Abstract
The new mixed compound Tl1.89K0.11(SO4)0.9(SeO4)0.1Te(OH)6 which is crystallized in the monoclinic system with space group P21/c was analyzed at room temperature using X-ray diffractometer data. The unit cell parameters are a = 12.3308(7), b = 7.2011(4), c = 12.0298(8) Å, β = 110.755(4)°, V = 998.87(11) Å3 and Z = 4. The final refinement led to R = 0.035 and Rw = 0.038. The main feature of these atomic arrangements is the coexistence of three and different anions (SO4 2−, SeO4 2− and TeO6 6− groups) in the unit cell, connected by hydrogen bonds (O–H···O) which make the building of the crystal. The Tl+ and K+ cations, occupying the same positions, are located between these polyhedral. The crystals of Tl1.89K0.11(SO4)0.9(SeO4)0.1Te(OH)6 underwent three endothermic peaks at 377, 466 and 472 K. These transitions were detected by DSC and analyzed by dielectric measurements using the impedance and modulus spectroscopy techniques. The IR and Raman spectra recorded at room temperature in the frequency ranges (50–1200) and (400–4000) cm−1, respectively, have confirmed the presence of TeO6 6−, SO4 2− and SeO4 2− groups in the crystal.
Similar content being viewed by others
References
K. Jaoudi, N. Zouari, T. Mhiri, A. Daoud, M. Jannin, J. Alloy Compd. 413, 46–53 (2006)
K. Jaoudi, N. Zouari, T. Mhiri, M. Giorgi, Phase Transit. 78, 627–638 (2005)
H. Khemakhem, Ferroelectrics 234, 47–59 (1999)
R. Zilber, A. Durif, M.T. Averbuch-Pouchot, Acta Crystallogr. B 36, 2743–2745 (1980)
R. Zilber, A. Durif, M.T. Averbuch-Pouchot, Acta Crystallogr. B 37, 650–652 (1981)
R. Zilber, A. Durif, M.T. Averbuch-Pouchot, Acta Crystallogr. B 38, 1554–1556 (1982)
M. Dammak, H. Khemakhem, T. Mhiri, A.W. Kolsi, A. Daoud, J. Alloys Compd. 280, 107–113 (1998)
M. Dammak, H. Khemakhem, T. Mhiri, J. Phys. Chem. Solids 62, 2069–2074 (2001)
M. Abdelhedi, M. Dammak, A.W. Kolsi, A. Cousson, Anal. Sci. X-ray Struct. Anal. Online 24, 93–94 (2008)
M. Abdelhedi, L. Ktari, M. Dammak, A. Cousson, A.W. Kolsi, Acta Crystallogr. E63, 153–154 (2007)
Nonius, in Kappa CCD Sever Software, ed. by B.V. Nonius (Delft, 1999)
APEX2 version 1. 0–8, Bruker AXS (Madison, WI, 2003)
D.J. Watkin, C.K. Prout, J.R. Carruthers, P.W. Betteridge, R.I. Cooper, Crystals Issue 11 (Chemical Crystallography Laboratory, Oxford, 2001)
K. Brandenburg, M. Berndt, DIAMOND Version 2.1.b, Crystal Impact, Gb R (Bonn, 1999)
A. Novak, Hydrogen Bonding in Solids, vol. 18 (Springer, Berlin, 1974), pp. 177–216
J. Faby, J. Loub, L. Feltl, J. Therm. Anal. 24, 95–100 (1982)
L. Ktari, M. Dammak, A.W. Kolsi, A. Cousson, J. Alloys Compd. 476, 54–59 (2009)
H. Litaiem, M. Dammak, L. Ktari, S. Kammoun, T. Mhiri, Phase Transit. 77, 929–940 (2004)
M. Djemel, M. Abdelhedi, L. Ktari, M. Dammak, J. Mol. Struct. 1047, 15–21 (2013)
M. Abdelhedi, M. Dammak, A.W. Kolsi, J. Chem. Crystallogr. 45, 257–265 (2015)
M. Dammak, H. Khemakhem, N. Zouari, A.W. Kolsi, T. Mhiri, J. Solid State Ion. 127, 125–132 (2000)
A. Orilukas, A. Dindune, Z. Kanepe, J. Ronis, E. Kazakevicius, A. Kezionis, Solid State Ion. 157, 177–181 (2003)
H. Kchaou, A.B. Rhaiem, K. Karoui, F. Jomni, K. Guidara, Appl. Phys. A 122, 82–89 (2016)
N. Chabchoub, H. Khemakhem, M. Gargouri, J. Alloys Compd. 359, 84–90 (2003)
S.G. Gauthier, J.C. Peuzin, M. Olivier, G. Rolland, Ferroelectrics 52, 293–306 (1984)
H. Khemakhem, J. Ravez, A. Daoud, Ferroelectrics 188, 41–51 (1996)
H. Khemakhem, R. Von der Muhll, J. Ravez, A. Daoud, Ferroelectrics 188, 85–93 (1996)
M. Djemel, M. Abdelhedi, N. Zouari, M. Dammak, A.W. Kolsi, J. Solid State Chem. 196, 267–273 (2012)
M. Dammak, H. Khemakhem, T. Mhiri, A.W. Kolsi, A. Daoud, J. Solid State Chem. 145, 612–618 (1999)
M. Dammak, H. Litaiem, P. Gravereau, T. Mhiri, A.W. Kolsi, J. Alloys Compd. 442, 316–319 (2007)
N. Zouari, M.B. Amor, T. Mhiri, A. Daoud, J.M. Réau, J. Alloys Compd. 240, 70–75 (1996)
D.C. Sinclair, A.R. West, J. Appl. Phys. 66, 3850–3856 (1989)
I.M. Hodge, M.D. Ingram, Q.A.R. West, J. Electroanal. Chem. Interfacial Electrochem. 74, 125–143 (1976)
S. Sen, P. Pramanik, R.N.P. Choudhary, Appl. Phys. A Mater. Sci. Process. 82, 549–557 (2006)
J.M. Reau, A. Simon, M. El Omari, J. Ravez, J. Eur. Ceram. Soc. 19, 777–779 (1999)
F.S. Howell, R.A. Bose, P.B. Macedo, C.T. Moynihan, J. Phys. Chem. 78, 639–648 (1974)
S.W. Martin, Appl. Phys. A 49, 239–247 (1989)
H.K. Palet, S.W. Martin, Phys. Rev. B 45, 10292–10300 (1992)
L. Ktari, M. Dammak, A. Hadrich, A. Cousson, M. Nierlich, F. Romain, T. Mhiri, J. Solid State Sci. 6, 1393–1401 (2004)
R. Allman, W. Hasse, Inorg. Chem. 15, 804–807 (1976)
G. Blasse, W. Hordijk, J. Solid State Chem. 15, 395–409 (1972)
M. Gargouri, T. Mhiri, A. Daoud, J.M. Reau, Solid State Ion. 125, 193–202 (1999)
K. Viswanathan, V.U. Nayar, G. Aruldhas, Infrared Phys. 26, 89–91 (1986)
G. Sekar, K. Viswanathan, G. Aruldhas, Infrared Phys. 27, 253–256 (1987)
G. Sekar, G. Aruldhas, Infrared Phys. 27, 371–374 (1987)
K. Viswanathan, V.U. Nayar, G. Aruldhas, V. Ramakrishnan, J. Solid State Chem. 77, 394–400 (1988)
M. Dammak, A. Hadrich, T. Mhiri, J. Alloys Compd. 428, 8–16 (2007)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Elferjani, A., Abdelhedi, M., Dammak, M. et al. Structural, dielectric and vibrational studies of the new mixed solid solution of thallium potassium sulfate selenate tellurate. Appl. Phys. A 122, 742 (2016). https://doi.org/10.1007/s00339-016-0266-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-016-0266-6