Abstract
The formation of a superlattice in theα-phase of Cu-12.4wt% Al alloy was studied during cooling. Specimens cooled at different rates were examined using electron microscopy and differential thermal analysis. The superlattice structure formed was described by means of theD-parameter which determines the position of superspots in the reciprocal lattice. Variation of theD-parameter with cooling rate has a linear form, hence it may be concluded that the superlattice in theα-phase is formed as a transitional structure. The relationship between theD-parameter and enthalpy suggests that the latter can be taken as a measure of superstructure development.
Similar content being viewed by others
References
R. P. Jewett andD. J. Mack,J. Inst. Metals 83 (1963/64) 59.
W. Gaudig andH. Warlimont,Z. Metallkde 60 (1969) 488.
Idem, Acta Metall. 26 (1978) 709.
A. Varschavsky andE. Donoso,Metall. Trans. 14 (1983) 875.
C. R. Brooks andE. Stransbury,Acta Metall. 11 (1963) 1303.
J. Popplewell andJ. Crane,Met. Trans. 2 (1971) 3411.
L. Clarebrough, M. Howgraves andM. Lorretto,Proc. Roy. Soc. A261 (1960) 500.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lelatko, J., Kwarciak, J., Bojarski, Z. et al. The effect of cooling rate on α-phase ordering in Cu-12.4wt% Al alloy. J Mater Sci 20, 3529–3534 (1985). https://doi.org/10.1007/BF01113759
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01113759