Abstract
M-type strontium ferrite is a kind of magnetic functional material with wide application prospect. In this work, SrFe12−xAlxO19 (0 ≤ x ≤ 1) and Sr1−yCayFe8Al4O19 (0 ≤ y ≤ 0.4) have been prepared by a hydrothermal method, and the effects of Al3+ doping and Al3+ and Ca2+ co-doping on the magnetic properties have been investigated. X-ray diffraction analysis indicates all the samples are a hexagonal structure, and the shift of the diffraction peaks suggests that Al3+ and Ca2+ are successfully doped in SrFe12O19. Field emission scanning electron microscope images show the particles have the hexagonal shape with the size of 1.1–2.9 µm. Vibrating sample magnetometer reveals that the doping of Al3+ and the co-doping Al3+ and Ca2+ can enhance magnetic properties of strontium ferrite. For example, the values of coercivity and the saturation magnetization of SrFe8Al4O19 are 914.1 Oe and 44.0 emu/g, which are 3% and 117% enhancement compared with SrFe12O19, respectively. For Sr1−yCayFe8Al4O19, coercivity and saturation magnetization increase from 914.1 Oe and 41.8 emu/g to 1047.2 Oe and 50.2 emu/g when the Ca2+ doping concentration increases from 0 to 0.4. Moreover, the effects of acid washing also on phase composition, morphology and magnetism are researched. The as-synthesized doping strontium ferrite will be useful for the applications in security switching and recording media.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig3_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig5_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig6_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig7_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig8_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-020-04739-z/MediaObjects/10854_2020_4739_Fig9_HTML.png)
Similar content being viewed by others
Change history
04 January 2021
The above named article contains errors, which have been corrected below
References
B.T. Shirk, W.R. Bussem, Temperature dependence of Ms and K1 of BaFe12O19 and SrFe12O19 single crystals. J. Appl. Phys. 40, 1294–1296 (1969)
R. Sun, X. Li, A.L. Xia, S.B. Su, C.G. Jin, Hexagonal SrFe12O19 ferrite with high saturation magnetization. Ceram. Int. 44, 13551–13555 (2018)
N. Yasmin, M. Mirza, S. Muhammad, M. Zahid, M. Ahmad, M.S. Awan, A. Muhammad, Influence of samarium substitution on the structural and magnetic properties of M-type hexagonal ferrites. J. Magn. Magn. Mater. 446, 276–281 (2018)
J. Du, T.C. Zhou, L.X. Lian, Y. Liu, Y.B. Du, Two-step sintering of M-type strontium ferrite with high coercivity. Ceram. Int. 45, 6978–6984 (2019)
N. Ji, S. Park, Y. Kim, H. Kwon, S. Kim, K. Lim, Magnetic properties of M-type strontium ferrites with different heat treatment conditions. Rare Met. 39, 84–88 (2020)
J. Singh, C. Singh, D. Kaur, S.B. Narang, R. Jotania, R. Joshi, Investigation on structural and microwave absorption property of Co2+ and Y3+ substituted M-type Ba-Sr hexagonal ferrites prepared by a ceramic method. J. Alloys Compd. 695, 792–798 (2017)
G. Ramezanzaeh, A. Ghasemi, R. Mozaffarinia, A. Alizadeh, Electromagnetic wave reflection loss and magnetic properties of M-type SrFe12–x(Mn0.5Sn0.5)xO19 hexagonal ferrite nanoparticles in the Ku microwave band. Ceram. Int. 43, 10231–10238 (2017)
S. Bierlich, T. Reimann, F. Gellersen, A.F. Jacob, J. Töpfer, Sintering, microwave properties, and circulator applications of textured Sc-substituted M-type ferrite thick films. J. Eur. Ceram. Soc. 39, 3077–3081 (2019)
A.L. Xia, T. Zhan, R. Sun, S.B. Su, J. Li, H.Y. Zhang, H.L. Li, C.G. Jin, M-type SrFe12O19 ferrites obtained by using cubic or spindle-like α-Fe2O3 as Fe sources: a comparative study. J. Alloys Compd. 784, 276–281 (2019)
T. Schmidt, D. Seifert, J. Töpfer, Phase formation and saturation magnetization of La-Zn-substituted M-type strontium ferrites. J. Magn. Magn. Mater. 508, 166887 (2020)
C.C. Liu, X.S. Liu, S.J. Feng, K.M.U. Rehman, M.L. Li, C. Zhang, H.H. Li, X.Y. Meng, Effect of Y-La-Co substitution on microstructure and magnetic properties of M-type strontium hexagonal ferrites prepared by ceramic method. J. Magn. Magn. Mater. 445, 1–5 (2018)
C.C. Chauhan, A.R. Kagdi, R.B. Jotania, A. Upadhyay, C.S. Sandhu, S.E. Shirsath, S.S. Meena, Structural, magnetic and dielectric properties of Co-Zr substituted M-type calcium hexagonal ferrite nanoparticles in the presence of α-Fe2O3 phase. Ceram. Int. 44, 17812–17823 (2018)
E. Roohani, H. Arabi, R. Sarhaddi, S. Sudkhah, M-type strontium hexaferrite nanoparticles prepared by sol–gel auto-combustion method: the role of Co substitution in structural, morphological, and magnetic properties. J. Supercond. Nov. Magn. 30, 1599–1608 (2017)
X. Meng, W. Yang, G. Han, Y. Yu, S. Ma, W. Liu, Z. Zhang, Three-dimensional foam-like Fe3O4@C core-shell nanocomposites: controllable synthesis and wideband electromagnetic wave absorption properties. J. Magn. Magn. Mater. 502, 166518 (2020)
X. Meng, Y. Liu, G. Han, W. Yang, Y. Yu, Three-dimensional (Fe3O4/ZnO)@C Double-core@shell porous nanocomposites with enhanced broadband microwave absorption. Carbon 62, 356–364 (2020)
W. Chen, W.W. Wu, C. Zhou, S.F. Zhou, M.Y. Li, Y. Ning, Structural and magnetic properties evolution of Co-Nd substituted M-type hexagonal strontium ferrites synthesized by ball-milling-assisted ceramic process. J. Electron. Mater. 47, 2110–2119 (2018)
X. Guo, M. Li, Y. Liu, Y. Huang, S. Geng, W. Yang, Y. Yu, Hierarchical core-shell electrode with NiWO4 nanoparticles wrapped MnCo2O4 nanowire arrays on Ni foam for high-performance asymmetric supercapacitors. J. Colloid Interface Sci. 563, 405–413 (2020)
Y. Huang, W. Yang, Y. Yu, S. Hao, Ordered mesoporous spinel CoFe2O4 as efficient electrocatalyst for the oxygen evolution reaction. J. Electroanal. Chem. 840, 409–414 (2019)
Y. Wang, S. Bao, Y. Liu, W. Yang, Y. Yu, M. Feng, K. Li, Efficient photocatalytic reduction of Cr(VI) in aqueous solution over CoS2/g-C3N4-rGO nanocomposites under visible light. Appl. Surf. Sci. 510, 145495 (2020)
C.C. Liu, X.S. Liu, S.J. Feng, K.M.U. Rehman, M.L. Li, C. Zhang, H.H. Li, X.Y. Meng, Microstructure and magnetic properties of M-type strontium hexagonal ferrites with Y-Co substitution. J. Magn. Magn. Mater. 436, 126–129 (2017)
L.A. Trusov, E.A. Gorbachev, V.A. Lebedev, A.E. Sleptsova, L.V. Roslyakov, E.S. Kozlykova, A.V. Vasiliev, R.E. Dinnebier, M. Jansen, P.E. Kazin, Ca-Al double-substituted strontium hexaferrites with giant coercivity. Chem. Commun. 54, 479–482 (2018)
L. Wang, X.J. Li, J. Li, M. Liu, S.C. Xu, H.B. Li, Structural and electromagnetic properties of NiAlxFe2–xO4/SiO2 nanocomposite films deposited using a sol–gel spin-coating method. J. Magn. Magn. Mater. 444, 193–196 (2017)
S.M. Peymani-Motlagh, A. Sobhani-Nasab, M. Rostami, H. Sobati, M. Eghbali-Arani, M. Fasihi-Ramandi, M.R. Ganjali, M. Rahimi-Nasrabadi, Assessing the magnetic, cytotoxic and photocatalytic influence of incorporating Yb3+ or Pr3+ ions in cobalt–nickel ferrite. J. Mater. Sci. Mater. Electron. 30, 6902–6909 (2019)
J. Coates, Interpretation of infrared spectra: a practical approach, in Encyclopedia of Analytical Chemistry. ed. by R.A. Meyers (Wiley, New York, 2000), pp. 10815–108137
M. Sivakumar, A. Gedanken, W. Zhong, Y.W. Du, D. Bhattacharya, Y. Yeshurun, I. Felner, Nanophase formation of strontium hexaferrite fine powder by the sonochemical method using Fe(CO)5. J. Magn. Magn. Mater. 268, 95–104 (2004)
Acknowledgements
This work was supported by the National Natural Science Foundation of China (No. 11504132).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Wang, L., He, L., Li, J. et al. Effects of Al and Ca ions co-doping on magnetic properties of M-type strontium ferrites. J Mater Sci: Mater Electron 31, 22375–22384 (2020). https://doi.org/10.1007/s10854-020-04739-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-020-04739-z