Abstract
Hybrid composite of MIL-101 with silica rich rice husk ash (RHA) was fabricated to explore such materials for improved low pressure hydrogen storage applications, compared to the well explored carbon based composites of MIL-101. RHA–MIL-101 was prepared by in situ incorporation of RHA in MIL-101 during the synthesis, under hydrothermal conditions. The incorporation of RHA in MIL-101 was confirmed by P-XRD, FTIR, TGA, SEM, EDS, and N2 adsorption and desorption isotherms studies. The as-synthesized RHA–MIL-101 composite displayed enhanced BET surface area (8.6% compared to bare MIL-101), whereas AC–MIL-101 showed an enhancement of 12.7% in BET surface area compared to bare MIL-101. Hydrogen uptake properties of these materials were evaluated at 77 K and 1 bar. Despite that RHA–MIL-101 exhibited lower surface area as compared to AC–MIL-101, the hydrogen uptake capacities of RHA–MIL-101 reached an enhanced value of 1.54 wt%, which is obviously higher than the bare MIL-101 (1.40 wt%) and AC–MIL-101 (1.48 wt%) by 9.1% and 5.7%, respectively, as well as comparable to most of the reported carbon incorporated MOFs. It has been observed that improved hydrogen uptake properties was due to the bifunctional properties of the synthesized RHA–MIL-101, abundance of silanol bonds of RHA (which shows high affinity towards H2 molecules), and tuned porous properties of RHA–MIL-101. Moreover, hydrogen adsorption isotherms data of these materials were best fitted with three parameter non-linear adsorption equilibrium isotherm equations.
Similar content being viewed by others
References
L. Schlapbach, A. Zuttel, Nature 414, 353 (2001)
A. Zuttel, Mater. Today 6, 24 (2003)
J. Graetz, Chem. Soc. Rev. 38, 73 (2009)
J.L.C. Rowsell, O.M. Yaghi, Angew. Chem. Int. Ed. 44, 4670 (2005)
S.S. Murthy, E.A. Kumar, Appl. Therm. Eng. 72, 176 (2014)
H.W. Langmi, J. Rena, B. Northa, M. Mathea, D. Bessarabov, Electrochim. Acta 128, 368 (2014)
M.P. Suh, H.J. Park, T.K. Prasad, D.W. Lim, Chem. Rev. 112, 782 (2012)
N.L. Rosi, J. Eckert, M. Eddaoudi, D.T. Vodak, J. Kim, M. O’Keeffe, O.M. Yaghi, Science 300, 1127 (2003)
J. Sculley, D. Yuan, H.C. Zhou, Energy Environ. Sci. 4, 2721 (2011)
L.J. Murray, M. Dinca, J.R. Long, Chem. Soc. Rev. 38, 1294 (2009)
O.M. Yaghi, M. O’Keeffe, N.W. Ockwig, H.K. Chae, M. Eddaoudi, J. Kim, Nature 423, 705 (2003)
J.R. Long, O.M. Yaghi, Chem. Soc. Rev. 38, 1213 (2009)
G. Kaur, R.K. Rai, D. Tyagi, X. Yao, P.Z. Li, X.C. Yang, Y. Zhao, Q. Xu, S.K. Singh, J. Mater. Chem. A 4, 14932 (2016)
R.J. Kuppler, D.J. Timmons, Q.R. Fang, J.R. Li, T.A. Makal, M.D. Young, D. Yuan, D. Zhao, W. Zhuang, H.C. Zhou, Coord. Chem. Rev. 253, 3042 (2009)
S.T. Meek, J.A. Greathouse, M.D. Allendorf, Adv. Mater. 23, 249 (2011)
G. Ferey, C.M. Draznieks, C. Serre, F. Millange, J. Dutour, S. Surble, I.A. Margiolaki, Science 309, 2040 (2005)
P. Horcajada, C. Serre, M. Vallet-Regi, M. Sebban, F. Taulelle, G. Ferey, Angew. Chem. Int. Ed. Engl. 45, 5974 (2006)
Y.K. Hwang, D.Y. Hong, J.S. Chang, S.H. Jhung, Y.K. Seo, J. Kim, A. Vimont, M. Daturi, C. Serre, G. Ferey, Chem. Int. Ed. 47, 4144 (2008)
S. Bhattacharjee, C. Chen, W.S. Ahn, RSC Adv. 4, 52500 (2014)
X.W. Liu, T.J. Sun, J.L. Hu, S.D. Wang, J. Mater. Chem. A 4, 3584 (2016)
C. Janiak, J.K. Vieth, New J. Chem. 34, 2366 (2010)
K.P. Prasanth, P. Rallapalli, M.C. Raj, H.C. Bajaj, R.V. Jasra, Int. J. Hydrog. Energy 36, 7594 (2011)
P.B.S. Rallapall, M.C. Raj, D.V. Patil, K.P. Prasanth, R.S. Somani, H.C. Bajaj, Int. J. Energy Res. 37, 746 (2013)
D.K. Panchariya, R.K. Rai, S.K. Singh, E.A. Kumar, Mater. Today Proc. 4, 388 (2017)
P.A. Szilagyi, E. Callini, A. Anastasopol, C. Kwakernaak, S. Sachdeva, R.V.D. Krol, H. Geerlings, A. Borgschulte, A. Zuttel, B. Dam, Phys. Chem. Chem. Phys. 16, 5803 (2014)
M. Anbia, S. Mandegarzad, J. Alloys Compd. 532, 61 (2012)
K.S. Lin, A.K. Adhikari, Y.H. Su, C.W. Shu, H.Y. Chan, Adsorption 18, 483 (2012)
Q.L. Zhu, Q. Xu, Chem. Soc. Rev. 43, 5468 (2014)
N. Stock, S. Biswas, Chem. Rev. 112, 933 (2012)
H. Jiang, Y. Feng, M. Chen, Y. Wang, Int. J. Hydrog. Energy 38, 10950 (2013)
P.K. Prabhakaran, J. Deschamp, J. Mater. Chem. A 3, 7014 (2015)
K.L. Mulfort, J.T. Hupp, J. Am. Chem. Soc. 129, 9604 (2007)
S.J. Yang, J.Y. Choi, H.K. Chae, J.H. Cho, K.S. Nahm, C.R. Park, Chem. Mater. 9, 1893 (2009)
M. Sigl, S. Ernst, J. Weitkamp, H. Knozinger, Catal. Lett. 45, 27 (1997)
J. Hohmeyer, E.V. Kondratenko, M. Bron, J. Krohnert, F.C. Jentoft, F. Schlogl, P. Claus, J. Catal. 269, 5 (2010)
V.K. Rajagopal, R.D. Guthrie, T. Fields, B.H. Davis, Catal. Today 31, 57 (1996)
Z. Karimi, A. Morsali, J. Mater. Chem. A 1, 3047 (2013)
Y. Lin, Q. Yan, C. Kong, L. Chen, Sci. Rep. 3, 1859 (2013)
L. Bromberg, Y. Diao, H. Wu, S.A. Speakman, T.A. Hatton, Chem. Mater. 24, 1664 (2012)
K.Y. Foo, B.H. Hameed, Chem. Eng. J. 156, 2 (2010)
V.K. Singh, E.A. Kumar, Appl. Therm. Eng. 97, 77 (2016)
X. Du, J. He, Nanoscale 4, 852 (2012)
F. Balas, M. Manzano, P. Horcajada, M. Vallet-Regi, J. Am. Chem. Soc. 128, 8116 (2006)
J.L.C. Rowsell, A.R. Millward, K.S. Park, O.M. Yaghi, J. Am. Chem. Soc. 126, 5666 (2004)
J.S. Li, Y.J. Tang, S.L. Li, S.R. Zhang, Z.H. Dai, L. Si, Y.Q. Lan, Cryst. Eng. Comm. 17, 1080 (2015)
Y. Li, R.T. Yang, J. Phys. Chem. B 110, 17175 (2006)
L. Wang, R.T. Yang, Ind. Eng. Chem. Res. 49, 3634 (2010)
S.Y. Lee, S.J. Park, J. Nanosci. Nanotechnol. 13, 443 (2013)
J.L.C. Rowsell, O.M. Yaghi, J. Am. Chem. Soc. 128, 1304 (2006)
S.J. Yang, J.H. Cho, K.S. Nahm, C.R. Park, Int. J. Hydrog. Energy 35, 13062 (2010)
M. Sabo, A. Henschel, H. Frode, E. Klemm, S. Kaskel, J. Mater. Chem. 17, 3827 (2007)
A.C. Chien, S.S.C. Chuang, Int. J. Hydrog. Energy 36, 6022 (2011)
K.S. Park, Z. Ni, A.P. Cote, J.Y. Choi, R. Huang, F.J. Uribe-Romo, H.K. Chae, M. O’Keeffe, O.M. Yaghi, Proc. Natl. Acad. Sci. USA 103, 10186 (2006)
D. Saha, Z. Wei, S. Deng, Int. J. Hydrog. Energy 33, 7479 (2008)
Y. Li, R.T. Yang, Langmuir 23, 12937 (2007)
G. Calleja, J.A. Botas, M.S. Sanchez, M.G. Orcajo, Int. J. Hydrog. Energy 35, 9916 (2010)
Acknowledgements
This work is financially supported by IIT Indore and SERB (DST), New Delhi. D.K.P. thanks IIT Indore and MHRD, Govt. of India, for his fellowship. R.K.R. thanks IIT Indore for his institute post-doctoral grant. The authors thank SIC, IIT Indore, for extending instrumentation facilities. Generous help from Dr. Pratibha Sharma, DAVV Indore for FTIR measurements is also acknowledged. The authors also thank Nishant Enterprises, Katni, India for providing rice husk ash (RHA). The authors would also like to thank Dr. Lakshmi Iyengar, former visiting faculty, School of Humanities and Social Science, IIT Indore for her valuable suggestions during the preparation of this manuscript.
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Panchariya, D.K., Rai, R.K., Kumar, E.A. et al. Silica rich MIL-101(Cr) for enhanced hydrogen uptake. J Porous Mater 26, 1137–1147 (2019). https://doi.org/10.1007/s10934-018-0710-4
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10934-018-0710-4