Abstract
In an earlier publication, [1] the occurrence of shrinkage porosity was described by a simple “geometric” model, which was based primarily on experimental data available for low-carbon steel alloys. In this publication, the predictions of the “geometric” model are compared to experimental data for long freezing range alloys. The comparison and a theoretical analysis show that the earlier results do not apply to the solidification of these alloys. A dimensionless group has been developed to characterize the freezing range, the original “geometric” model has been modified, and a new analysis is presented to characterize shrinkage porosity formation in long freezing range alloys.
Similar content being viewed by others
References
G.K. Sigworth and C. Wang:Metall. Trans. B, 1993, vol. 24B, pp. 349–64.
M.C. Flemings:Solidification Processing, McGraw-Hill, New York, NY, 1974, pp. 12 and 146–54.
E. Niyama, T. Uchida, M. Morikawa, and S. Saito:AFS Int. Cast Met. J., 1982, vol. 7 (3), pp. 52–63.
K. Kubo and R.D. Pehlke:Metall. Trans. B, 1985, vol. 16B, pp. 359–66.
V. de L. Davies:AFS Cast Met. Res. J., 1975, vol. 11, pp. 33–44.
R.A. Flinn:AFS Trans., 1956, vol. 64, pp. 665–67.
W. Michels and S. Engler:Giessereiforschung, 1989, vol. 41, pp. 174–87.
Q.T. Fang and D.A. Granger:AFS Trans., 1989, vol. 97, pp. 989–1000.
Y.W. Lee, E. Chang, and C.F. Chieu:Metall. Trans. B, 1990, vol. 21B, pp. 715–22.
W.S. Pellini:AFS Trans., 1953, vol. 61, pp. 61–80.
P.K. Trojan and R.A. Flinn:AFS Trans., 1957, vol. 65, pp. 238–46.
W.H. Johnson, H.F. Bishop, and W.S. Pellini:AFS Trans., 1955, vol. 63, pp. 345–52.
W.H. Johnson, H.F. Bishop, and W.S. Pellini:Foundry, 1955, November, pp. 120–27.
S. Viswanathan: Ph.D. Thesis, University of Pittsburgh, Pittsburgh, PA, 1990.
W.H. Johnson and J.G. Kura:AFS Trans., 1959, vol. 67, pp. 535–52.
M.V. Chamberlin and J.G. Mezoff:AFS Trans., 1946, vol. 54, pp. 648–62.
D.R. Irani and V. Kondic:AFS Trans., 1969, vol. 77, pp. 208–11.
L. Backerud, G. Chai, and J. Tamminen:Solidification Characteristics of Aluminum Alloys, AFS, Des Plaines, IL, 1990, pp. 67 and 131.
S. Ganeson, R. Speiser, and D.R. Poirier:Metall. Trans. B, 1987, vol. 18B, pp. 421–24.
S. Ganesan and D.R. Poirier:Metall. Trans. A, 1987, vol. 18A, pp. 721–23.
D.R. Poirier:Metall. Trans. B, 1987, vol. 18B, pp. 245–55.
A. Mortensen, V.J. Michaud, J.A. Cornie, M.C. Flemings, and L. Masur: inCast Metal Reinforced Metal Composites, ASM, Metals Park, OH, 1989, pp. 7–13.
A. Mortensen and J.A. Cornie:Metall. Trans. A, 1987, vol. 18A, pp. 1160–63.
G. Chai, T. Rolland, L. Amberg, and L. Backerud:Proc. 2nd Int. Conf. on Semi-Solid Processing of Alloys and Composites, MIT, Cambridge, MA, June 10–12, 1992, pp. 193–201.
L. Backerud and G. Chai: University of Stockholm, Stockholm, Sweden, private communication, 1991.
C.Y. Liu, K. Murakami, and T. Okamoto:Acta Metall., 1986, vol. 34, pp. 159–66.
J.T. Berry and T. Watmough:AFS Trans., 1961, vol. 69, pp. 11–22.
S. Engler and L. Henrichs:Aluminium, 1972, vol. 48, pp. 351–56.
L. Backerud, E. Kroll, and J. Tamminen:Solidification Characteristics of Aluminum Alloys, Universitetsforlaget, Oslo, 1986, p. 144.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sigworth, G.K., Wang, C. Evolution of porosity in long freezing range alloys. Metall Trans B 24, 365–377 (1993). https://doi.org/10.1007/BF02659139
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02659139