Abstract
We have investigated the microdomain structure and viscoelastic properties of polystyrene-block-poly(ethylene-co-(ethylene-propylene)-block-polystyrene copolymer (SEEPS-1)/paraffinic oil (Oil-1) blends. The SAXS results revealed that, with increasing oil content, the structures change from a lammelar microdomain for SEEPS-1/Oil-1 = 100/0 to a hexagonally packed cylindrical microdomain for SEEPS-1/Oil-1 = 75/25 blend, and furthermore change to a spherical microdomain packed in a cubic lattice for SEEPS-1/Oil-1 = 50/50 and 25/75 blends. SEEPS-1/Oil-1 = 100/0 and 75/25 blends held each same microdomain structure below 300 °C. In contrast, SEEPS-1/Oil-1 = 50/50 and 25/75 blends, respectively, exhibited order-disorder transition temperature (T ODT) at 210–220 °C and 150–160 °C. Below T ODT, the microdomain structures did not change. Corresponding to the SAXS observations, the viscoelastic responses showed that the dynamic storage modulus G′, respectively, is proportional to ω1/2, ω1/4∼ω1/3, and ω0 at low frequencies for SEEPS-1/Oil-1 = 100/0, 75/25, and 50/50 and 25/75, indicating lamellar, cylindrical, and spherical microdomains The time-temperature superposition was applicable on the ordered state, and the activation energy obtained from the shift factors was roughly independent of blend composition (in other words, microdomain structure), suggesting that the viscoelastic responses are due to the presence of defects of long range order of microdomain structures.
Similar content being viewed by others
References
Bates FS (1984) Block copolymers near the microphase separation transition. 2. linear dynamic mechanical properties. Macromolecules 17:2607–2613
Balsara NP, Dai HJ, Watanabe H, Sato T, Osaki K (1996) Influence of defect density on the rheology of ordered block copolymers. Macromolecules 29:3507–3510
Chung CI, Lin MI (1978) Nature of melt rheological transition in a styrene-butadiene-styrene block copolymer. J Polym Sci: Polym Phys Ed 16:545–553
Ferry JD (1980) Viscoelastic properties of polymers, 3rd edn. Wiley, New York
Floudas G, Ulrich R, Wiesner U (1999) Microphase separation in poly(isoprene-b-ethylene oxide) diblock copolymer melts. 1. Phase state and kinetics of the order-to-order transition. J Chem Phys 110:652–662
Fredrikson GH, Bates FS (1996) Dynamics of block copolymers: theory and experiment. Annu Rev Mater Sci 26:501–550
Gouinlock EV, Porter RS (1977) Linear dynamic mechanical properties of an SBS block copolymer. Polym Eng Sci 17:534–543
Kawasaki K, Onuki A (1990) Dynamics and rheology of diblock copolymers quenched into microphase-separated states. Phys Rev A 42:3664–3666
Koppi KA, Tirrell M, Bates FS, Almdal K, Colby RH (1992) Lamellae orientation in dynamically sheared diblock copolymer melts. J Phys II (France) 2:1941–1961
Koppi KA, Tirrell M, Bates FS, Almdal K, Mortensen K (1994) Epitaxial growth and shearing of the body centered cubic phase in diblock copolymer melts. J Rheol 38:999–1027
Kossuth MB, Morse DC, Bates FS (1999) Viscoelastic behavior of cubic phases in block copolymer melts. J Rheol 43:167–196
Larson RG, Winey KI, Patel SS, Watanabe H, Bruinsma R (1993) The rheology of layered liquids: lammelar block copolymers and smectic liquid crystals. Rheol Acta 32:245–253
Larson RG (1999) The structure and rheology of complex fluids. Oxford University Press, New York
Morrison FA, Winter HH (1989) Effect of unidirectional shear on the structure of triblock copolymers. 1. Polystyrene-polybutadiene-polystyrene. Macromolecules 22:3533–3540
Morrison FA, Winter HH, Gronski W, Barnes JD (1990) Effect of unidirectional shear on the structure of triblock copolymers. 2. polystyrene-polyisoprene-polystyrene. Macromolecules 23:4200–4205
Mortensen K, Almdal K, Kleppinger R, Mischenko N, Reynaers H (1998) Networks of gel-forming triblock copolymers solutions: in situ SANS and rheological measurements. Physica B 241-243:1025–1028
Mortensen K, Theunissen E, Kleppinger R, Almdal K, Reynaers H (2002) Shear-induced morphologies of cubic ordered block copolymer micellar networks studied by in situ small-angle neutron scattering and rheology. Macromolecules 35:7773–7781
Nishioka A, Aoki Y, Suzuki T, Ishigami A, Endo T, Koda T, Koyama K (2011) Dynamic mechanical properties of polystyrene-block-poly[ethylene-co-(ethylene-propylene)]-block polystylene triblock copolymer/hydrocarbon oil blends. J Appl Polym Sci 121:3001–3006
Patel SS, Larson RG, Winey KI, Watanabe H (1995) Shear orientation and rheology of a lamellar polystyrene-polyisoprene block copolymer. Macromolecules 28:4313–4318
Rosedale JH, Bates FS (1990) Rheology of ordered and disordered symmetric poly(ethylenepropylene)-poly(ethylethylne) diblock copolymers. Macromolecules 23:2329–2338
Rubinstein M, Obukhov SP (1993) Power-law-like stress relaxation of block copolymers: disentanglement regimes. Macromolecules 26:1740–1750
Ryu CY, Lee MS, Hajduk DA, Lodge TP (1997) Structure and viscoelasticity of matched asymmetric diblock and triblock copolymers in the cylinder and sphere microstructures. J Polym Sci Part B: Polym Phys 35:2811–2823
Sakamoto N, Hashimoto T, Han CD, Kim D, Vaidya NY (1997) Effect of addition of a neutral solvent on the order-order and order-disorder transitions in a polystyrene-block-polyisoprene-block-polystyrene copolymer. Macromolecules 30:5321–5330
Sugimoto M, Sakai K, Aoki Y, Taniguchi T, Koyama K (2009) Rheology and morphology change with temperature of SEBS/hydrocarbon oil blends. J Polym Sci Part B: Polym Phys 47:955–965
Takahashi R, Nishioka A, Ishigami A, Suzuki T, Nishitsuji S, Koda T, Aoki Y (2012) Rheology of polystyrene-block-poly[ethylene-co-(ethylene-propylene)]- block-polystyrene triblock copolymer/paraffinic oil blends - effect of oil molecular weight on the order-disorder transition -. Nihon Reoroji Gakkaishi (J Soc Rheol Jpn) 40:171–177
Wang H, Newstein MC, Krishnan A, Balsara NP, Garetz BA, Hammouda B, Krishnamoorti R (1999) Ordering kinetics and alignment of block copolymer lamellae under shear flow. Macromolecules 32:3639–3711
Watanabe H, Kotaka T, Hashimoto T, Shibayama M, Kawai H (1982) Rheological and morphological behavior of styrene-butadiene diblock copolymer solutions in selective solvents. J Rheol 26:153–179
Winter HH, Scott DB, Gronski W, Okamoto S, Hashimoto T (1993) Ordering by flow near the disorder-order transition of a triblock copolymer styrene-isoprene-styrene. Macromolecules 26:7236–7244
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Aoki, Y., Takahashi, R., Nishitsuji, S. et al. Viscoelasticity and morphology of polystyrene-block-poly[ethylene-co-(ethylene-propylene)]-block-polystyrene tri-block copolymer/paraffinic oil blends. 1. Effect of oil content. Rheol Acta 55, 293–301 (2016). https://doi.org/10.1007/s00397-016-0917-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00397-016-0917-8