Preparation of rod-shaped BaTiO₃ powder

Abstract

Rod-shaped BaTiO₃ powder particles have been prepared from rod-shaped TiO₂ ·nH₂O and BaCO₃ in molten chloride. The morphology of BaTiO₃ particles was studied referring to the effects of the chemical species of the starting titanium compound, amount of chloride, particle size of the titanium compound and reaction conditions, and the preparation condition of rod-shaped BaTiO₃ has been determined: i.e., large TiO₂ ·nH₂O particles were heated at 700°C in molten salt with an equal amount of BaTiO₃. This condition was effective in suppressing the formation of BaTiO₃ by a solution-precipitation process as well as the deformation of either TiO₂ ·nH₂O or BaTiO₃, which are responsible for the formation of equiaxed BaTiO₃ particles. The obtained rod-shaped BaTiO₃ particles had a cubic symmetry. Electron diffraction analysis showed that the following topotactic relation is retained; 〈0 1 0〉_{potassium tetratitanate} ∥ 〈0 1 0〉_{hydrated titania} ∥ 〈1 0 0〉_anatase ∥ 〈1 0 0〉_{barium titanate}