Influence of printing parameters on structures, mechanical properties and surface characterization of aluminium alloy manufactured using selective laser melting

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

The selective laser melting (SLM) technology, a 3D printing method, has been gaining more attraction recently due to its ability to fabricate highly complex and intricate featured medical, aerospace, automotive components. The extensive use of SLM in recent years has been augmented by readily available processing materials and distinct product features such as enhanced surface properties and improved mechanical strength of the printed products. This paper investigated the effects of support structures, building direction and post-processing on mechanical properties, surface roughness and microscopic analysis of parts printed by SLM. Support structures are required during the SLM printing process. It is desired to optimize the support structures, as this increases printing time and material consumption and reduces surface finish. Finite element analysis has been carried out prior to metal printing to optimize the support structure. It was found that the spider-cone line support shows efficient structure for this study. The mechanical properties of the fabricated specimen were studied, and experimental results were validated and compared with conventionally machined specimen. It was observed that the SLM printed parts have 20% increment in tensile strength as compared with conventionally cast specimen. However, the percent of elongation is low for SLM specimen due to large number of pores and un-melted powder presented in the printed part. In this study, the SLM specimens were subjected to heat treatment at the temperature of 550 °C for 2 h in order to achieve increment or optimal mechanical properties. The heat treatment demonstrated a 2-fold increment in elongation, as compared with the SLM as printed specimen. The present study is also aimed at evaluating the surface roughness of SLM printed specimen. It was observed that the surface roughness of SLM specimen ranged between ~ 0.3 and 3 μm. This demonstrated that SLM process is capable of providing the good surface quality component and considered an alternative process to conventional manufacturing process. The morphological studies have been carried out to support the results derived from the evaluation of mechanical properties and surface roughness. The morphological behaviour clearly shows the large pores and un-melted particles in fractured specimen. The results revealed that the support structure, build direction, orientation, surface finish and post-processing are important parameters to build a part using SLM effectively and efficiently.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. Thijs L, Kempen K, Kruth JP, Van Humbeeck J (2013) Fine-structured aluminium products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder. Acta Mater 61(5):1809–1819

    Article  Google Scholar 

  2. Yan C, Hao L, Hussein A, Bubb SL, Young P, Raymont D (2014) Evaluation of light-weight AlSi10Mg periodic cellular lattice structures fabricated via direct metal laser sintering. J Mater Process Technol 214(4):856–864

    Article  Google Scholar 

  3. Read N, Wang W, Essa K, Attallah MM (2015) Selective laser melting of AlSi10Mg alloy: process optimisation and mechanical properties development. Mater Des (1980-2015) 65:417–424

    Article  Google Scholar 

  4. Olakanmi EO (2013) Selective laser sintering/melting (SLS/SLM) of pure Al, Al–Mg, and Al–Si powders: effect of processing conditions and powder properties. J Mater Process Technol 213(8):1387–1405

    Article  Google Scholar 

  5. Wang L, Jiang X, Zhu Y, Zhu X, Sun J, Yan B (2018) An approach to predict the residual stress and distortion during the selective laser melting of AlSi10Mg parts. Int J Adv Manuf Technol 97(9–12):3535–3546

    Article  Google Scholar 

  6. Liu YJ, Liu Z, Jiang Y, Wang GW, Yang Y, Zhang LC (2018) Gradient in microstructure and mechanical property of selective laser melted AlSi10Mg. J Alloys Compd 735:1414–1421

    Article  Google Scholar 

  7. Kempen K, Thijs L, Van Humbeeck J, Kruth JP (2012) Mechanical properties of AlSi10Mg produced by selective laser melting. Phys Procedia 39:439–446

    Article  Google Scholar 

  8. Brandl E, Heckenberger U, Holzinger V, Buchbinder D (2012) Additive manufactured AlSi10Mg samples using selective laser melting (SLM): microstructure, high cycle fatigue, and fracture behavior. Mater Des 34:159–169

    Article  Google Scholar 

  9. Kempen K, Thijs L, Van Humbeeck J, Kruth JP (2015) Processing AlSi10Mg by selective laser melting: parameter optimisation and material characterisation. Mater Sci Technol 31(8):917–923

    Article  Google Scholar 

  10. Buchbinder D, Schleifenbaum HB, Heidrich S, Meiners W, Bültmann J (2011) High power selective laser melting (HP SLM) of aluminum parts. Phys Procedia 12:271–278

    Article  Google Scholar 

  11. Watkins KG, McMahon MA, Steen WM (1997) Microstructure and corrosion properties of laser surface processed aluminium alloys: a review. Mater Sci Eng A 231(1–2):55–61

    Article  Google Scholar 

  12. Wong TT, Liang GY, Tang CY (1997) The surface character and substructure of aluminium alloys by laser-melting treatment. J Mater Process Technol 66(1–3):172–178

    Article  Google Scholar 

  13. Dinda GP, Dasgupta AK, Mazumder J (2012) Evolution of microstructure in laser deposited Al–11.28% Si alloy. Surf Coat Technol 206(8–9):2152–2160

    Article  Google Scholar 

  14. Rosenthal I, Stern A, Frage N (2014) Microstructure and mechanical properties of AlSi10Mg parts produced by the laser beam additive manufacturing (AM) technology. Metallography, Microstructure, and Analysis 3(6):448–453

    Article  Google Scholar 

  15. Yi H, Qi L, Luo J, Zhang D, Li H, Hou X (2018) Effect of the surface morphology of solidified droplet on remelting between neighboring aluminum droplets. Int J Mach Tools Manuf 130:1–11

    Article  Google Scholar 

  16. Yi H, Qi L, Luo J, Li N (2019) Hole-defects in soluble core assisted aluminum droplet printing: metallurgical mechanisms and elimination methods. Appl Therm Eng 148:1183–1193

    Article  Google Scholar 

  17. Yi H, Qi LH, Luo J, Jiang Y, Deng W (2016) Pinhole formation from liquid metal microdroplets impact on solid surfaces. Appl Phys Lett 108(4):041601

    Article  Google Scholar 

  18. Calignano F, Manfredi D, Ambrosio EP, Iuliano L, Fino P (2013) Influence of process parameters on surface roughness of aluminum parts produced by DMLS. Int J Adv Manuf Technol 67(9–12):2743–2751

    Article  Google Scholar 

  19. Calignano F, Lorusso M, Pakkanen J, Trevisan F, Ambrosio EP, Manfredi D, Fino P (2017) Investigation of accuracy and dimensional limits of part produced in aluminum alloy by selective laser melting. Int J Adv Manuf Technol 88(1–4):451–458

    Article  Google Scholar 

  20. Delgado J, Ciurana J, Rodríguez CA (2012) Influence of process parameters on part quality and mechanical properties for DMLS and SLM with iron-based materials. Int J Adv Manuf Technol 60(5–8):601–610

    Article  Google Scholar 

  21. Qattawi A, Castañón MAG (2018) Effect of manufacturing parameters on the microstructure and mechanical properties of metal laser sintering parts of precipitate hardenable metals. Int J Adv Manuf Technol 99(9–12):2491–2507

    Google Scholar 

  22. Boschetto A, Bottini L, Veniali F (2018) Surface roughness and radiusing of Ti6Al4V selective laser melting-manufactured parts conditioned by barrel finishing. Int J Adv Manuf Technol 94(5–8):2773–2790

    Article  Google Scholar 

  23. Jhabvala J, Boillat E, André C, Glardon R (2012) An innovative method to build support structures with a pulsed laser in the selective laser melting process. Int J Adv Manuf Technol 59(1–4):137–142

    Article  Google Scholar 

  24. Rios CO, Amine T, Newkirk JW (2018) Tensile behavior in selective laser melting. Int J Adv Manuf Technol 96(1–4):1187–1194

    Article  Google Scholar 

  25. Prashanth KG, Scudino S, Klauss HJ, Surreddi KB, Löber L, Wang Z, Eckert J (2014) Microstructure and mechanical properties of Al–12Si produced by selective laser melting: effect of heat treatment. Mater Sci Eng A 590:153–160

    Article  Google Scholar 

  26. Vojtech D, Serak J, Ekrt O (2004) Improving the casting properties of high-strength aluminium alloys. Mater Technol 38(1/2):99–102

    Google Scholar 

  27. Kammer C (2009) “Aluminium Taschenbuch 1, Grundlagen und Werkstoffe”, 16. überarbeiteteAuflage. Aluminium-Verlag Marketing &Kommunikation GmbH, Düsseldorf 978-3870172923

    Google Scholar 

  28. Aboulkhair NT, Everitt NM, Ashcroft I, Tuck C (2014) Reducing porosity in AlSi10Mg parts processed by selective laser melting. Addit Manuf 1:77–86

    Google Scholar 

  29. Louvis E, Fox P, Sutcliffe CJ (2011) Selective laser melting of aluminium components. J Mater Process Technol 211(2):275–284

    Article  Google Scholar 

  30. Gong H, Rafi K, Starr T, Stucker B (2013) The effects of processing parameters on defect regularity in Ti-6Al-4V parts fabricated by selective laser melting and electron beam melting. In24th Annual International Solid Freeform Fabrication Symposium—An Additive Manufacturing Conference, Austin, TX, pp 12–14

Download references

Author information

Authors and Affiliations

  1. Institute of Plastics Technology (IPT), Central Institute of Plastics Engineering and Technology (CIPET), Lucknow, 226008, India

    Rajkumar Subbiah, Joseph Bensingh, Abdul Kader & Sanjay Nayak

Authors
  1. Rajkumar Subbiah
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Joseph Bensingh
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Abdul Kader
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sanjay Nayak
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Rajkumar Subbiah.

Additional information

Publisher’s note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Subbiah, R., Bensingh, J., Kader, A. et al. Influence of printing parameters on structures, mechanical properties and surface characterization of aluminium alloy manufactured using selective laser melting. Int J Adv Manuf Technol 106, 5137–5147 (2020). https://doi.org/10.1007/s00170-020-04929-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-020-04929-3

Keywords

Search

Navigation