The quantities of deposited carbon were measured and the quality of the nanotubes was characterized by means of transmission electron microscopy and scanning tunneling microscopy. The inner and outer diameters of the nanotubes were also measured and the diameter distribution histograms were established. The multi-wall straight and coiled nanotubes were found to be quite regular with an average inner (outer) diameter of 4–7 nm (15–25 nm) and with lengths up to 50 μm. The walls contain concentric cylindrical graphene sheets separated by the graphitic interlayer distance. The single-wall nanotubes were found as bundles of hundreds of aligned straight 1-nm-diameter nanotubes with lengths up to 1-μm.
The influence of various parameters such as the method of catalyst preparation, the nature and the pore size of the support, the nature of the metal, the quantity of catalyst active particles, and the reaction conditions on the nanotubes formation were studied. The numbers and dimensions of the catalyst active particles dispersed on the support were found to be of importance in regulating the shape of the produced nanotubes. Following these results, a model of growth mechanism was suggested for the nanotubes obtained by this method.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 5 January 1998
Rights and permissions
About this article
Cite this article
Fonseca, A., Hernadi, K., Piedigrosso, P. et al. Synthesis of single- and multi-wall carbon nanotubes over supported catalysts . Appl Phys A 67, 11–22 (1998). https://doi.org/10.1007/s003390050732
Issue Date:
DOI: https://doi.org/10.1007/s003390050732