Abstract
A new degradation function of the friction coefficient is used. Based on the double shear-lag model and Paris formula, the interfacial damage of coated-fiber-reinforced composites under tension-tension cyclic loading is studied. The effects of strength and thickness of the coating materials on the debond stress, debond rate as well as debond length are simulated.
Similar content being viewed by others
References
Hsueh CH. Interfacial debonding and fiber pull-out stresses of fiber-reinforced composites, X: with an elastic interfacial coating.Materials Science and Engineering, 1993, A165: 189–195
Kakavas PA, Anifantis NK, Baxevanakis K, Katsareas DE, Papanicolaou GC. The effect of interfacial imperfections on the micromechanical stress and strain distribution in fiber reinforced composites.Journal of Meterials Science, 1995, 30(18): 4541–4548
Pagano NJ. On the micromechnical failure modes in a class of ideal brittle matrix composites, Part 1: coated-fiber composites.Composites Part B, 1998, 29B: 93–119
Majumdar BS, Newaz GM. Constituent damage mechanisms in metal matrix composites under fatigue loading and their effect on fatigue life.Materials Science and Engineering, 1995, A200: 114–129
Suo SQ, Kagawa Y, Bobet JL, Mauda C. Fatigue damage evolution in SiC fiber-reinforced Ti-15-3 alloy matrix composite.Materials Science and Engineering 1996, A220: 57–68
Zhou LM, Kim JK, Mai YW. Micromechanical characterization of fiber/matrix interfaces.Composites Science and Technology, 1993, 48: 227–236
Walls DP, Zok FW. Iterfacial fatigue in a fiber reinforced metal matrix composite.Acta Metall Mater, 1994, 42(8): 2675–2681
Gao YC, Zhou LM. Analysis on interface damage of fiber reinforced composites under cyclic load.Theory and Applied Fracture Mechanics, 1997, 28: 29–39
Shi ZF, Zhou LM. Modeling of fiber-matrix composite under cyclic loading. In: Sih GC ed. Mesomechanics 2000, Proceeding of an International Conference of Role of Mechanics for Development of Science and Technology, Xi'an, 2000-06-13-16. Beijing: Tsinghua University Press, 2000, 1075–1082
Lu GY, Mai YW. Effect of plastic coating on fiber-matrix interface debonding.Journal of Materials Science, 1995, 30(23): 5872–5878
Author information
Authors and Affiliations
Additional information
The subject supported by the National Natural Science Foundation of China (No.59778034), Teaching and Research Award Program for Outstanding Young Teachers in Higher Education Institutions of MOE, China and The Hong Kong Polytechnic University (G-S737)
Rights and permissions
About this article
Cite this article
Zhifei, S., Limin, Z. Interfacial debonding of coated-fiber-reinforced composites under tension-tension cyclic loading. Acta Mech Sinica 16, 347–356 (2000). https://doi.org/10.1007/BF02487687
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02487687