In this study, a new soft magnetic composite (SMC) material design scheme was put forward. According to this design scheme, SMC with silicate glass insulation layers was prepared by powder metallurgy with nanometer glass powder and micron iron powder. It can be annealed at high temperature for reducing residual stress. The magnetic properties were good. The maximum permeability, saturation magnetic induction, residual magnetic flux density and coercivity were 467, 1.47 T, 1.25 T and 394 A/m, respectively. The core loss versus alternating magnetic field frequency showed linear growth. The core loss was 4.4 W/kg at an induction level of 1 T, 50 Hz.
Similar content being viewed by others
References
Asaka, K., Ishihara, C.: Hitachi Powdered Met. Tech. Rep. 4, 3–9 (2005)
http://www.staff.ncl.ac.uk/s.j.bull/smc.html, Accessed 2 February 2013
Cross, J., Viarouge, P.: IEEE Trans. Ind. Appl. 40, 113–120 (2004)
Hamler, A., Goričan, V., Šuštaršič, B., Sirc, A.: J. Magn. Magn. Mater. 304, 816–819 (2006)
Pennander, L.-O., Jack, A.G.: In: Proceedings Euro PM, vol. 2, pp. 213–220 (2003)
Anhalt, M., Weidenfeller, B.: J. Magn. Magn. Mater. 304, e549–e551 (2006)
Shokrollahi, H., Janghorban, K.: Mater. Sci. Eng. B 134, 41–43 (2006)
Verduzco, J.A., Betancourt, I., Ortiz, N., Olmos, L.R., Garcia, J.: Mater. Lett. 60, 2033–2037 (2006)
Hemmati, I., Madaah Hosseini, H.R., Kianvash, A.: J. Magn. Magn. Mater. 305, 147–151 (2006)
Gilbert, I.P., Moorthy, V., Bull, S.J., Evans, J.T., Jack, A.G.: J. Mater. Sci. 232, 242–245 (2002)
Pang, Y.X., Hodgson, S.N.B., Koniarek, J., Weilinski, B.: J. Magn. Magn. Mater. 310, 83–91 (2007)
Kim, Y.B., Jang, D.H., Seok, H.K., Kim, K.Y.: Mater. Sci. Eng. A 449–451, 389–393 (2007)
Uozumi, G., Watanabe, M., Nakayama, R., Igarashi, K., Morimoto, K.: Mater. Sci. Forum 534–536, 1361–1364 (2007)
Kim, Y.B., Jee, K.K.: J. Appl. Phys. 103, 07E704 (2008)
Yang, B., Wu, Z.B., Zou, Z.Y., Yu, R.H.: J. Phys. D, Appl. Phys. 43, 365003 (2010)
Gan, Y.: China Materials Engineering Canon. Beijing, pp. 150 (2005), Chap. 4
Takahashi, K.: J. Soc. Glass Technol. 37, 3N–7N (1953)
Nasu, H., Heo, J., Mackenzie, J.D.: J. Non-Cryst. Solids 99, 140–150 (1988)
Pu, H., Jiang, F., Yang, Z.: Mater. Chem. Phys. 100, 10–14 (2006)
Brauer, J.R., Cendes, Z.J., Beihoff, B.C., Phillips, K.P.: IEEE Trans. Ind. Appl. 36, 1132–1137 (2000)
Mchenry, M.E., Willard, M.A., Laughlin, D.E.: Prog. Mater. Sci. 44, 291–433 (1999)
Zhou, Y., Hultman, L., Kiellén, L.: http://www.hoganas.com/Documents/Published%20Articles/2004/Production_aspects_of_smc_components.pdf, February 2, 2013
Lefebvre, L.-P., Pelletier, S., Gélinas, C.: http://qmp-powders.com/rtecontent/document/1998/LPL2_LV.pdf, February 2, 2013
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ding, W., Jiang, L., Li, B. et al. Microstructure and Magnetic Properties of Soft Magnetic Composites with Silicate Glass Insulation Layers. J Supercond Nov Magn 27, 239–245 (2014). https://doi.org/10.1007/s10948-013-2249-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-013-2249-6