Abstract
Nb-doped SrBi4Ti4O15 (SBT) was produced by conventional method. Structural and ferroelectric properties of SBT were examined as a function of niobium composition. Analyzing the structure futures of SBT by XRD, XPS and Raman spectrum, Nb5+ substituted Ti4+ to form NbO6 octahedron and did not change the structure of SBT. The XRD patterns indicated the formation of the single phase of SBT for x = 0.01and 0.03 and secondary phase of Sr3Ti2O7 appeared when x > 0.1. To compare the effect of Nb doping, the ferroelectric properties (hysteresis loop, piezoelectric coefficient) of Nb-doped SBT were measured. The SBT doped with x = 0.15 was found to exhibit higher remanent polarization with d 33 = 17 pC/N.
Similar content being viewed by others
References
M.V. Gelfuso, J. Am. Ceram. Soc. 82(9), 2368–2372 (1999)
T. Ogawa, J. Eur. Ceram. Soc. 24, 1517–1520 (2004)
Ph. Boullay, G. Trolliard, D. Mercurio, J. Solid State Chem. 164, 252–260 (2002)
C.H. Hervoches, A. Snedden, R. Riggs, S.H. Kilcoyne, P. Manuel, P. Lightfoot, J. Solid State Chem. 164, 280–291 (2002)
A.S. Bhalla, R. Guo, R. Roy, Mat. Res. Innovat. 4, 3–26 (2000)
Y.P. Chen, Y.Y. Yao, Z.H. Bao, P. Bao, J.S. Zhu, Y.N. Wang, Mater. Lett. 57, 3623–3628 (2003)
H. Hao, H.X. Liu, M.H. Cao, X.M. Min, S.X. Ouyang, Appl. Phys. A 85(1), 69–73 (2006)
P. S. Dobal, R. S. Katiyar, J. Raman Spectrosc. 33, 405–423 (2002)
P.J. Klar, T. Rentschler, Solid State Commun. 103(6), 341–345 (1997)
Y.L. Dua, G. Chena, M.S. Zhang, Solid State Commun. 131, 313–317 (2004)
J. Zhu, X.-Y. Mao, X.-B. Chen, Solid State Commun. 130, 363–366 (2004)
R.Z. Hou, X.M. Chen, Solid State Commun. 130, 469–472 (2004)
Acknowledgement
The authors would like to acknowledge the support of the Natural Science Foundation of China (NSFC, Grant no. 50472016, 50502027), the main project of the Ministry of Education of China (MOE) and 973-Project (2002 CB613303) of China.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hao, H., Liu, H. & Ouyang, S. Structure and ferroelectric property of Nb-doped SrBi4Ti4O15 ceramics. J Electroceram 22, 357–362 (2009). https://doi.org/10.1007/s10832-007-9180-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10832-007-9180-9