Corrosion of Steel in MSE Walls Due to Deicers and Backfill Aggregates

  • Original Paper
  • Published:
Geotechnical and Geological Engineering Aims and scope Submit manuscript

Abstract

Corrosion of the reinforced steel is the main cause that afflicts the long-term performance of mechanically stabilized earth (MSE) walls. The deicing salts used on pavements to melt down snow is one of the major reasons of corrosion of these reinforced steels. The aggressiveness of deicers in terms of corrosion of reinforced steel was estimated through the potentiodynamic polarization technique at various concentrations of deicers. The present study aims to determine the corrosion behavior on bare steel in presence of various individual deicing salt or deicers e.g., sodium chloride, calcium chloride, magnesium chloride and potassium acetate at various concentration i.e., 0.25, 0.50 and 1.00 M. In addition, the corrosivity of two backfill aggregates i.e., natural aggregate and recycled concrete aggregate, was compared. The results show that the corrosion effect of deicers on reinforced steel of MSE wall depends on its chemical composition and concentration. Among the deicers used, the sodium chloride was most aggressive and potassium acetate is the least aggressive for the bare steel. The pH and electrical resistivity values of the natural and recycled concrete aggregates were compared with the standards provided by American Association of State Highway and Transportation Officials and found to be non-corrosive. The corrosion rate of both the aggregates on bare steel were inappreciable and while analyzing the corrosiveness of these two aggregates, recycled concrete aggregate sample was observed to be more aggressive than the natural aggregate.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  • AASHTO (2010) LRFD Bridge design specifications, 5th edn. American Association of State Highway and Transportation Officials, Washington

    Google Scholar 

  • Anderson PL, Gladstone RA, Sankey JE (2012a) State of the practice of MSE wall design for highway structures. In: Geotechnical engineering state of the art and practice: keynote lectures from GeoCongress, pp 443–463

  • Anderson P, Gladstone R, Sankey J (2012b) State of the practice of MSE wall design for highway structures. In: Geotechnical engineering state of the art and practice, pp 1–21. doi:10.1061/9780784412138.0018

  • Andrade C, Alonso C, Sarrıa J (2002) Corrosion rate evolution in concrete structures exposed to the atmosphere. Cement Conc Compos24(1):55–64

    Article  Google Scholar 

  • Asgari H, Toroghinejad MR, Golozar MA (2009) Effect of coating thickness on modifying the texture and corrosion performance of hot-dip galvanized coatings. Curr Appl Phys 9(1):59–66

    Article  Google Scholar 

  • ASTM G102–89, (2010) Standard practice for calculation of corrosion rates and related information from electrochemical measurements. ASTM International, West Conshohocken

    Google Scholar 

  • ASTM G3–89 (2010) Standard practice for conventions applicable to electrochemical measurements in corrosion testing. ASTM International, West Conshohocken

    Google Scholar 

  • ASTM G59–97 (2014) Standard test method for conducting potentiodynamic polarization resistance measurements. ASTM International, West Conshohocken

    Google Scholar 

  • Baboian R (2002) NACE corrosion engineer's reference book, 3rd edn. NACE Press, Houston

    Google Scholar 

  • Beben D (2015) Backfill corrosivity around corrugated steel plate culverts. J Perform Constr Facil ASCE 29(6):1–10

    Article  Google Scholar 

  • Berg R, Christopher B, Samtani N (2009) Design and construction of mechanically stabilized earth walls and reinforced soil slopes—volume II. Federal Highway Administration (FHWA), report no. FHWA-NHI-10–025.

  • Bligh RP, Briaud J-L, Kim KM, Abu-Odeh A (2010) Design of roadside barrier systems placed on MSE retaining walls. NCHRP REPORT 663, Project 22–20.

  • Bourgeois E, Corfdir A, Chau TL (2013) Analysis of long-term deformations of MSE walls based on various corrosion scenarios. Soils Found 53(2):259–271

    Article  Google Scholar 

  • Bronson, A., Rocha, S., Nazarian, S., and Borrock, D. M., 2013, Characterization of coarse backfill materials for prevention of corrosion of MSE metallic wall reinforcement (No. FHWA/TX-11/0–6359–1).

  • Casey PC, Alwan CW, Kline CF, Landgraf GK, Linsenmayer KR (2014) Impacts of using salt and salt brine for roadway deicing (No. FHWA-ID-14–231).

  • da Costa Pereira RF, de Oliveira ESD, de Andrade Lima MAG, Cezar SLD (2015) Corrosion of galvanized steel under different soil moisture contents. Mater Res 18(3):563–568

    Article  Google Scholar 

  • Elias V, Fishman KL, Christopher BR, Berg RR (2000) US Department of Transportation Federal Highway Administration, Corrosion/Degradation of Soil Reinforcement for Mechanically Stabilized Earth Walls and Reinforced Soils Slopes. Publication no. FHWA-NHI-00–044, 1

  • Elias V, Fishman KL, Christopher BR, Berg RR (2009) Corrosion/degradation of soil reinforcements for mechanically stabilized earth walls and reinforced soil slopes. (FHWA-NHI-09–087).

  • Fay L, Volkening K, Gallaway C, Shi X (2008) Performance and impacts of current deicing and anti-icing products: user perspective versus experimental data. In: 87th annual meeting of the transportation research board, Washington, DC.

  • Gerber TM, Billings DA (2010) Assessing corrosion of MSE wall reinforcement (No. UT-10.20).

  • Holz RD, Christopher BR, Berg RR (1998) Geosynthetic design and construction guidelines (No. FHWA HI-95–038).

  • Kelly RG, Scully JR, Shoesmith D, Buchheit RG (2002) Electrochemical techniques in corrosion science and engineering. CRC Press, Boca Raton

    Book  Google Scholar 

  • McGraw J, Iverson D, Schmidt, G (2001) Effect of corrosion inhibitive deicers (draft report). Minnesota Department of Transportation, August 2001

  • Perry JH, Chilton CH (1973) Chemical engineer’s handbook. McGraw Hill, New York

    Google Scholar 

  • Raeburn CL, Monkul MM, Pyles MR (2008) Evaluation of corrosion of metallic reinforcements and connections in MSE retaining walls (No. FHWA-OR-RD-08–10).

  • Revie RW (2008) Corrosion and corrosion control: an introduction to corrosion science and engineering, 4th edn. Wiley, New York

    Book  Google Scholar 

  • Samouëlian A, Cousin I, Tabbagh A, Bruand A, Richard G (2005) Electrical resistivity survey in soil science: a review. Soil and Tillage Research 83(2):173–193

    Article  Google Scholar 

  • Shi X, Song S (2005) Evaluating the corrosivity of chemical deicers: an electrochemical technique. In: 16th international corrosion congress. Beijing, China

  • Shi X, Fay L, Yang Z, Nguyen TA, Liu Y (2009) Corrosion of deicers to metals in transportation infrastructure: introduction and recent developments. Corros Rev 27(1):23

    Article  Google Scholar 

  • Sjögren L, Camitz G, Peultier J, Jacques S, Baudu V, Barrau F, Chareyre B, Bergquist A, Pourbaix A, Carpentiers P (2011) Corrosion resistance of stainless steel pipes in soil. Mater Corros 62(4):299–309

    Article  Google Scholar 

  • Soil Science Society of America (2008) Glossary of soil science terms 2008. ASA-CSSA-SSSA

  • Soil Survey Division (1993) Soil survey manual. United States Department of Agriculture

  • Tahir SNFMM, Noor NM, Yahaya N, Sing LK (2015) Relationship between in-situ measurement of soil parameters and metal loss volume of X70 carbon steel coupon. Asian J Sci Res 8(2):205

    Article  Google Scholar 

  • Tam VWY, Tam CM, Le KN (2007) Removal of cement mortar remains from recycled aggregate using pre-soaking approaches. Resour Conserv Recycl 50(1):82–101

    Article  Google Scholar 

  • Tanyu BF, Sabatini PJ, Berg RR (2008) Earth retaining structures. US Department of Transportation, Federal Highway Administration, FHWA-NHI-07–071, Washington, DC

  • Xi, Y, Xie Z (2002) Corrosion effects of magnesium chloride and sodium chloride on automobile components (No. CDOT-DTD-R-2002–4). Colorado Department of Transportation, Research Branch

  • Zhang XG (1996) Galvanic corrosion of zinc and its alloys. J Electrochem Soc 143(4):1472–1484

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Civil and Environmental Engineering, Southern Illinois University Carbondale, Carbondale, IL, 62901, USA

    Prabir K. Kolay & Dipesh Tajhya

  2. Department of Mechanical Engineering and Energy Process, Southern Illinois University Carbondale, Carbondale, IL, 62901, USA

    Kanchan Mondal

Authors
  1. Prabir K. Kolay
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dipesh Tajhya
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Kanchan Mondal
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Prabir K. Kolay.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Kolay, P.K., Tajhya, D. & Mondal, K. Corrosion of Steel in MSE Walls Due to Deicers and Backfill Aggregates. Geotech Geol Eng 38, 2493–2507 (2020). https://doi.org/10.1007/s10706-019-01164-w

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10706-019-01164-w

Keywords

Search

Navigation