Abstract
A double-network (DN) polyethylene glycol/polyacrylic acid (PEG/PAA) hydrogel with high compressive strength was synthesized by one-pot solution polymerization. The PEG network crosslinked by glutaraldehyde (GA) was fabricated via condensation reaction while the PAA network crosslinked by N,N’-dimethylenebiacrylamide (MBAM) via free-radical polymerization. The components of hydrogel were analyzed with Fourier transform infrared spectroscopy (FTIR). Mechanical strength of PEG/PAA hydrogels was examined, and the results showed that the addition of GA and PEG endowed the DN hydrogel with a high compressive strength of 10.9 MPa in a water content of 90 wt% due to lightly crosslinking and special entangled bundles morphology. Morphological studies showed that the hydrogels exhibited various pore structures when they were synthesized using different molar ratio of GA to PEG. This work provided a simple way to prepare ultrastrong DN hydrogels.
Similar content being viewed by others
References
Azuma C, Yasuda K, Tanabe Y, Taniguro H, Kanaya F, Nakayama A, Chen YM, Gong JP, Osada Y (2007) J Biomed Mater Res A 81A:373–380
Liu Y, Chan-Park MB (2009) Biomaterials 30:196–207
Na K, Park KH, Kim SW, Bae YH (2000) J Contr Release 69:225–236
Perale G, Veglianese P, Rossi F, Peviani M, Santoro M, Llupi D, Micotti E, Forloni G, Masi M (2011) Mater Lett 65:1688–1692
Kim SH, Kiick KL (2010) Macromol Rapid Commun 31:1231–1240
Liu P, Peng J, Li J, Wu J (2005) Radiat Phys 72:635–638
Artyukhov AA, Shtilman MI, Kuskov AN, Fomina AP, Lisovyy DE, Golunova AS, Tsatsakis AM (2011) J Polym Res 18:667–673
Yin Y, Lv X, Tu H, Xu S, Zheng H (2010) J Polym Res 17:471–479
Gong JP, Katsuyama Y, Kurokawa T, Osada Y (2003) Adv Mater 15:1155–1158
Webber RE, Creton C, Brown HR, Gong JP (2007) Macromolecules 40:2919–2927
Myung D, Waters D, Wiseman M, Duhamel PE, Noolandi J, Ta CN, Frank CW (2008) Polym Adv Technol 19:647–657
Fei X, Xu S, Feng S, Lin J, Lin J, Shi X, Wang J (2011) J Polym Res 18:1131–1136
Lin J, Xu S, Shi X, Feng S, Wang J (2009) Polym Adv Technol 20:645–649
Peng HT, Blostein MD, Shek PN (2009) J Biomed Mater Res B 89B:199–209
Myung D, Koh W, Ko J, Hu Y, Carrasco M, Noolandi J, Ta CN, Frank CW (2007) Polymer 48:5376–5387
Myung D, Farooqui N, Zheng LL, Koh W, Gupta S, Bakri A, Noolandi J, Cochran JR, Frank CW, Ta CN (2009) J Biomed Mater Res A 90A:70–81
Yim ES, Zhao B, Myung D, Kourtis LC, Frank CW, Carter D, Smith RL, Goodman SB (2009) J Biomed Mater Res A 91A:894–902
Tang Q, Wu J, Sun H, Fan S, Hu D, Lin J (2009) Polym Compos 30:1183–1189
Acknowledgment
Financial supports for this work were provided from Natural Science Foundation of China (No. 50763005) and the Startup Foundation for Doctors of Xinjiang University, China (BS100116).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, P., Wu, R., Wang, J. et al. One-pot preparation of ultrastrong double network hydrogels. J Polym Res 19, 9825 (2012). https://doi.org/10.1007/s10965-012-9825-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10965-012-9825-5