Shear modulus, internal bond and density profile of medium density fibre board (MDF)

Abstract

For five different types of Medium Density Fibreboard (MDF) the correlation between in-plane shear properties (interlaminar shear, standard method prEN 789 Appendix B), internal bond and parameters derived from the density profile were determined. There are high correlations between interlaminar shear modulus (G _xz, G_yz), shear strength and internal bond (IB) as well as between mean density and internal bond, shear modulus and shear strength. A correlation between the failure position and parameters derived from the density profile could not be established. 69% of the failures were found in the outer layers of the specimens (15–35% and 65–85% of thickness, respectively), even if the lowest density was found in the core layer. Failures in the centre of the specimens were found only when the lowest density was less than 30% of the mean density.

Zusammenfassung

Für fünf verschiedene Typen mitteldichter Faserplatten (MDF) wurde der Zusammenhang zwischen dem Schubmodul in Plattenebene, getestet nach prEN 789 Anhang B, der Querzugfestigkeit und charakteristischen Werten des Dichteprofils untersucht. Für das untersuchte Material besteht eine hohe Korrelation zwischen Schubmodul (G _xz G_yz), Schubfestigkeit und Querzugfestigkeit. Ein hoher Zusammenhang liegt auch zwischen der mittleren Dichte, der Querzugfestigkeit und den Schubeigenschaften vor. Keiner der herangezogenen charakteristischen Werte des Dichteprofils besitzt einen Zusammenhang zur Bruchposition der geprüften Proben. Beim Querzugtest waren 69% aller Brüche in einem Bereich von 15–35% bzw. 65–85% der Plattendicke zu finden. In diesen Bereichen war der Bruch auch zu finden, wenn die minimale Dichte deutlich in Plattenmitte lag. Brüche in der Mittellage der Proben konnten nur festgestellt werden, wenn die minimale Dichte mehr als 30% von der mittleren Dichte abwich.