Abstract
Nanocrystalline TiO2 with 3–10 nm in diameter was prepared with a surfactant-template method. Dye-sensitized solar cells were assembled using the prepared nanocrystalline TiO2 with large surface area and high crystallinity, which achieved significant higher Jsc when compared to cells fabricated with bigger particles of 25 nm in diameter. In the cells with nanocrystalline TiO2, the sintering temperature drastically affected the conversion performance of the cells.
Similar content being viewed by others
References
B. O’Regant, M. Grätzel, Nature 353 737 (1991)
M. Grätzel, Nature 414 338 (2001)
M. Grätzel, J. Photochem. Photobiol. A: Chem, 164 3 (2004)
S. Kambe, K. Murakoshi, T. Kitamura, Y. Wada, S. Yanagida, H. Kominami, Y. Kera, Sol. Energy Mater. Sol. Cells 61 427 (2000)
S. Itoa, T. Kitamurab, Y. Wada, S. Yanagida, Sol. Energy Mater. Sol. Cells 76 3 (2003)
Y. Li, J. Hagen, W. Schaffrath, P. Otschik, D. Haarer, Sol. Energy Mater. Sol. Cells 56 167 (1999)
Z. Wang, H. Kawauchi, T. Kashima, H. Arakawa, Coord. Chem. Rev. 248 1381 (2004)
M. Zukalova, A. Zukal, L. Kavan, M.K. Nazeeruddin, P. Liska, M. Gratzel, Nano. Lett. 5 1789 (2005)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jiu, J., Isoda, S., Adachi, M. et al. Dye-sensitized solar cell based on nanocrystalline TiO2 with 3–10 nm in diameter. J Mater Sci: Mater Electron 18, 593–597 (2007). https://doi.org/10.1007/s10854-006-9100-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-006-9100-9