Thermal behavior of α-(Cu–Al–Ag) alloys, i.e. alloys with composition less than about 8.5 mass% Al, was studied using differential scanning calorimetry (DSC), differential thermal analysis (DTA), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicated that the presence of silver introduces new thermal events ascribed to the formation of a silver-rich phase and, after addition higher amounts than 8 mass% Ag to the Cu–8 mass% Al alloy it is possible to observe the formation of the γ1 phase (Al4Cu9), which is only observed in alloys containing minimum of 9 mass% Al. These results may be attributed to some Ag characteristics and its interaction with Cu and Al.
Similar content being viewed by others
References
C Panseri M Leoni (1961) Alluminio 30 289 Occurrence Handle1:CAS:528:DyaF2cXms1OitA%3D%3D
AT Adorno RAG Silva (2004) Mater. Sci. Eng. A 374 170 Occurrence Handle10.1016/j.msea.2004.02.006
TV Philip JD Mack (1962) Trans. AIME 34 224
AT Adorno RAG Silva (2005) J. Alloys Compd. 402 170 Occurrence Handle10.1016/j.jallcom.2005.04.145
AT Adorno MR Guerreiro AV Benedetti (1998) J. Alloys Compd. 268 122 Occurrence Handle10.1016/S0925-8388(97)00564-1 Occurrence Handle1:CAS:528:DyaK1cXhvVymurg%3D
TB Massalski JH Perepezko (1963) Z. Metallkd. 64 173
AT Adorno M Cilense W Garlipp (1989) J. Mater. Sci. Lett. 8 1294 Occurrence Handle10.1007/BF00721498 Occurrence Handle1:CAS:528:DyaK3cXktVOjtw%3D%3D
AT Adorno MR Guerreiro CA Ribeiro CTR Guerreiro (2001) J. Therm. Anal. Cal. 64 1141 Occurrence Handle10.1023/A:1011584727408 Occurrence Handle1:CAS:528:DC%2BD3MXlslKqur4%3D
AT Adorno RAG Silva (2006) J. Therm. Anal. Cal. 83 241 Occurrence Handle10.1007/s10973-005-6986-z Occurrence Handle1:CAS:528:DC%2BD28XitF2ntLs%3D
J Kwarciak (1986) J. Thermal Anal. 31 559 Occurrence Handle10.1007/BF01914232 Occurrence Handle1:CAS:528:DyaL28XlslKru7s%3D
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Adorno, A.T., Silva, R.A.G. & Magdalena, A.G. Thermal behavior of α-(Cu–Al–Ag) alloys. J Therm Anal Calorim 87, 759–762 (2007). https://doi.org/10.1007/s10973-006-7790-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-006-7790-0