The crack-sized c and the strength distributions of structural ceramics after non-destructive inspection (NDI) were analysed by supposing penny-shaped cracks to be inner cracks. The theoretical crack-size distribution function after NDI coincides well with the experimental data for a three-point bending test of HP-Si3N4 in the regiond c > 30μm. The distribution function of the fracture strength calculated from the crack-size data after NDI coincides well with the experimental data.
Similar content being viewed by others
References
Y. Matsuo andK. Kitakami,J. Jpn Soc. Mech. Eng. 51 (1985) 2575.
Idem, in “Fracture Mechanics of Ceramics”, Vol. 7, edited by Bradtet al. (Plenum Press, 1986) pp. 223–236.
H. L. Oh andI. Finnie,Int. J. Fract. Mech. 6 (1970) 287.
S. M. Wiederhorn, in “Fracture Mechanics of Ceramics”, Vol. 2, edited by Bradtet al. (Plenum Press, 1974) pp. 613–646.
Y. Matsuo,J. Soc. Mater. Sci. Jpn 33 (1984) 857.
S. Ito, S. Sakai andM. Ito,ibid. 30 (1981) 1019.
Y. Matsuo, K. Kitakami andS. Kimura,Yogyo Kyokai-shi 94(8) (1986) 711.
H. Murata, Y. Matsuo, M. Miyakawa andK. Kitakami,J. Jpn Soc. Mech. Eng. 52 473(A), (1986) 27–34.
K. Kitakami andY. Matsuo,J. Soc. Mater. Sci. Jpn 34 (1985) 1466.
E. L. Kaplan andP. Meier,Amer. Stat. Ass. J. 53 (1958) 457.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Matsuo, Y., Kitakami, K. & Kimura, S. Crack size and strength distribution of structural ceramics after non-destructive inspection. J Mater Sci 22, 2253–2256 (1987). https://doi.org/10.1007/BF01132968
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01132968