Abstract
In accelerated weathering tests, specimens are exposed to higher radiation intensity, temperature and humidity than is likely under natural weathering in order to achieve rapid degradation of the polymer in a convenient short time. In the current work, a correlation between the two environments is attempted so that a prediction of lifetimes in the natural environment can be achieved. During aging, surface flaws are created due to the chain scission process. This is initiated by the absorption of ultra-violet light and directly affects visual appearance and impact strength. After natural weathering, the material shows only plastic deformation in an impact test. However, after artificial weathering to 5000 h of UV exposure, there is a decrease of 85% in impact strength. Colour change occurs at a high rate in the early stages of UV exposure. Beyond 2000 h of exposure, the colour change approaches a steady state and a correlation between the changes under natural and artificial weathering becomes apparent for a potential prediction of lifetimes. From the analysis including the specular component (SCI), taking surface roughening into account, 1 year under natural weathering was found to be equivalent to 25 days under accelerated weathering.
Similar content being viewed by others
References
Mwanzaa BG, Mbohwa C (2017) Procedia Manuf 8:649–656
Al-Salem SM, Lettieri P, Baeyens J (2009) Waste Manag 29:2625–2643
Achilias DS, Antonakou E, Roupakias C, Megalokonomos P, Lappas A (2007) Global Nest J 10, 1:114–122
La Mantia FP, Correnti A (2003) Prog Rubber Plast Recycl Technol 19:135
Sadat-Shojai M, Gholam-Reza B (2011) Polym Degrad Stab 96:404–415
Zhang Z, Hirose T, Nishio S, Morioka Y, Azuma N, Ohkita AH, Okada M (1995) Ind Eng Chem Res 34:4514
Pracella M, Chionna D, Ishak R, Galeski A (2004) Polym-Plast Technol Eng 43:1711
Scheirs J (1998) Polymer recycling. Wiley, London
Awaja F, Pavel D (2005) Eur Polym J 41:1453
Thiele U (2006) In: Proceedings of the 9th international polyester recycling forum, Washington
Mancini S, Zanin M (1997) Polym Recycl 3(98):239
Oromiehie A, Mamizadeh A (2004) Polym Intern 53:728
Jain R, Lee L (2012) Fiber reinforced polymer (FRP) composites for infrastructure applications. Springer, Berlin
Saravanan D (2007) Autex Res J 7:53
Davis L, Grace Y (2003) Geot Geom 21:111
Gonzalez A, Desaja J (2005) J Appl Polym Sci 41:1961
Davis A, Sim D (1983) Weathering of polymers. Applied Science Publishers Ltd, London
Capanescu C, Cincu C (2003) Adv Polym Technol 18:365
Jakubowicz I (2001) Polym Test 20:545
Feller RL (1994) Accelerated aging: photochemical and thermal aspects. Research in conservation. The Getty Conservation Institute
Norman S, Edge M, Mohammadian M, Jones K (1994) Polym Degrad Stab 43:229
Wang W, Taniguchi A, Fukuhara M, Okada T (1998) J Appl Polym Sci 67:705
Wang W, Taniguchi A, Fukuhara M, Okada T (1990) J Appl Polym Sci 74:306
Fechine G, Souto R (2002) J Mater Sci 37:4979
Zhu Z, Kelley M (2005) Polymer 46:8883
Fechine G, Rabello M, Souto R (2002) Polym Degrad Stab 75:153
Fechine G, Christensen P, Egerton T, White J (2009) Polym Degrad Stab 94:234
Hurley C, Leggett G (2009) ACS Appl Mater Interface 1:1688
Fernando S, Christensen P, Egerton T, Eveson R (2009) Mater Sci Technol 25:549
Krishnan S, Mitra S, Russell P, Benz G (1985) In: Proceedings of ACS symposium series 287. American Chemical Society, Washington, DC
Ilišković N, Bravar M (1986) Polym Degrad Stab 15:173
Fechine G, Rabello M, Souto R (2004) Polymer 45:2303
Russo P, Acierno D, Marinucci L, Greco A, Frigione M (2013) J Appl Polym Sci 127:2213
Tuasikal M, Alothman O, Luqman M, Al-Zahrani S, Jawad M (2014) Int J Polym Anal Charact 19:189
Wijdekop M, Arnold J, Evans M, John V, Alloyd A (2005) Mater Sci Technol 21:791
Malanowski P (2009) Weathering of aromatic polyester coating. Ph.D Thesis. Eindhoven University of Technology, Eindhoven
Donald D (1995) Polym-Plast Technol Eng 34:227
Koo H, Chang G, Kim S, Hahm W, Park S (2013) Fib Polym 14:2083
Badia J, Vilaplana F, Karlsson S, Ribes A (2009) Polym Test 28:169
QUV accelerated weathering tester: operating manual (Q-Panel Lab Products, USA, 1997)
Precise colour communications: instruction manual (Minolta, Japan, 2007)
Attwood J, Philip M, Hulme A, Williams G, Shipton P (2006) Polym Degrad Stab 91(12):3407–3415
Acknowledgements
The authors are grateful to Dr. Padmasari Kankanam Gamage for his technical support within the polymer laboratories at London Metropolitan University.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Philip, M., Al-Azzawi, F. Effects of Natural and Artificial Weathering on the Physical Properties of Recycled Poly(ethylene terephthalate). J Polym Environ 26, 3139–3148 (2018). https://doi.org/10.1007/s10924-018-1191-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10924-018-1191-x