Abstract
206Po was implanted into iron at T<0.2 K. After electron capture decay to206Bi nuclear magnetic resonance of oriented206BiFe was observed with an asymmetric resonance line shape. Evaluation of the data with the superposition of two Gaussian lines results in ν=693.7(2) MHz for the center frequency of the narrow one of the two lines at external field zero. From this Bhf (BiFe)=119.0(1.3) T is derived. The effective spin-lattice relaxation time of206BiFe at T=13 mK was measured as Ti=0.94(5) s.
Similar content being viewed by others
References
P. Herzog, H.-R. Folle, K. Freitag, M. Reuschenbach and H.U. Schmidt, Phys. Lett. 62A(1977)245.
P. Herzog, H. Walitzki, K. Freitag, H. Hildebrand and K. Schlösser, Z.Phys. A311(1983)351.
P.K. James, P. Herzog, N.J. Stone and K. Freitag, Phys.Rev. B13(1976)59.
M. Hansen, Constitution of Binary Alloys (McGraw-Hill, New York, 1958) p. 309.
F. Bacon, H. Haas, G. Kaindl and H.-E. Mahnke, Phys.Lett. 38A(1972)401.
M. Kaplan, P.D. Johnston, P. Kittel and N.J. Stone, Phys.Lett. 41A(1972)315,
M. Kaplan, P.D. Johnston, P. Kittel and N.J. Stone, Nucl.Phys. A212(1973)478.
P.D. Johnston, M. Kaplan, and N.J. Stone, Phys.Rev.Lett. 32(1974)784.
P.R.H. McConnel, P.W. Martin and B.G. Turrell, Can.J.Phys. 55(1977)456.
P. Herzog, H.-R. Folle, K. Freitag, A. Kluge, M. Reuschenbach and E. Bodenstedt, Nucl.Instr. 155(1978)421.
I. Lindgren and C.M. Johansson, Arkiv Fysik 15(1959)445.
E. Hagn, K. Leuthold, E. Zech and H. Ernst, Z.Phys. A295(1980)385.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Herzog, P., Freitag, K., Herrmann, C. et al. NMR/ON of206BiFe produced by decay of cold implanted206Po. Hyperfine Interact 15, 329–332 (1983). https://doi.org/10.1007/BF02159767
Issue Date:
DOI: https://doi.org/10.1007/BF02159767