Summary
Theoretical investigation was attempted for the dielectric crystalline dispersion which is observed at high temperatures in highly crystallized polymer samples such as polypropylene and oxidized polyethylene. The dielectric dispersion of this kind had been confirmed experimentally to come from the crystalline part, but no theoretical investigation had been reported for this dielectric dispersion.
The proposed mechanism was such that this dielectric dispersion is attributed to the dipole polarization due to torsional and longitudinal motions of skeletal chains in polymer crystallites. On the basis of such a mechanism, the expression of the complex dielectric constant was calculated by solving theBoltzmann equation for the motion of the skeletal chain. The magnitude of the absorption, its temperature dependence and the shape of the absorption curve were derived from the complex dielectric constant. The activation energy was also calculated by the use of Fröhlich's method.
The agreement between the theoretical results and the observed data seems quantitatively good, which seems to show the appropriateness of the present mechanism for the dielectric dispersion of this sort. The observed data up to date are, however, given as the tan δ vs. temperature curve, in which might be included in the effect of the structural alteration such as the recrystallization. The observation by varying the frequency at constant temperatures seems to be desirable for being compared with the present theory.
Zusammenfassung
Diese theoretische Untersuchung wurde für dielektrische Dispersion im Kristallinen, beobachtet bei hohen Temperaturen, in hochkristallisierten Polymerproben wie Propylen und oxydiertes Polyäthylen durchgeführt. Die dielektrische Dispersion dieser Art wurde als vom kristallinen Teil herrührend experimentell gesichert, doch gibt es bisher noch keine theoretische Untersuchung darüber.
Als Mechanismus wurde vorgeschlagen, daß diese dielektrische Dispersion einer Dipolpolarisation gehörig zu longitudinalen und tordierenden Bewegungen der Skelettketten in den polymeren Kristallen gehört. Auf Grundlage dieses Mechanismus wurde die komplexe Dielektrizitätskonstante durch Lösung derBoltzmann-Gleichung für die Bewegung der Skelettkette berechnet. Die Größe der Absorption, ihre Temperaturabhängigkeit und die Gestalt der Absorptionskuve wurden aus der komplexen Dielektrizitätskonstante abgeleitet. Die Aktivierungsenergie wurde ebenfalls nach der Methode vonFröhlich berechnet.
Die Übereinstimmung zwischen theoretischen Ergebnissen und den Beobachtungen scheint quantitativ gut. Das dürfte zeigen, daß der Mechanismus der dielektrischen Dispersion tatsächlich von dieser Art ist. Die bisherigen Beobachtungsdaten geben jedoch tgδ als Funktion der Temperatur, so daß Strukturänderungen wie z. B. solche durch Rekristallisation eingeschlossen sind. Untersuchungen beiVariation der Frequenz und konstanten Temperaturen wären zum Vergleich mit der vorgelegten Theorie erwünscht.
Similar content being viewed by others
References
An example of the theories of the dielectric αa-dispersion is given byKirkwood, J. E. andR. M. Fuoss, J. Chem. Phys.9, 329 (1941).
Yamafuji, K., J. Phys. Soc. Japan15, 2295 (1960).
Yamafuji, K. andY. Ishida, Kolloid-Z. u. Z. Polymere183, 15 (1962).
Saito, N., K. Okano, S. Iwayanagi andT. Hideshima, Molecular Motion in Solid State Polymer in; Solid State Physics (edited by F. Seitz and D. Turnbull) (Vol. 14).
Oakes, W. G. andD. W. Robinson, J. Polymer Sci.14, 505 (1954).
Mikhailov, G. K., Zhur. Fiz.27, 2050 (1957).
Okamoto, S. andK. Takeuchi, J. phys. Soc. Japan14, 378 (1959).
Krämer, H. andK. E. Helf, Kolloid-Z. u. Z. Polymere180, 114 (1962).
Krum, F., Kolloid-Z.165, 77 (1959).
Slichter, W. P., J. Appl. Phys.32, 2339 (1961).
Peterlin, A., J. Appl. Phys.31, 1934 (1960);Peterlin, A. andE. W. Fischer, Z. Physik159, 272 (1960);Peterlin, A., E. W. Fischer andChr Reinhold, J. Chem. Phys.37, 1403 (1962).
Rempel, R. C., H. E. Weaver, R. H. Sands andR. L. Miller, J. Appl. Phys.28, 1082 (1957).
Glasstone, S., K. J. Laidler andH. Eyring, The Theory of Rate Process (New York 1941).
Gross, E. P., Phys. Rev.97, 395 (1955).
Fröhlich, H., Proc. Phys. Soc.54, 422 (1942).
Natta, G., J. Polymer Sci.16, 143 (1955).
Onsager, L., J. Amer. Chem. Soc.58, 1486 (1936).
Ishida, Y. (private communications).
Chandrasekhar, S., Rev. Mod. Phys.15, 1 (1943).
Urey, H. C. andC. A. Bradley, Phys. Rev.38, 1969 (1931).
Szigeti, B., Trans. Faraday Soc.48, 400 (1952).
Shimanouchi, T. andS. Mizushima, J. Chem. Phys.23, 707 (1955).
Tadokoro, H. (private communications).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yamafuji, K. Theory of dielectric crystalline dispersion in high polymers. Kolloid-Z.u.Z.Polymere 195, 111–122 (1964). https://doi.org/10.1007/BF01503658
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01503658