Summary
A series of superabsorbent composites containing Montmorillonite (MMT), modified- Montmorillonite (OMMT) and sodium acrylate were synthesized by free-radical polymerization in aqueous solution. The structure of composites was characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM) and X-ray diffraction (XRD), and the results showed that the polymer chains were grafted onto the edge and the surface of MMT or OMMT. At the same time, the equilibrium swelling ratio of the composites was investigated as a function of the clay content and the results showed that the equilibrium swelling ratio of composites was improved by the introduction of clay. The maximum equilibrium swelling ratio of composite in distilled water and 0.9 wt% sodium chloride solutions were up to 2450 g/g and 118 g/g, respectively. Finally, the result of thermogravimetric analysis (TGA) suggested that the introduction of clay and modified clay could improve the thermal stability of superabsorbent composites.
Similar content being viewed by others
References
Yao KJ, Zhou WJ. J Appl Polym Sci 1994; 53:1533–1538.
Zhou WJ, Yao KJ, Kurth MJ. J Appl Polym Sci 1996; 62:911–915.
Tsubakimoto T, Shimomura T, Kobabyashi H. Jpn Patent 1987; 62, 149, 335.
Miura Y, Hirano K, Nate T, Kambayashi T, Ohtsuka M, Nagai T. Eur Patent 1991; 440, 256.
Tanaka H, Kambayashi T, Sugiyama Y, Nagai T, Nagata K, Kubota K, Hirano K. Eur Patent 1992; 501, 482.
Clarence O. Walker, Richmond , Texaco Inc, White Plains,. US Patent 1987; 4(664):816.
Colombo P. Adv Drug Delivery Rev 1993; 11:37–57.
Dong LC, Hoffman AS. J Control Release 1991; 15:141–152.
Ende M, Hariharan D, Pappas NA. React Polym 1995; 25:127–137.
US Department of Agriculture. US Patent 1961; 3, 981, 100.
J.H. Wu. Y.L. Wei. J.M. Lin. S.B. Lin. Polym. Inter. 2003; 52:1909–1912.
J.H. Wu. J.M. Lin. M. Zhou. C.C. Wei. Macromol. Rapid. Commun. 2000; 21:1032–1034.
J.M. Lin. J.H. Wu. Z.F. Yang. M.L. Pu. Macromol. Rapid. Commun. 2001; 22:422–424.
K. Kabiri. M.J. Zohuriaan-Mehr. Polym. Adv. Tech. 2003; 14:438–444.
W.F. Lee. L.G. Yang. J. Appl. Polym. Sci. 2004: 92:3422–3429.
J.H. Wu. Y.L. Wei. J.M. Lin. S.B. Lin. Polymer 2003; 44:6513–6520.
W.F. Lee. C.C. Yung. J. Appl. Polym. Sci. 2004; 94:2417–2424.
D.Y. Gao. R.B. Heimann. M.C. Williams. L.T. Wardhavgh. M. Mvhammad. J. Mater. Sci. 1999; 34:1542–1543.
Z.H. Huang. K.Y. Qiu. Polymer 1997; 38:521–526.
Kourosh Kabiri, M. J. Zohuriaan-Mehr, polymer adv tech, 2003; 14:438–444.
X.L. Lu. Y.L. Mi. Macromolecules 2005; 38:839–843.
H. Ye. J.Q. Zhao. Y.H. Zhang. J. Appl. Polym. Sci. 2004; 91:936–940.
S.D. Burnside. E.P. Giannelis. Chem. Mater. 1995: 7:1597–1600.
Jiang GL, Zhang PP. 2005, Chemical Industry press, p96
Boyd SA, Lee J-F and Mortland MM. 1988. Nature, 333:345–347
Jeannine E. Elliott, Mara Macdonald, Jun Nie and Christopher N. Bowman , Polymer 2004; 45:1503–1510.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Su, X., Zhang, G., Xu, K. et al. The Effect of MMT/Modified MMT on the Structure and Performance of the Superabsorbent Composite. Polym. Bull. 60, 69–78 (2008). https://doi.org/10.1007/s00289-007-0843-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-007-0843-0