Structural effects on the thermal properties of PDPS/PDMS copolymers

Abstract

A series of PDPS/PDMS copolymers were synthesized through living anionic polymerization withn-butyllithium as an initiator. The changes of thermal property as a function of PDPS content were compared with respect to different types of monomer sequence using differential scanning calorimetry and thermogravimtery. The results indicated that the related variations of the thermal propertiesvs. the PDPS content and the monomer sequence provided independent operative control for preparing materials with desired thermal properties. The thermal stability of these copolymers was dramatically improved with introducing PDPS segment. However, the degree of these improvement pedended greatly on the monomer sequence in the copolymers.

Zusammenfassung

Mittels stöchiometrischer anionischer Polymerisation mit n-Butyllithium als Initiator wurde eine Reihe von PDPS/PDMS Kopolymeren hergestellt. Im Hinblick auf die verschiedenen Arten von Monomersequenzen wurden mittels DSC und TG die Änderungen der thermischen Eigenschaften als eine Funktion des PDPS-Gehaltes untersucht. Die Ergebnisse zeigen, daß die Änderung der thermischen Eigenschaften in Abhängigkeit von PDPS-Gehalt und Monomersequenz eine unabhängige operative Kontrolle zur Herstellung von Materialien mit den gew=:unschten thermischen Eigenschaften bietet. Die thermische Stabilität dieser Kopolymere wird durch Einbringen von PDPS-Segmenten sehr stark verbessert. Das Ausmaß dieser Verbesserung hängt jedoch stark von der Monomersequenz innerhalb des Kopolymers ab.