Pressure-controlled preparation of nanocrystalline complex oxides using pulsed-laser ablation at room temperature

Abstract.

Nanocrystalline thin films of complex oxides such as BaTiO₃ and LaFeO₃ were prepared by pulsed laser ablation without substrate heating. Targets under various Ar pressures were irradiated using an ArF excimer laser. The off-axis configuration of targets and substrates was used to synthesize the films. The crystallinity and chemical composition of the deposited films were strongly dependent on the processing Ar gas pressure. In case of BaTiO₃, the film deposited at 10 Pa was a single phase of BaTiO₃ with a crystallite size around 7.2 nm. With increasing Ar pressure to 200 Pa, XRD peaks of BaTiO₃ as well as BaCO₃ were observed. The by-products could be due to reaction with carbon dioxide in air after taking the sample out of the chamber. For LaFeO₃, the films deposited under 50 to 200 Pa had a single phase with a crystallite size below 10 nm. When the Ar pressure exceeded 100 Pa, the crystallite size tended to decrease for both BaTiO₃ and LaFeO₃, which could be due to formation of aggregated nanoparticles. Below 10 Pa, oxygen deficiency was observed. Over 50 Pa, the atomic concentration of all the constituent elements was almost constant, especially the [Ba]/[Ti] and [La]/[Fe] ratios, which were nearly unity.