Abstract
In this study, four kinds of melt-processed YBCO samples were fabricated with the MPMG procedure. The compacted powders were located on a crucible with a buffer layer of Y2O3 to avoid liquid to spread on the furnace plate. Their microstructures were defined by XRD analysis and polarized light optical microscopy. The microstructure investigations indicated that the 123 grains were very big and fine and dispersed 211 particles remained in the samples. Resistivities of the samples were measured by a standard continuous dc four-probe method. Magnetization measurements were made and flux jumps were observed at a relatively higher temperature for Y1060. The critical current density, J c , values of the samples, measured by VSM in 5 T magnetic field, exceeded 0.6×103 A⋅cm−2 at 77 K and 4 T.
Similar content being viewed by others
References
Wu, M.K., Ashburn, J.R., Torng, C.J., Hor, P.H., Meng, R.L., Gao, L., Huang, Z.J., Wang, Y.Q., Chu, C.W.: Phys. Rev. Lett. 58, 908 (1987)
Giovannelli, F., Monot-Laffez, I.: Supercond. Sci. Technol. 15, 1193 (2002)
Feng, J., Lu, Y., Zhang, L.P., Xu, X., Chen, S., Zhang, C., Xiong, X., Liu, G.: Physica C 59, 52 (2007)
Murakami, M.: Supercond. Sci. Technol. 5, 185 (1992)
Ateş, A., Yanmaz, E.: J. Alloys Compd. 279, 220 (1998)
Sudhakar Reddy, E., Hari Babu, N., Shi, Y., Cardwell, D.A.: J. Eur. Ceram. Soc. 25, 2935 (2005)
Zhang, H., Zou, X.W., Wang, Z.H.: Physica C 386, 254 (2003)
Campbell, T.A., Haugan, T.J., Maartense, I., Murphy, J., Brunke, L., Barnes, P.N.: Physica C 423, 1 (2005)
Hasegawa, M., Yoshida, Y., Iwata, M., Ishizawa, K., Takai, Y., Hirabayashi, I.: Physica C 336, 295 (2000)
Pellerin, N., Jouan, G., Odier, P.: J. Mater. Res. 8, 18 (1993)
Chaud, X., Isfort, D., Beaugnon, E., Tournier, R.: Physica C 341–348, 2413 (2000)
Mohanta, A., Behera, D.: International Conference MSM-09 at S.N. Bose National Centre for Basic Sciences, Kolkata 1-11 (2009)
Palstra, T.T.M., Batlogg, B., Schneemeyer, L.F., Waszczak, J.V.: Phys. Rev. Lett. 61, 1662 (1988)
Palstra, T.T.M., Batlogg, B., van Dover, R.B., Schneemeyer, L.F., Waszczak, J.V.: Phys. Rev. B 41, 6621 (1990)
Zheng, M.H., Xiao, L., Ren, H.T., Jiao, Y.L., Chen, Y.X.: Physica C 386, 258 (2003)
Diko, P., Chaud, X., Antall, V., Kănuchovál, M., Šefčíkovál, M., Kováčı, J.: Supercond. Sci. Technol. 21, 115008 (2008)
Chikumoto, N., Ozawa, S., Yoo, S.I., Hayashi, N., Murakami, M.: Physica C 278, 187 (1997)
Theuss, H., Kronmüller, H.: Physica C 177, 253 (1991)
Ossandon, J.G., Thompson, J.R., Christen, D.K., Sales, B.C., Kerchner, H.R., Thompson, J.Q., Sun, Y.R., Lay, K.W., Tkaczyk, J.E.: Phys. Rev. B 45, 12534 (1992)
Sandiumenge, F., Martinez, B., Obradors, X.: Supercond. Sci. Technol. 10, A93 (1997)
Feng, Y., Wen, J.G., Pradhan, A.K., Koshizuka, N., Zhou, L., Chen, S.K., Wang, K.G., Wu, X.Z.: Supercond. Sci. Technol. 13, 703 (2000)
Martinez, B., Obradors, X., Gou, A., Gomis, V., Pinol, S., Fontcuberta, J., Van Tol, H.: Phys. Rev. B 53, 2797 (1996)
Yanmaz, E., Savaşkan, B., Başoğlu, M., Koparan, E.T., Dilley, N.R., Grovenor, C.R.M.: J. Alloy Compd. 480, 203 (2009)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Çakır, B., Aydıner, A. Preparation and Properties of MPMG YBCO Bulk with Y2O3 Layer. J Supercond Nov Magn 24, 1577–1584 (2011). https://doi.org/10.1007/s10948-010-1060-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-010-1060-x