnol 5:1561–1573. doi:10.1166/jnn.2005.182
Georgieva Y, Konthur Z (2011) Design and screening of M13 phage display cDNA libraries. Molecules 16:1667–1681. doi:10.3390/molecules16021667
Gerstel P, Lipowsky P, Durupthy O, Hoffmann RC, Bellina P, Bill J, Aldinger F (2006) Deposition of zinc oxide and layered basic zinc salts from aqueous solutions containing amino acids and dipeptides. J Ceram Soc Jpn 114:911–917. doi:10.2109/jcersj.114.911
Goyal DJ, Agashe C, Takwale MG, Marathe BR, Bhide VG (1992) Development of transparent and conductive ZnO films by spray pyrolysis. J Mater Sci 27:4705–4708. doi:10.1007/BF01166010
Kjærgaard K, Sørensen JK, Schembri MA, Klemm P (2000) Sequestration of zinc oxide by fimbrial designer chelators. Appl Environ Microbiol 66:10–14. doi:10.1128/AEM.66.1.10-14.2000
Li Q, Mahendra S, Lyon DY, Brunet L, Liga MV, Li D, Alvarez PJ (2008) Antimicrobial nanomaterials for water disinfection and microbial control: potential applications and implications. Water Res 42:4591–4602. doi:10.1016/j.watres.2008.08.015
Łoś JM, Golec P, Węgrzyn G, Węgrzyn A, Łoś M (2008) Simple method for plating Escherichia coli bacteriophages forming very small plaques or no plaques under standard conditions. Appl Environ Microbiol 74:5113–5120. doi:10.1128/AEM.00306-08
Meulenkamp EA (1998) Synthesis and growth of ZnO nanoparticles. J Phys Chem B 102:5566–5572. doi:10.1021/jp980730h
Okochi M, Ogawa M, Kaga C, Sugita T, Tomita Y, Kato R, Honda H (2010) Screening of peptides with a high affinity for ZnO using spot-synthesized peptide arrays and computational analysis. Acta Biomater 6:2301–2306. doi:10.1016/j.actbio.2009.12.025
Park HY, Go HY, Kalme S, Mane RS, Han SH, Yoon MY (2009) Protective antigen detection using horizontally stacked hexagonal ZnO platelets. Anal Chem 81:4280–4284. doi:10.1021/ac900632n
Rasmussen JW, Martinez E, Louka P, Wingett DG (2010) Zinc oxide nanoparticles for selective destruction of tumor cells and potential for drug delivery applications. Expert Opin Drug Deliv 7:1063–1077. doi:10.1517/17425247.2010.502560
Sano K, Shiba K (2003) A hexapeptide motif that electrostatically binds to the surface of titanium. J Am Chem Soc 125:14234–14235. doi:10.1021/ja038414q
Seker OU, Demir HV (2011) Material binding peptides for nanotechnology. Molecules 16:1426–1451. doi:10.3390/molecules16021426
Shinde VR, Gujar TP, Lokhande CD, Mane RS, Han SH (2007) Use of chemically synthesized ZnO thin film as a liquefied petroleum gas sensor. Mater Sci Eng B 137:119–125. doi:10.1016/j.mseb.2006.11.008
Tomczak MM, Gupta MK, Drummy LF, Rozenzhak SM, Naik RR (2009) Morphological control and assembly of zinc oxide using a biotemplate. Acta Biomater 5:876–882. doi:10.1016/j.actbio.2008.11.011
Umetsu M, Mizuta M, Tsumoto K, Ohara S, Takami S, Watanabe H, Kumagai I, Adschiri T (2005) Bioassisted room-temperature immobilization and mineralization of zinc oxide—the structural ordering of ZnO nanoparticles into a flower-type morphology. Adv Mater 17:2571–2575. doi:10.1002/adma.200500863
Vreuls C, Zocchi G, Genin A, Archambeau C, Martial J, Van de Weerdt C (2010) Inorganic-binding peptides as tools for surface quality control. J Inorg Biochem 104:1013–1021. doi:10.1016/j.jinorgbio.2010.05.008
Weintraub B, Zhou Z, Li Y, Deng Y (2010) Solution synthesis of one-dimensional ZnO nanomaterials and their applications. Nanoscale 2:1573–1587. doi:10.1039/C0NR00047G
Whaley SR, English DS, Hu EL, Barbara PF, Belcher AM (2000) Selection of peptides with semiconductor binding specificity for directed nanocrystal assembly. Nature 405:665–668. doi:10.1038/35015043
Wilson RK (1993) High-throughput purification of M13 templates for DNA sequencing. Biotechniques 15:414–422
Yu H, Zhang Z, Han M, Hao X, Zhu F (2005) A general low-temperature route for large-scale fabrication of highly oriented ZnO nanorod/nanotube arrays. J Am Chem Soc 127:2378–2379. doi:10.1021/ja043121y
Acknowledgments
This study was supported by National Science Center (Poland) within the project grant no. N N302 181439 (to G.W.).
Open Access
This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Golec, P., Karczewska-Golec, J., Łoś, M. et al. Novel ZnO-binding peptides obtained by the screening of a phage display peptide library. J Nanopart Res 14, 1218 (2012). https://doi.org/10.1007/s11051-012-1218-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11051-012-1218-5