Effects of post surface treatments including Er:YAG laser with different parameters on the pull-out bond strength of the fiber posts

  • Original Article
  • Published:
Lasers in Medical Science Aims and scope Submit manuscript

Abstract

This study aims to evaluate the effects of Er:YAG laser irradiation under different power settings on the pull-out bond strengths of fiber-reinforced composite posts. The crowns of single-rooted 60 teeth were removed by separation and the root canals were cleaned and shaped. Root canals were filled and post spaces were prepared. Sixty fiber posts were divided into five groups according to surface treatment methods as follows: an untreated control group, a sandblasting-coated group, and three groups undergoing surface preparation with Er:YAG laser under three different power settings (150, 300, and 450 mJ at 10 Hz for 60 s at 100-μs pulse duration). After root canal procedures, fiber posts were cemented to the root canal. After all of the specimens were set, pull-out tests were performed using a universal testing machine at a crosshead speed of 2 mm/min. The data were analyzed using one-way ANOVA and Tukey post-hoc test (p < 0.05). The pull-out strength values ranged between 5.26 and 6.76 Mpa. The lowest values were observed in the groups without surface treatment. Surface treatment applied by 4.5-W Er:YAG laser increased the pull-out bond strength compared to the control group (p < 0.05). 4.5-W Er:YAG laser irradiation increased the pull-out bond strength of fiber posts to resin cement.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3

Similar content being viewed by others

References

  1. Monticelli F, Toledano M, Tay FR, Cury AH, Goracci C, Ferrari M (2006) Post-surface conditioning improves interfacial adhesion in post/core restorations. Dent Mater 22:602–609. doi:10.1016/j.dental.2005.05.018

    Article  CAS  PubMed  Google Scholar 

  2. Sadek FT, Monticelli F, Goracci C, Tay FR, Cardoso PE, Ferrari M (2007) Bond strength performance of different resin composites used as core materials around fiber posts. Dent Mater 23:95–99. doi:10.1016/j.dental.2005.12.005

    Article  CAS  PubMed  Google Scholar 

  3. Vano M, Goracci C, Monticelli F, Tognini F, Gabriele M, Tay FR et al (2006) The adhesion between fibre posts and composite resin cores: the evaluation of microtensile bond strength following various surface chemical treatments to posts. Int Endod J 39:31–39. doi:10.1111/j.1365-2591.2005.01044.x

    Article  CAS  PubMed  Google Scholar 

  4. Martinez-Insua A, da Silva L, Rilo B, Santana U (1998) Comparison of the fracture resistances of pulpless teeth restored with a cast post and core or carbon-fiber post with a composite core. J Prosthet Dent 80:527–532

    Article  CAS  PubMed  Google Scholar 

  5. Bateman G, Ricketts DN, Saunders WP (2003) Fibre-based post systems: a review. Br Dent J 195:43–48. doi:10.1038/sj.bdj.4810278, discussion 37

    Article  CAS  PubMed  Google Scholar 

  6. Mannocci F, Bertelli E, Watson TF, Ford TP (2003) Resin-dentin interfaces of endodontically treated restored teeth. Am J Dent 16:28–32

    PubMed  Google Scholar 

  7. Qualtrough AJ, Mannocci F (2003) Tooth-colored post systems: a review. Oper Dent 28:86–91

    CAS  PubMed  Google Scholar 

  8. Lassila LV, Tanner J, Le Bell AM, Narva K, Vallittu PK (2004) Flexural properties of fiber reinforced root canal posts. Dent Mater 20:29–36

    Article  CAS  PubMed  Google Scholar 

  9. de Sousa Menezes M, Queiroz EC, Soares PV, Faria-e-Silva AL, Soares CJ, Martins LR (2011) Fiber post etching with hydrogen peroxide: effect of concentration and application time. J Endod 37:398–402. doi:10.1016/j.joen.2010.11.037

    Article  PubMed  Google Scholar 

  10. Monticelli F, Osorio R, Albaladejo A, Aguilera FS, Ferrari M, Tay FR et al (2006) Effects of adhesive systems and luting agents on bonding of fiber posts to root canal dentin. J Biomed Mater Res B Appl Biomater 77:195–200. doi:10.1002/jbm.b.30420

    Article  PubMed  Google Scholar 

  11. Alaçam T NL, Alaçam A (1998) İleri Restorasyon Teknikleri. Ankara: Polat Yayınları

  12. Monticelli F, Osorio R, Sadek FT, Radovic I, Toledano M, Ferrari M (2008) Surface treatments for improving bond strength to prefabricated fiber posts: a literature review. Oper Dent 33:346–355. doi:10.2341/07-86

    Article  PubMed  Google Scholar 

  13. Mazzitelli C, Ferrari M, Toledano M, Osorio E, Monticelli F, Osorio R (2008) Surface roughness analysis of fiber post conditioning processes. J Dent Res 87:186–190

    Article  CAS  PubMed  Google Scholar 

  14. Sahafi A, Peutzfeld A, Asmussen E, Gotfredsen K (2004) Effect of surface treatment of prefabricated posts on bonding of resin cement. Oper Dent 29:60–68

    PubMed  Google Scholar 

  15. Valandro LF, Yoshiga S, de Melo RM, Galhano GA, Mallmann A, Marinho CP et al (2006) Microtensile bond strength between a quartz fiber post and a resin cement: effect of post surface conditioning. J Adhes Dent 8:105–111

    PubMed  Google Scholar 

  16. Sahar-Helft S (2009) [The laser technology in dentistry]. Refuat Hapeh Vehashinayim 26: 12–19, 59

  17. Walsh JT Jr, Cummings JP (1994) Effect of the dynamic optical properties of water on midinfrared laser ablation. Lasers Surg Med 15:295–305

    Article  PubMed  Google Scholar 

  18. Hibst R, Keller U (1989) Experimental studies of the application of the Er:YAG laser on dental hard substances: I. Measurement of the ablation rate. Lasers Surg Med 9:338–344

    Article  CAS  PubMed  Google Scholar 

  19. Mannocci F, Sherriff M, Watson TF, Vallittu PK (2005) Penetration of bonding resins into fibre-reinforced composite posts: a confocal microscopic study. Int Endod J 38:46–51. doi:10.1111/j.1365-2591.2004.00900.x

    Article  CAS  PubMed  Google Scholar 

  20. Akgungor G, Akkayan B (2006) Influence of dentin bonding agents and polymerization modes on the bond strength between translucent fiber posts and three dentin regions within a post space. J Prosthet Dent 95:368–378. doi:10.1016/j.prosdent.2006.02.027

    Article  CAS  PubMed  Google Scholar 

  21. Aksornmuang J, Foxton RM, Nakajima M, Tagami J (2004) Microtensile bond strength of a dual-cure resin core material to glass and quartz fibre posts. J Dent 32:443–450. doi:10.1016/j.jdent.2004.03.001

    Article  CAS  PubMed  Google Scholar 

  22. Bell AM, Lassila LV, Kangasniemi I, Vallittu PK (2005) Bonding of fibre-reinforced composite post to root canal dentin. J Dent 33:533–539. doi:10.1016/j.jdent.2004.11.014

    Article  PubMed  Google Scholar 

  23. Balbosh A, Kern M (2006) Effect of surface treatment on retention of glass-fiber endodontic posts. J Prosthet Dent 95:218–223. doi:10.1016/j.prosdent.2006.01.006

    Article  CAS  PubMed  Google Scholar 

  24. Xible AA, de Jesus Tavarez RR, de Araujo Cdos R, Bonachela WC (2006) Effect of silica coating and silanization on flexural and composite-resin bond strengths of zirconia posts: an in vitro study. J Prosthet Dent 95:224–229. doi:10.1016/j.prosdent.2005.12.010

    Article  CAS  PubMed  Google Scholar 

  25. Cardoso MV, Coutinho E, Ermis RB, Poitevin A, Van Landuyt K, De Munck J et al (2008) Influence of Er, Cr:YSGG laser treatment on the microtensile bond strength of adhesives to dentin. J Adhes Dent 10:25–33

    PubMed  Google Scholar 

  26. Esteves-Oliveira M, Zezell DM, Apel C, Turbino ML, Aranha AC, Eduardo Cde P et al (2007) Bond strength of self-etching primer to bur cut, Er, Cr:YSGG, and Er:YAG lased dental surfaces. Photomed Laser Surg 25:373–380. doi:10.1089/pho.2007.2044

    Article  PubMed  Google Scholar 

  27. Tachibana A, Marques MM, Soler JM, Matos AB (2008) Erbium, chromium:yttrium scandium gallium garnet laser for caries removal: influence on bonding of a self-etching adhesive system. Lasers Med Sci 23:435–441. doi:10.1007/s10103-007-0503-5

    Article  PubMed  Google Scholar 

  28. Kayano T, Ochiai S, Kiyono K, Yamamoto H, Nakajima S, Mochizuki T (1989) Effects of Er:YAG laser irradiation on human extracted teeth. Kokubyo Gakkai Zasshi 56:381–392

    Article  CAS  PubMed  Google Scholar 

  29. Cavalcanti AN, Pilecki P, Foxton RM, Watson TF, Oliveira MT, Gianinni M et al (2009) Evaluation of the surface roughness and morphologic features of Y-TZP ceramics after different surface treatments. Photomed Laser Surg 27:473–479. doi:10.1089/pho.2008.2293

    Article  CAS  PubMed  Google Scholar 

  30. Jacobsen NL, Mitchell DL, Johnson DL, Holt RA (1997) Lased and sandblasted denture base surface preparations affecting resilient liner bonding. J Prosthet Dent 78:153–158

    Article  CAS  PubMed  Google Scholar 

  31. Spohr AM, Borges GA, Junior LH, Mota EG, Oshima HM (2008) Surface modification of In-Ceram Zirconia ceramic by Nd:YAG laser, Rocatec system, or aluminum oxide sandblasting and its bond strength to a resin cement. Photomed Laser Surg 26:203–208. doi:10.1089/pho.2007.2130

    Article  CAS  PubMed  Google Scholar 

  32. Akin H, Tugut F, Akin GE, Guney U, Mutaf B (2012) Effect of Er:YAG laser application on the shear bond strength and microleakage between resin cements and Y-TZP ceramics. Lasers Med Sci 27:333–338. doi:10.1007/s10103-011-0883-4

    Article  PubMed  Google Scholar 

  33. Tuncdemir AR, Yildirim C, Guller F, Ozcan E, Usumez A (2013) The effect of post surface treatments on the bond strength of fiber posts to root surfaces. Lasers Med Sci 28:13–18. doi:10.1007/s10103-012-1053-z

    Article  PubMed  Google Scholar 

Download references

Conflict of Interest

The authors deny any conflict of interest related to this study.

Author information

Authors and Affiliations

  1. Department of Endodontics, Faculty of Dentistry, İzmir Katip Celebi University, İzmir, 35620, Turkey

    Hakan Arslan

  2. Department of Prosthodontics, Faculty of Dentistry, Ataturk University, Erzurum, 25040, Turkey

    Duygu Kurklu & Cenk Burak Yılmaz

  3. Department of Endodontics, Faculty of Dentistry, Ataturk University, Erzurum, 25040, Turkey

    Leyla Benan Ayrancı & Ertugrul Karatas

  4. Department of Restorative Dentistry, Faculty of Dentistry, Akdeniz University, Antalya, 07058, Turkey

    Cagatay Barutcigil

  5. Department of Endodontics, Faculty of Dentistry, Erciyes University, Kayseri, 38039, Turkey

    Hüseyin Sinan Topçuoğlu

  6. Department of Endodontics, Faculty of Dentistry, Ataturk University, Erzurum, 25240, Turkey

    Leyla Benan Ayrancı

Authors
  1. Hakan Arslan
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Duygu Kurklu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Leyla Benan Ayrancı
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Cagatay Barutcigil
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Cenk Burak Yılmaz
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Ertugrul Karatas
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Hüseyin Sinan Topçuoğlu
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Leyla Benan Ayrancı.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Arslan, H., Kurklu, D., Ayrancı, L.B. et al. Effects of post surface treatments including Er:YAG laser with different parameters on the pull-out bond strength of the fiber posts. Lasers Med Sci 29, 1569–1574 (2014). https://doi.org/10.1007/s10103-013-1485-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10103-013-1485-0

Keywords

Search

Navigation