Structural and electro-magnetic properties of low temperature co-fired BaSrTiO3 and NiCuZn ferrite composites for EMI filter applications

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

For the application of electro-magnetic interference filter, magneto-electric composites of spinel ferrite (Ni0.25Cu0.20Zn0.55)Fe2O4 and dielectric (Ba0.75Sr0.25)TiO3 have been prepared by a standard ceramic technique and the effects on structural, dielectric and electro-magnetic properties have been investigated. Ferrite-dielectric mixed powder is uniaxially pressed into toroids and pellets. Specimens are sintered at 950 °C. Powder X-ray diffraction (XRD) indicates a mixed phase of composites with spinel and perovskite phase. The microstructural analysis shows dense structure with some porosity. The variations in dielectric constant and loss tangent with frequency are also studied. The dielectric constant of composite continuously decreases and permeability increases with increasing ferrite content. Observations of P–E hysteresis loops and M–H hysteresis loops, respectively, confirm the dielectric and ferromagnetic nature of the composite samples.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  1. M.I. Bichurin, V.M. Petrov, Y.V. Kiliba, G. Srinivasan, Phys. Rev. B 66(13), 134404–134413 (2002)

    Article  Google Scholar 

  2. A. Bush, Y.K. Fetisov, K.E. Kamentsev, V.F. Meshcheryakov, G. Srinivasan, J. Magn. Magn. Mater. 258–259 45–47. (2003)

    Article  Google Scholar 

  3. L. Mitoseriu, V. Buscaglia, Phase Trans. 79(2), 1095–1121 (2006)

    Article  Google Scholar 

  4. A. Rafferty, Y. Gunko, R. Raghavendra, J. Eur. Ceram. Soc. 24, 2005–2013 (2004)

    Article  Google Scholar 

  5. H.I. Hsiang, T.H. Chen, Ceram. Int. 35, 2035–2039 (2009)

    Article  Google Scholar 

  6. C. Miao, J. Zhou, X. Cui, X. Wang, Z. Yue, L. Li, Mat. Sci. Eng. B 127, 1–5 (2006)

    Article  Google Scholar 

  7. H. Su, H. Zhang, X. Tang, J. Magn. Magn. Mater 321(18), 2763–2766 (2009)

    Article  Google Scholar 

  8. N. Kitahara, H. Kageyama, T. Kawasaki, K. Abe, H. Itoh, J. Takahashi, J. Ceram. Soc. Jpn. 121(1), 54–61 (2013)

    Article  Google Scholar 

  9. Y. Lin, Z. Zhu, J. Mater. Sci. 23, 733–738 (2012)

    Google Scholar 

  10. V.R. Mudinepalli, S.H. Song, B.S. Murty, Scripta Mater. 82, 9–12 (2014)

    Article  Google Scholar 

  11. M. Kumar, K.L. Yadav, J. Phys. Chem. Solids 68, 1791–1795 (2007)

    Article  Google Scholar 

  12. R.S. Devan, C.M. Kanamadi, S.A. Lokare, B.K. Chougule, Smart Mater. Struct. 15, 1877–1881 (2006)

    Article  Google Scholar 

  13. H. Su, H. Zhang, X. Tang, Y. Liu, J. Mater. Sci. 42, 2849–2853 (2007)

    Article  Google Scholar 

  14. M. Niyaifar, H. Shalilian, A. Hasanpour, H. Mohammadpour, J. Magn. 18(4), 391–394 (2013)

    Article  Google Scholar 

  15. M.L. Li, M.X. Xu, Mat. Res. Bull. 44, 937–942 (2009)

    Article  Google Scholar 

  16. M.L. Li, H. Liang, M.X. Xu, Mater. Chem. Phys. 112, 337–341 (2008)

    Article  Google Scholar 

  17. G. Zhang, S. Jiang, Y. Zeng, Y. Zhang, Q. Zhang, Y. Yu, J. Wang, Phys. Status Solidi A 208(11), 2699–2708 (2011)

    Article  Google Scholar 

  18. G. Zhang, S. Jiang, Y. Zeng, Y. Zhang, Q. Zhang, Y. Yu, J. Appl. Phys. 106, 034110–034115 (2009)

    Article  Google Scholar 

  19. J. Bera, P.K. Roy, Phys. B 363, 128–132 (2005)

    Article  Google Scholar 

  20. Z. Yue, L. Li, J. Zhou, H. Zhang, Z. Gui, Mat. Sci. Eng. B 64, 68–72 (1999)

    Article  Google Scholar 

  21. N. Adhlakha, K. Yadav, Smart Mat. Struct. 21, 11502–11529 (2012)

    Article  Google Scholar 

  22. K. Sun, Z. Lan, Z. Yu, X. Nie, L. Li, C. Liu, J. Magn. Mag. Mat. 320, 1180–1183 (2008)

    Article  Google Scholar 

  23. S.A. Khader, T. Sankarappa, Int. J. Adv. Res. Phys. Sci. 2, 21–27 (2015)

    Google Scholar 

  24. S.N. Babu, S.G. Min, L. Malkinski, J. Appl. Phys. 109, 07D911 (2011)

    Article  Google Scholar 

  25. J.J. Shrotri, S.D. Kulkarni, C.E. Deshpande, S.K. Dtate, Mater. Chem. Phys. 59, 1–5 (1999)

    Article  Google Scholar 

  26. K.E. Maalam, M.B. Ali, H.E. Moussaoui, O. Mounkachi, M. Hamedoun, R. Masrour, E.K. Hlil, A. Benyoussef, J. Alloys Compd. 622, 761–764 (2015)

    Article  Google Scholar 

  27. P.K. Roy, J. Bera, Mat. Chem. Phys. 132, 354–357 (2012)

    Article  Google Scholar 

  28. H. Su, H. Zhang, X. Tang, J. Alloys Compd. 475, 683–685 (2008)

    Article  Google Scholar 

  29. X. Qi, J. Zhou, Z. Yue, Z. Gui, L. Li, S. Buddhudu, Adv. Funct. Mater. 14, 920–926 (2004)

    Article  Google Scholar 

  30. Y.A. Wang, Y.B. Wang, W. RAO, J.X. Gao, W.L. Zhou, J. Yu, Chin. Phys. Lett. 29(6), 067701–067704 (2012)

    Article  Google Scholar 

  31. L. Zhang, J.W. Zhai, W.F. Mo, X. Yao, Solid State Sci. 13, 321–325 (2011)

    Article  Google Scholar 

  32. W. Chen, Z.H. Wang, W. Zhu, O.K. Tan, J. Phys. D 42, 075421–075425 (2009)

    Article  Google Scholar 

  33. E. Melagiriyappa, H.S. Jayanna, B.K. Chougule, Mat. Chem. Phys. 112, 68–73 (2008)

    Article  Google Scholar 

  34. S.S. Kumbhar, M.A. Mahadik, V.S. Mohite, Y.M. Hunge, P.K. Chougule, K.Y. Rajpure, C.H. Bhosale, J. Mater. Sci. 27, 3799–3811 (2016)

    Google Scholar 

  35. K.O. Low, F.R. Sale, J. Magn. Magn. Mater. 246, 30–35 (2002)

    Article  Google Scholar 

Download references

Acknowledgements

Author, P. K. Roy, wishes to thank IIT (BHU) for providing facilities.

Author information

Authors and Affiliations

  1. Department of Ceramic Engineering, IIT (BHU), Varanasi, 221005, UP, India

    SK. S. Hossain & P. K. Roy

Authors
  1. SK. S. Hossain
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. P. K. Roy
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to P. K. Roy.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Hossain, S.S., Roy, P.K. Structural and electro-magnetic properties of low temperature co-fired BaSrTiO3 and NiCuZn ferrite composites for EMI filter applications. J Mater Sci: Mater Electron 28, 18136–18144 (2017). https://doi.org/10.1007/s10854-017-7759-8

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-017-7759-8

Search

Navigation