The behaviour of fracture mode and intermediate temperature embrittlement of ferritic spheroidal graphite cast iron is influenced by many factors. From the experimental results, intermediate temperature embrittlement can be considered to be dominated by dynamic strain ageing and the triaxial stress field developed in the ferrite matrix amongst the graphite particles. In order to understand the effect of dynamic strain ageing on high-temperature properties, tensile properties, push-pull low-cycle fatigue properties, rotary bending fatigue properties and creep-rupture properties were investigated from room temperature to 500° C. It was found that all the properties investigated were influenced by dynamic strain ageing. The intermediate temperature embrittlement of ferritic spheroidal graphite cast iron found in different load conditions is reported.
Similar content being viewed by others
References
K. Chichiwa andM. Hayashi,Imono 51 (7) (1979) 395.
E. NECHTELBERGER, “Fachverlag Schiele und Schon Gmbh, Berlin, (1977) p. 442.
T. S. Lui andO. Yanagisawa,J. Foundry Ind. Taiwan 36 (9) (1985) 1.
O. Yanagisawa andT. S. Lui,Metall. Trans. A 16A (1985) 667.
S. Rigger, O. Vohringer andE. Macherauch,Gieserei Forsch. 23 (1971) 35.
J. S. Blackwore andE. O. Hall:Iron Steel Inst. 8 (1966) 817.
T. S. Lui, Proceedings of the 2nd ROC-ROK Joint Workshop on Fracture of Metals (Tsing Hua University, Hsinchu, Taiwan, 1986) p. 297.
T. Takeyama andH. Takahashi,Tetsu to Hagane 58 (1972) 1054.
T. Sakii, M. Ohashi, M. Kozai andS. Sakui,ibid. 63 (1977) 124.
O. Yanagisawa andT. S. Lui,Trans. Jpn Inst. Metals 12 (1983) 858.
C. E. Jaske,Trans. ASME (1977) 432.
M. Omori, Y. Yoshinaga andT. Kawahata,Jpn Inst. Metals 33 (1969) 730.
A. K. Sachdev,Met. Trans. 13A (1982) 1793.
M. Abe,Jpn Inst. Metals 45 (1981) 942.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lui, T.S., Chao, C.G. High-temperature properties of ferritic spheroidal graphite cast iron. J Mater Sci 24, 2503–2507 (1989). https://doi.org/10.1007/BF01174520
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01174520