Abstract
1,4-phenylenediamine-1-propylsilica hybrid xerogels were obtained for two composition at different temperatures of gelation, from 5 up to 70∘C. The morphological effects produced by the different gelation temperatures were investigated by using N2 adsorption-desorption isotherms and scanning electron microscopy. The thermal stability of the organic groups and their distribution on the xerogel matrix, i.e. the fraction of the organic groups that were trapped in closed pores, formed during the xerogel synthesis, and the fraction of organic groups present on the surface, were obtained by using infrared thermal analysis. The higher porosity of the xerogels and the higher thermal stability of the organic groups were achieved for samples gelled at 25∘C.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
J.Y. Wen and G.L. Wilkes, Chem. Mater. 8, 1667 (1996).
S. Yano, K. Iwata, and K. Kurita, J. Sol–gel Sci. Technol. 6, 75 (1998).
M.M. Collinson, Microchim. Acta 129, 149 (1998).
G. Cerveau, and R.J.P. Corriu, Coord. Chem. Rev. 178, 1051 (1998).
K.H. Haas, Adv. Eng. Mater. 2, 571 (2000).
A. Walcarius, Chem. Mater. 13, 3351 (2001).
F.A. Pavan, A.M.S. Lucho, R.S. Gonçalves, T.M.H. Costa, and E.V. Benvenutti, J. Colloid Interface Sci. 263, 688 (2003).
C. Sanchez, B. Lebeau, F. Chaput, and J.P. Boilot, Adv. Mater. 15, 1969 (2003).
F.A. Pavan, S. Leal, Y. Gushikem, T.M.H. Costa, and E.V. Benvenutti, J. Sol–gel Sci. Technol. 23, 129 (2002).
D.R. Azolin, C.C. Celso, T.M.H. Costa, and E.V. Benvenutti, J. Non-Cryst. Solids 337, 201 (2004).
L.T. Arenas, A. Langaro, Y. Gushikem, C.C. Moro, E.V. Benvenutti, and T.M.H. Costa, J. Sol-Gel Sci. Technol. 28, 51 (2003).
F.A. Pavan, Y. Gushikem, C.C. Moro, T.M.H. Costa, and E.V. Benvenutti, Colloid Polymer Sci. 281, 173 (2003).
J.D. Mackenzie and E. Bescher, J. Sol–gel Sci. Technol. 27, 7 (2003).
Z. Ahmad, and J.E. Mark, Chem. Mater. 13, 3320 (2001).
J.D. Mackenzie and E.P. Bescher, J. Sol-Gel Sci. Technol. 19, 23 (2000).
F.A. Pavan, H.S. Hoffmann, Y. Gushikem, T.M.H. Costa, and E.V. Benvenutti, Mater. Lett. 55, 378 (2002).
T.C.K. Yang, T.S. Yeh, and T.W. Chung, Chem. Eng. Commun. 186, 25 (2001).
S. Klein, S. Thorimbert, and W.F. Maier, J. Catal. 163, 476 (1996).
F.A. Pavan, S.A. Gobbi, T.M.H. Costa, and E.V. Benvenutti, J. Therm. Anal. Calorim. 68, 199 (2002).
J.C.P. Vaghetti, M. Zat, K.R.S. Bentes, L.S. Ferreira, E.V. Benvenutti, and E.C. Lima, J. Anal. At. Spectrom. 18, 376 (2003).
E.P. Barret, L.G. Joyner, and P.P. Halenda, J. Am. Chem. Soc. 73, 373 (1951).
S. Brunauer, P.H. Emmett, and E. Teller, J. Am. Chem. Soc. 60, 309 (1938).
P.D. Maniar, A. Navrotsky, E.M. Rabinovich, J.Y. Ying, and J.B. Benziger, J. Non-Cryst. Solids 124, 101 (1990).
J.Y. Ying, J.B. Benziger, and A. Navrotsky, J. Am. Ceram. Soc. 76, 2571 (1993).
R.M. Almeida and C.G. Pantano, J. Appl. Phys. 68, 4225 (1990).
L.T. Arenas, T.A.S. Aguirre, A. Langaro, Y. Gushikem, E.V. Benvenutti, and T.M.H. Costa, Polymer, 44, 5521 (2003).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gay, D.S.F., Gushikem, Y., Moro, C.C. et al. The Effects of Temperature of Condensation on the Thermal Stability and Morphology of 1,4-Phenylenediamine-1-Propylsilica Xerogels. J Sol-Gel Sci Technol 34, 189–195 (2005). https://doi.org/10.1007/s10971-005-1365-6
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10971-005-1365-6