Abstract
A pure aluminum matrix composite reinforced by Bi2O3-coated Al18B4O33 whisker was fabricated by squeeze casting method. The effects of Bi2O3 coating on the whisker/matrix wettability and the ultimate tensile strength and elongation to fracture of the composite are investigated. The results show that Bi2O3 coating can react with aluminum matrix during casting process, which improves the whisker/matrix wettability. Moreover, the ultimate tensile strength and elongation to fracture of the composite attain the maximum values at the mass ratio of 40:1 between whisker and Bi2O3 coating.
Similar content being viewed by others
References
Suganuma K, Fujita T, Suzuki N, Niihara K (1990) J Mater Sci Lett 9:633
Zhu SJ, Iizuka T (2003) Comp Sci Tech 63:265
Fei WD, Li YB (2004) Mater Sci Eng A27:379
Bi G, Rao Q, Xi F (2004) Mater Lett 58:833
Fei WD, Jiang XD, Li C, Yao CK (1996) J Mater Sci Lett 15:1966
Hu J, Fei WD, Li C, Yao CK (1990) J Mater Sci Lett 9:633
Levi CG, Abbaschian GJ, Mehrabian R (1978) Metall Trans A9:697
Kulkarni AG (1979) J Mater Sci 14:595
Leon CA, Drew RAL (2000) J Mater Sci 35:4763
Dellanney F, Rozen L, Deryttere A (1987) J Mater Sci 22:1
Kimura Y (1984) J Mater Sci 19:3107
Li ZJ, Fei WD (2007) Comp Sci Tech 67:963
Zhang HQ, Zhang JZ, Lin YS (2001) Practice chemical handbook. Science Publishing Company Press, p 123 (In Chinese)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, Z.J., Wang, L.D., Yue, H.Y. et al. Effect of Bi2O3 coating on interfacial wettability and tensile properties of Al18B4O33w/Al composite. J Mater Sci 42, 9355–9358 (2007). https://doi.org/10.1007/s10853-007-1862-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-007-1862-9