Abstract
The aim of this research was to fabricate YBa2Cu3O7−δ (YBCO) superconductor composite with graphene oxide nanosheets and to study the effect of the graphene oxide nanosheets on YBCO superconductor properties. For this purpose, the samples of pure superconductor and superconductor composite with 0.001, 0.01, and 0.1 wt.% graphene oxide were synthesized. First, graphite oxide was made by Hummer’s chemical method; after that, graphene oxide nanosheets were produced by bath-keeper ultrasonic. Then, different amounts of graphene oxide were added to the process of superconductor fabrication, which was made by solid-state reaction method. The samples were characterized and studied by Meissner effect test, XRD analysis, FESEM imaging, EDX measurement, and ac magnetic susceptibility. The critical current density (Jc) of samples was measured by four probes method. The results showed that by increasing the weight ratio of graphene oxide, Jc and Tc decrease.
Similar content being viewed by others
References
Strickland, N.M., Long, N.J., Talantsev, E.F., Hoefakker, P., Xia, J.: Enhanced flux pinning by BaZrO3 nanoparticles in metal-organic deposited YBCO second-generation HTS wire. Physica C 468, 183–189 (2008)
Jia, Z.Y., Tang, H., Yang, Z.Q., Xing, Y.T., Wang, Y.Z., Qiao, G. W.: Effects of nano-ZrO2 particles on the superconductivity of Pb-doped BSCCO. Physica C 337, 130–132 (2000)
Cui, X.M., Liu, G.Q., Wang, J., Huang, Z.C., Zhao, Y.T., Tao, B.W., Li, Y.R.: Enhancement of critical current density of YBa2Cu3O7−δ thin films by nanoscale CeO2 pretreatment of substrate surfaces. Physica C 466, 1–4 (2007)
Soltanian, S., Horvat, J., Wang, X. L., Munroe, P., Dou, S. X.: Effect of nano-carbon particle doping on the flux pinning properties of MgB2 superconductor. Physica C 390, 185–190 (2003)
Fan, Z., Wang, K., Wei, T.: An environmentally friendly and efficient route for the reduction of graphene oxide by aluminum powder. Carbon 48, 1670–1692 (2010)
Stankovich, S., Dikin, D. A., Piner, R. D., Kohlhaas, K. A., Kleinhammes, A., Jia, Y., Wu, Y., Nguyen, S. T., Ruoff, R. S.: Synthesis of graphene nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45, 1558–1565 (2007)
Salamati, H., Kameli, P.: Ac susceptibility of YBa2Cu3O7−δ superconducting thin film in perpendicular field. Physica B 321, 331 (2002)
Dadras, S, Soufiabadi, E: The mechanical properties investigation of the CNT doped YBCO high temperature superconductor with ANSYS finite element software. Iran. J. Sci. Technol. 39A4, 543–549 (2015)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shoushtari, M.Z., Akbari, M. & Hajati, Y. Study of YBa2Cu3O7−δ Superconductor/Graphene Oxide Composite. J Supercond Nov Magn 31, 2733–2739 (2018). https://doi.org/10.1007/s10948-017-4549-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-017-4549-8