Abstract
The effect of hot-rolling texture on the plastic strain ratio of a continuously cast low-carbon steel and a vacuum-melted low-carbon iron has been investigated as a function of the temperature of hot rolling. Normal cold rolling and a simulated box anneal, in dry hydrogen to decarburize, were employed subsequently. The microstructure and texture at every stage of the process was examined, and the plastic strain ratio (R value) of the final strip was determined. Results indicate that •R varies strongly with the hot-rolling temperature. OptimumR values were obtained when the hot-rolling temperature was 925° to 950°C.
Similar content being viewed by others
References
W. T. Unkford, S. C. Snyder, and J. A. Bauscher:Trans. ASM, 1950, vol. 42, pp. 1197–1225.
R. S. Burns and R. H. Heyer:Sheet Metal Ind., 1958, vol. 35, pp. 261–75.
R. D. Hindson:Proc. International Symposium on the Annealing of Low Carbon Steel, pp. 9–17, Lee Wilson Eng. Co., Cleveland, Ohio, 1958.
R. L. Whiteley and D. E. Wise:Flat Rolled Products III, pp. 47–63, Interscience, N.Y., 1962.
H. Yoshida, K. Sasaki, and F. Kansaki:Colloquium on Anisotropy and Tensile Test Properties and Their Relationship to Sheet Metal Forming, IDDRG., London, 1964.
S. R. Goodman and H. Hu: U. S. Patent 3,404,047, October, 1968.
H. Kubotera and K. Nakaoka: Mechanical Working and Steel Processing VI, Met. Soc. AIME 10th Conf., Chicago, 1967.
H. Takechi, H. Kato, and S. Nagashima:Trans. TMS-AIME, 1968, vol. 242, pp. 56–65.
M. Fukuda:Trans. Iron Steel Inst. Japan, 1968, vol. 8, pp. 68–77.
C. A. Stickels:Trans. TMS-AIME, 1965, vol. 233, pp. 1550–58.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Goodman, S.R., Hu, H. Effect of hot-rolling texture on the plastic strain ratio of low-carbon steels. Metall Trans 1, 1629–1640 (1970). https://doi.org/10.1007/BF02642010
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02642010