Abstract
Graphene-SnS2 nanocomposites were prepared via a solvothermal method with different loading of SnS2. The nanostructure and morphology of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The XRD patterns revealed that hexagonal SnS2 was obtained. SEM and TEM results indicated that SnS2 particles distributed homogeneously on graphene sheets. The electrochemical properties of the samples as active anode materials for lithium-ion batteries were examined by constant current charge–discharge cycling. The composite with weight ratio between graphene and SnS2 of 1:4 had the highest rate capability among all the samples and its reversible capacity after 50 cycles was 351 mAh/g, which was much higher than that of the pure SnS2 (23 mAh/g). With graphene as conductive matrix, homogeneous distribution of SnS2 nanoparticles can be ensured and volume changes of the nanoparticles during the charge and discharge processes can be accomodated effectively, which results in good electrochemical performance of the composites.
Similar content being viewed by others
References
Kim HS, Chung YH, Kang SH, Sung YE (2009) Electrochim Acta 54:3606–3610
Zai JT, Wang KX, Su YZ, Qian XF, Chen JS (2011) J Power Sources 196:3650–3654
Patra CR, Odani A, Pol VG, Aurbach D, Gedanken A (2007) J Solid State Electrochem 11:186–194
Wang ZY, Chen G, Xia DG (2008) J Power Sources 184:432–436
Novoselov KS, Geim AK, Morozov SV, Jiang D, Zhang Y, Dubonos SV, Grigorieva IV, Firsov AA (2004) Science 306:666–669
Novoselov KS, Geim AK, Morozov SV, Jiang D, Katsnelson MI, Grigorieva IV, Dubonos SV, Firsov AA (2005) Nature 438:197–200
Yao J, Shen XP, Wang B, Liu HK, Wang GX (2009) Electrochem Commun 11:1849–1852
Wang XY, Zhou XF, Yao K, Zhang JG, Liu ZP (2011) Carbon 49:133–139
Wang GX, Wang B, Wang XL, Park J, Dou SX, Ahn H, Kim K (2009) J Mater Chem 19:8378–8384
Qiu DF, Xu ZJ, Zheng MB, Zhao B, Pan LJ, Pu L, Shi Y (2011) Graphene anchored with mesoporous NiO nanoplates as anode material for lithium-ion batteries. J Solid State Electrochem. doi:10.1007/s10008-011-1466-9
Du QL, Zheng MB, Zhang LF, Wang YW, Chen JH, Xue LP, Dai WJ, Ji GB, Cao JM (2010) Electrochim Acta 55:3897–3903
Hummers WS, Offeman RE (1958) J Am Chem Soc 80:1339–1339
Wu ZS, Ren WC, Wen L, Gao LB, Zhao JP, Chen ZP, Zhou GM, Li F, Cheng HM (2010) ACS Nano 4:3187–3194
Momma T, Shiraishi N, Yoshizawa A, Osaka T, Gedanken A, Zhu JJ, Sominski L (2001) J Power Sources 97–98:198–200
Kim TJ, Kim C, Son D, Choi M, Park B (2007) J Power Sources 167:529–535
Acknowledgments
This work was supported by China Postdoctoral Science Foundation (no. 20100471296), Postdoctoral Foundation of Jiangsu Province (no. 1001003C), and National Nature Science Foundation of China (nos. 60928009, 61076017, and 60990314).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Shen, C., Ma, L., Zheng, M. et al. Synthesis and electrochemical properties of graphene-SnS2 nanocomposites for lithium-ion batteries. J Solid State Electrochem 16, 1999–2004 (2012). https://doi.org/10.1007/s10008-011-1602-6
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10008-011-1602-6