Summary
The titanium-silver phase diagram was investigated over the concentration range from 20 to 100 at. % Ag by means of metallographic, thermal, and x-ray diffraction analyses. It was confirmed that the system contains two intermediate phases,η andγ. The phases are based on the compounds TiAg andTi2Ag, which are isostructural with the compounds TiCu and Ti2Cu. The temperatures of nonvariant transformations were determined, and the character of the transformation taking place in the silver-rich alloys was established.
Similar content being viewed by others
Literature cited
F. Laves and H. J. Wallbaum, Naturwissenschaften,27, No. 40, 674 (1939).
E. Raub, P. Walter, and M. Engel, Z. Metallk.,43, No. 4, 112 (1952).
R. J. van Thyne, W. Rostoker, and H. D. Kessler, J. Metals,5, No. 5, 670 (1959).
N. A. De Cecco and M. J. Parks, Welding J.,32, No. 11, 1071 (1953).
H. K. Adenstedt and W. R. Freeman, Wright Air Develop. Center Res. Rept., Part 1, 53 (1953).
H. K. Worner, J. Inst. Metals,82, No. 5, 222 (1954).
T. Morinaga, J. Miura, and T. Takagdi, J. Japan Inst. Met.,23, No. 2, 117 (1952).
M. K. McQuillan, J. Inst. Metals,88, No. 5, 235 (1960).
R. Reinbach and F. Fischmann, Z. Metallk.,54, No. 5, 314(1963).
K. Schubert, Z. Metallk.,56, No. 3, 197 (1965).
G. Shinoda and H. Kawabe, Electron Microprobe, John Wiley and Sons, New York-London-Sydney (1966), p. 503.
Author information
Authors and Affiliations
Additional information
Translated from Poroshkovaya Metallurgiya, No. 7 (79), pp. 55–59, July, 1969.
Rights and permissions
About this article
Cite this article
Eremenko, V.N., Buyanov, Y.I. & Panchenko, N.M. Constitution diagram of the system titanium-silver. Powder Metall Met Ceram 8, 562–566 (1969). https://doi.org/10.1007/BF00775520
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00775520