Abstract
A series of poly(N,N-diethylacrylamide-co-sodium acrylate) with a degree of crosslinking of 1 mol% have been prepared as thermosensitive superabsorbents for water. The critical swelling temperatures or the volume phase transition temperature (VPTT) and the water absorption capacity of the polymers can be modulated by varying the amount of sodium acrylate (0–60 mol%) in the copolymers. The water absorption and swelling properties of the different hydrogels have been studied as function of temperature. The crosslinked copolymers can absorb large amounts of water at ambient temperatures and dehydrate at higher temperatures with relative ease, making the absorbent materials thermally responsive and thus reusable. The water absorption capacity of the copolymers depends on the pH of the media as the acrylate monomer has a higher water absorption in its deprotonated state. Added urea in the media raises and sharpens the VPTT values of the copolymers containing sodium acrylate.
Similar content being viewed by others
References
Kazanskii, K.S. and Dubrovskii, S.A., Adv. Polym. Sci., 1992, 104: 97
Smetanyuk, V.I., Pet. Chem., 1995, 35: 248
Li, Y.F., Li, X.Z., Zhou, L.C., Zhu, X.X. and Li, B.N., Polym. Adv. Technol., 2004, 15: 34
Buchholz, F.L., Chemtech, 1994, 38
Yoshida, R., Sakai, K., Okano, T., Sakurai, Y., Bae, Y.H. and Kim S.W., J. Biomater. Sci., Polym. Ed., 1991, 3: 155
Schild, H.G., Prog. Polym. Sci., 1992, 17: 163
Liu, H.Y., Avoce, D., Song, Z. and Zhu, X.X., Macromol. Rapid Commun., 2001, 22: 675
Avoce, D., Liu, H.Y. and Zhu, X.X., Polymer, 2003, 44: 1081
Osada, Y. and Gong, J.P., Adv. Mater., 1998, 10: 827
Plestil, J., Ilavsky, M., Pospisil, H., Hlavata, D., Ostanevich, Y.M., Degovics, G., Kriechbaum, M. and Laggner, P., Polymer, 1993, 34: 4846
Idziak, I., Avoce, D., Lessard, D., Gravel, D. and Zhu, X.X., Macromolecules, 1999, 32: 1260
Liu, H.Y. and Zhu, X.X., Polymer, 1999, 40: 6985
Nichifor, M. and Zhu, X.X., Polymer, 2003, 44: 3053
Lessard, D.G., Ousalem, M. and Zhu, X.X., Can. J. Chem., 2001, 79: 1870
Lessard, D., Ousalem, M., Zhu, X.X., Eisenberg, A. and Carreau, P.J., J. Polym. Sci. Part B: Polym. Phys., 2003, 41: 1627
Kawasaki, H., Sasaki, S. and Maeda, H., J. Phys. Chem. B, 1997, 101: 5089
Yu, H. and Grainger, D.W., J. Appl. Polym. Sci., 1993, 49: 1553
Suzuki, A. and Suzuki, H., J. Chem. Phys., 1995, 103: 4706
Zhang, Y.Q., Tanaka, T. and Shibayama, M., Nature, 1992, 360: 142
Inomata, H. and Saito, S., Langmuir, 1992, 2: 1030
Inomata, H., Goto, S., Otake, K. and Saito, S., Langmuir, 1992, 8: 687
Kawasaki, H., Sasaki, S., Maeda, H., Mihara, S., Tokita, M. and Komai, T., J. Phys. Chem., 1996, 100: 16282
Zhang, W., Zou, S., Wang, C. and Zhang, X., J. Phys. Chem. B, 2000, 104: 10258
Ilmain, F., Tanaka, T. and Kokufuta, E., Nature, 1991, 349: 400
Sasaki, S., Kawasaki, H. and Maeda, H., Macromolecules, 1997, 30: 1847
Author information
Authors and Affiliations
Corresponding author
Additional information
The work was financially supported by AbsorbPlus Textiles Inc., NSERC of Canada and Canada Research Chair Program.
Rights and permissions
About this article
Cite this article
Lessard, D.G., Li, Yf. & Zhu, X.X. Thermosensitive superabsorbents based on poly(N,N-diethylacrylamide-co-sodium acrylate). Chin J Polym Sci 30, 873–878 (2012). https://doi.org/10.1007/s10118-012-1186-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-012-1186-3