Abstract
Metal carboxylato-hydrazinates are very good precursors for the synthesis of metal as well as mixed metal oxides as these, most of the times decomposes to nanosized oxides with high surface area at comparatively lower temperatures. In the present study one such novel precursor has been prepared and characterized by XRD, IR, SEM-EDS and chemical analysis. The thermal decomposition of the precursor has also been studied by isothermal, differential scanning calorimetry (DSC) and thermogravimetric analysis (TG). The precursor shows two-step dehydrazination followed by decarboxylation to form Ni0.5Mn0.1Zn0.4Fe2O4. The infrared spectra show N-N stretching frequency at 972 cm−1 which confirms the bidentate bridging hydrazine. XRD confirms the formation of single phase Ni0.5Mn0.1Zn0.4Fe2O4.
Similar content being viewed by others
References
K. C. Patil, Proc. Ind. Acad. Sci. (Chem. Sci.), 96 (1986) 459.
B. N. Sivasankar and S. Govindrajan, Synth. React. Inorg. Met.-Org. Chem., 24 (1994) 1573.
B. N. Sivasankar and S. Govindrajan, Synth. React. Inorg. Met.-Org. Chem., 24 (1994) 1583.
S. Y. Sawant, V. M. S. Verenkar and S. C. Mojumdar, J. Therm. Anal. Cal., 90 (2007) 669.
R. A. Porob, S. Z. Khan, S. C. Mojumdar and V. M. S. Verenkar, J. Therm. Anal. Cal., 86 (2006) 605.
M. Dováľ, M. Palou and S. C. Mojumdar, J. Therm. Anal. Cal., 86 (2006) 595.
A. More, V. M. S. Verenkar and S. C. Mojumdar, J. Therm. Anal. Cal., 94 (2008) 63.
S. C. Mojumdar and L. Raki, J. Therm. Anal. Cal., 85 (2006) 99.
L. R. Gonsalves, V. M. S. Verenkar and S. C. Mojumdar, J. Therm. Anal. Cal., in press.
I. Janotka and L’. Krajči, CERAMICS-Silikaty, 39 (1995) 105.
K. G. Varshney, A. Agrawal and S. C. Mojumdar, J. Therm. Anal. Cal., 90 (2007) 721.
L’. Krajči, I. Janotka, I. Kraus and P. Jamnicky, CERAMICS-Silikaty, 51 (2007) 217.
G. Madhurambal, P. Ramasamy, P. A. Srinivasan and S. C. Mojumdar, J. Therm. Anal. Cal., 90 (2007) 673.
K. G. Varshney, A. Agrawal and S. C. Mojumdar, J. Therm. Anal. Cal., 90 (2007) 731.
S. C. Mojumdar, M. Melník and E. Jóna, J. Anal. Appl. Pyrolysis, 53 (2000) 149.
D. Czakis-Sulikowska, A. Czylkowska and A. Malinowska, J. Therm. Anal. Cal., 67 (2002) 667.
B. Borah and J. L. Wood, Can. J. Chem., 50 (1976) 2470.
S. C. Mojumdar, K. G. Varshney and A. Agrawal, Res. J. Chem. Environ., 10 (2006) 89.
S. C. Mojumdar, M. Sain, R. Prasad, L. Sun and J. E. S. Venart, J. Therm. Anal. Cal., 90 (2007) 653.
A. Ramadevi and K. Srinivasan, Res. J. Chem. Environ., 9 (2005) 54.
S. Meenakshisundaram, S. Parthiban, G. Madhurambal and S. C. Mojumdar, J. Therm. Anal. Cal., 94 (2008) 21.
I. Janotka and L’. Krajči, Int. J. Cem. Comp. Light. Concr., 11 (1989) 221.
J. S. Skoršepa, K. Györyová and M. Melník, J. Thermal Anal., 44 (1995) 169.
D. Ondrušová, E. Jóna and P. Šimon, J. Therm. Anal. Cal., 67 (2002) 147.
E. Jona, E. Rudinska, M. Sapietova, M. Pajtasova and D. Ondrusova, Res. J. Chem. Environ., 10 (2006) 31.
M. Kubranová, E. Jóna, E. Rudinská, K. Nemčeková, D. Ondrušová and M. Pajtášová, J. Therm. Anal. Cal., 74 (2003) 251.
E. Jóna, M. Hvastijová and J. Kohout, J. Thermal Anal., 41 (1994) 161.
D. Czakis-Sulikowska and A. Czylkowska, J. Therm. Anal. Cal., 71 (2003) 395.
R. K. Verma, L. Verma, M. Ranjan, B. P. Verma and S. C. Mojumdar, J. Therm. Anal. Cal., 94 (2008) 27.
F. Tian, L. Sun, J. E. S. Venart, R. C. Prasad and S. C. Mojumdar, J. Therm. Anal. Cal., 94 (2008) 37.
G. Madhurambal, P. Ramasamy, P. Anbusrinivasan, G. Vasudevan, S. Kavitha and S. C. Mojumdar, J. Therm. Anal. Cal., 94 (2008) 59.
E. A. Ukraintseva, V. A. Logvinenko, D. V. Soldatov, T. A. Chingina, J. Therm. Anal. Cal., 75 (2004) 337.
S. C. Mojumdar, M. Melník and E. Jóna, J. Therm. Anal. Cal., 56 (1999) 541.
H. S. Rathore, G. Varshney, S. C. Mojumdar and M. T. Saleh, J. Therm. Anal. Cal., 90 (2007) 681.
S. C. Mojumdar, G. Madhurambal and M. T. Saleh, J. Therm. Anal. Cal., 81 (2005) 205.
K. G. Varshney, A. Agrawal and S. C. Mojumdar, J. Therm. Anal. Cal., 81 (2005) 183.
E. Jóna, E. Rudinská, M. Sapietová, M. Pajtášová, D. Ondrušová, V. Jorík and S. C. Mojumdar, Res. J. Chem. Environ., 9 (2005) 41.
S. C. Mojumdar, J. Miklovic, A. Krutošíková, D. Valigura and J. M. Stewart, J. Therm. Anal. Cal., 81 (2005) 211.
S. C. Mojumdar, Res. J. Chem. Environ., 9 (2005) 23.
G. Madhurambal, S. C. Mojumdar, S. Hariharan and P. Ramasamy, J. Therm. Anal. Cal., 78 (2004) 125.
S. C. Mojumdar, J. Therm. Anal. Cal., 64 (2001) 629.
S. Y. Sawant, K. R. Kannan and V. M. S. Verenkar, in Proc. 13th Nat. Symp. on Thermal Analysis, B.A.R.C., Mumbai 2002, C. G. S. Pillai, K. L. Ramakumar, P. V. Ravindran and V. Venugopal, Eds,, Indian Thermal Analysis Society, Mumbai 2002, p. 154.
U. Gawas, A. More, S. Bhattacharyya and V. M. S. Verenkar, Synthesis and characterization of nanosize Ni0.6Zn0.4Fe2O4 obtained by self-propagating autocombustion of a novel precursor, in International Conference on Advanced Materials and Applications, November 15–17, 2007, Shivaji University, Kolhapur, India, p. 23.
A. I. Vogel, ’A Textbook of Quantitative Inorganic Analysis’, 4th Ed., Longman, UK 1985.
A. Braibanti, F. Dallavalle, M. A. Pellinghelli and E. Leporati, Inorg. Chem., 7 (1968) 1430.
B. N. Sivasankar and S. Govindrajan, Z. Naturforsch., 49b (1994) 950.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gawas, U.B., Mojumdar, S.C. & Verenkar, V.M.S. Ni0.5Mn0.1Zn0.4Fe2(C4H2O4)3·6N2H4 precursor and Ni0.5Mn0.1Zn0.4Fe2O4 nanoparticle. J Therm Anal Calorim 96, 49–52 (2009). https://doi.org/10.1007/s10973-008-9836-y
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-008-9836-y