Abstract
To obtain new information about the mechanical and physical properties of dry wood in unstable states, the influence of heating history on viscoelastic properties and dimensional changes of dry wood in the radial, tangential, and longitudinal directions was studied between 100° and 200°C. Unstable states of dry wood still existed after heating at 105°C for 30 min and were modified by activated molecular motion in the first heating process to temperatures above 105°C. This phenomenon is thought to be caused by the unstable states reappearing after wetting and drying again. Dry wood components did not completely approach the stable state in the temperature range tested, because they did not entirely surpass the glass transition temperatures in most of the temperature range. In constant temperature processes at 135° and 165°C, E′ increased and E″ decreased with time regardless of the direction. This indicated that the unstable states of dry wood components were gradually modified with time at constant temperatures. On the other hand, anisotropy of dimensional change existed and dimension increased in the longitudinal direction, was unchanged in the radial direction, and decreased in the tangential direction with time at constant temperatures.
Article PDF
Similar content being viewed by others
References
Kadita S, Yamada T, Suzuki M, Komatsu K (1961) Studies on rheological properties of wood. II. Effects of heat-treating condition on hygroscopicity and dynamic Young’s modulus of wood (in Japanese). Mokuzai Gakkaishi 7:34–38
Kubojima Y, Okano T, Ohta M (2000) Bending strength and toughness of heat-treated wood. J Wood Sci 46:8–15
Obataya E, Tanaka F, Norimoto M, Tomita B (2000) Hygroscopicity of heat-treated wood I: effects of after-treatments on the hygroscopicity of heat-treated wood (in Japanese). Mokuzai Gakkaishi 46:77–87
Ishimaru Y, Oshima K, Iida I (2001) Changes in the mechanical properties of wood during a period of moisture conditioning. J Wood Sci 47:254–261
Iida I, Kudo M, Onizuka J, Ishimaru Y, Furuta Y (2002) Stress relaxation of wood during elevating and lowering processes of temperature and the set after relaxation II: consideration of the mechanism and simulation of stress relaxation behavior using a viscoelastic model. J Wood Sci 48:119–125
Kudo M, Iida I, Ishimaru Y, Furuta Y (2003) The effect of quenching on the mechanical properties of wet wood (in Japanese). Mokuzai Gakkaishi 49:253–259
Kamei K, Ishimaru Y, Iida I, Furuta Y (2004) Effect of samples preparation methods on mechanical properties of wood I (in Japanese). Mokuzai Gakkaishi 50:10–17
Nakano T (2005) Effects of quenching on relaxation properties of wet wood. J Wood Sci 51:112–117
Kovacs AJ (1964) Transition vitreuse dans les polymères amorphes. Etude phénoménologique. Algebra Universalis 3:394–507
Struik LCE (1978) Physical aging in amorphous polymers and other materials. Elsevier, Amsterdam
Ishimaru Y (2003) Mechanical properties of wood in unstable states caused by changes in temperature and/or swelling. Proceedings of the 2nd International Conference of the European Society for Wood Mechanics, Stockholm, pp 69–78
Takahashi C, Ishimaru Y, Iida I, Furuta Y (2004) The creep of wood destabilized by change in moisture content. Part 1: the creep behaviors of wood during and immediately after drying. Holzforschung 58:261–267
Furuta Y, Soma N, Obata Y, Kanayama K (2001) Research to make better use of wood as sustainable resource — physical property change of wood due to heating and drying histories. Proceedings of the 4th International Conference on Materials for Resources, Akita, vol 2, pp 260–265
Kojiro K, Furuta Y, Ishimaru Y (2008) Effects of heating from 100°C and 200°C on dynamic viscoelastic properties of dry wood (in Japanese). J Soc Mater Sci Jpn (in press)
Kojiro K, Furuta Y, Ishimaru Y (2008) Influence of histories on dynamic viscoelastic properties and dimension of water-swollen wood. J Wood Sci doi: 10.1007/s10086-007-0926-4
Goring DAI (1963) Thermal softening of lignin, hemicellulose, and cellulose. Pulp Pap December:T517–527
Sobue N, Shibata Y, Mizusawa T (1992) X-Ray measurement of lattice strain of cellulose crystals during the shrinkage of wood in the longitudinal direction (in Japanese). Mokuzai Gakkaishi 38:336–341
Author information
Authors and Affiliations
Corresponding author
About this article
Cite this article
Kojiro, K., Furuta, Y. & Ishimaru, Y. Influence of heating history on dynamic viscoelastic properties and dimensions of dry wood. J Wood Sci 54, 196–201 (2008). https://doi.org/10.1007/s10086-007-0942-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10086-007-0942-4