Abstract
YCa4O(BO3)3 crystal having various concentration of Ce ions were synthesized by solid-state diffusion technique. XRD pattern of the sample confirmed the formation of the sample. Thermoluminescence (TL) and lyoluminescence (LL) of the γ-ray-irradiated sample were recorded. Two distinct peaks around 160 and 277 °C were observed in TL glow curves. TL intensity increased with increasing dopant concentration up to 2 mol%. A single sharp peak was observed in the LL glow curve of the sample. It was found that both TL and LL increased almost linearly with γ-ray doses up to 1.5 kGy. Photoluminescence (PL) of the sample was recorded to find the role of rare earth ion doped in YCa4O(BO3)3. PL emission spectrum showed two peaks lying very close to each other around 390 nm which are characteristics of 5d → 4f transition of Ce3+ ions. When LL of samples was recorded after removing the TL peaks it did not show any emission. This indicates that emission centres responsible for TL are also responsible for LL.
Similar content being viewed by others
References
Mckeever SWS (1985) Thermoluminescence of solids. Cambridge University Press, Cambridge, p 127
Li J, Hao JQ, Zhang CX, Tang Q, Zhang YL, Su Q, Wang S (2004) Nucl Instrum Methods Phys Res B Beam Interact Mater Atoms 222:577
Furetta C, Prokic M, Salamon R, Prokic V, Kitis G (2001) Nucl Instrum Methods Phys Res Sect A Accel Spectrom Detect Assoc Equip 456:411
Li J, Hao JQ, Li CY, Zhang CX, Tang Q, Zhang YL, Su Q, Wang SB (2005) Radiat Meas 39:229
Furetta C, Kitis G, Weng PS, Chu TC (1999) Nucl Instrum Methods Phys Res Sect A Accel Spectrom Detect Assoc Equip 420:441
Liu LY, Zhang YL, Hao JQ, Li CY, Tang Q, Zhang CX, Su Q (2005) Phys Status Solidi A Appl Res 202:2800
Liu LY, Zhang YL, Hao JQ, Li CY, Tang Q, Zhang CX, Su Q (2006) Mater Lett 60:639
Norrestam R, Nygran J-O Bovin M et al (1992) Chem Mater 4:734
Widdmann E, Schmidt GC (1895) Annal Phys Chem 604:54
Dhoble SJ, Moharil SV (1992) J Lumin 51:209
Dhoble SJ (2002) Radiat Protec Dosim 100(1–4):285
Kher RS, Upadhyay AK, Dhoble SJ, Khokhar MSK (2008) Ind J Pure Appl Phys 46:607
Upadhyay A, Dhoble SJ, Rai R, Kher RS (2008) Nucl Instr Meth Phys Res B 266:2549
Yosida T, Yamaga M, Lee D, Jhan TP, Gallagher HG, Henderson B (1997) J Lumin Cond Matter 9(18):3733
Porwal NK, Kadam RM, Sheshagiri TK, Natrajan V, Dhobale AR, Page AG (2005) Radiat Measure 40(1):69
Ahnstrom G (1965) Acta Chem Scand 19:300
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mishra, G.C., Upadhyay, A.K., Kher, R.S. et al. Thermoluminescence and lyoluminescence in γ-ray irradiated and Ce3+-doped YCa4O(BO3)3 phosphors. J Mater Sci 46, 7275–7278 (2011). https://doi.org/10.1007/s10853-011-5687-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-011-5687-1