Force modulation microscopy (FMM) is used to characterize the external surface and internal fracture surface morphologies of three different block copolymer samples. A roll-cast poly(styrene-butadiene-styrene) triblock copolymer film, spin-coated poly(styrene-b-methyl methacrylate) thin films, and an ultrathin poly(styrene-b-hexyl isocyanate) rod-coil block copolymer film were investigated. For each sample, height and elasticity images were obtained for the same areas allowing direct comparison. The elasticity images obtained using force modulation microscopy were independent of surface roughness and found to exhibit better contrast and spatial resolution of the respective block copolymer domains than the height images. The lateral resolution of the elasticity images was sufficient to show microphase separated domains having length scales as small as about 10 nm. The poly(styrene-b-methyl methacrylate) samples demonstrate that FMM can even be successfully used to study block copolymers in which both blocks are glassy under the conditions of measurement.
Similar content being viewed by others
References
E. L. THOMAS, in “The Encyclopedia of Polymer Science and Engineering”, Vol. 5, edited by J. I. Kroschwitz (John Wiley, New York, 1986) p. 644.
D. L. VEZIE, E. L. THOMAS and W. W. ADAMS,Polymer 36 (1995) 1761.
D. W. SCHWARK, D. L. VEZIE, J. R. REFFNER, E. L. THOMAS and B. K. ANNIS,J. Mater. Sci. Lett. 11 (1992) 352.
B. K. ANNIS, D. L. SCHWARK, J. R. REFFNER, E. L. THOMAS and B. WUNDERLICH,Makromol. Chem. 193 (1992) 2589.
B. COLLIN, D. CHATENAY, G. COULON, D. AUSSERRE and Y. GALLOT,Macromolecules 25 (1992) 1621.
J. FROMMER,Angew. Chem. Int. Ed. Engl. 31 (1992) 1298.
P. MAIVALD, H. J. BUTT, S. A. C. GOULD, C. B. PRATER, B. DRAKE, J. A. GURLEY, V. B. ELINGS and P. K. HANSMA,Nanotechnology 2 (1991) 103.
M. RADMACHER, R. W. TILLMANN, M. FRITZ and H. E. GAUB,Science 257 (1992) 1900.
M. RADMACHER, R. W. TILLMANN and H. E. GAUB,Biophys. J. 64 (1993) 735.
E.-L. FLORIN, M. RADMACHER, B. FLECK and H. E. GAUB,Rev. Sci. Instrum. 65 (1994) 639.
R. M. OVERNEY, T. BONNER, E. MEYER, M. RUETSCHI, R. LUTHI, L. HOWALD, J. FROMMER, H.-J. GUNTHERODT, M. FUJIHARA and H. TAKANO,J. Vac. Sci. Technol. B 12 (1994) 1973.
T. KAJIYAMA, K. TANAKA, I. OHKI, S.-R. GE, J.-S. YOON and A. TAKAHARA,Macromolecules 27 (1994) 7932.
R. M. OVERNEY, E. MEYER, J. FROMMER, H.-J. GUNTHERODT, M. FUJIHARA, H. TAKANO and Y. GOTOH,Langmuir 10 (1994) 1281.
G. BINNIG, C. F. QUATE and C. GERBER,Phys. Rev. Lett. 56 (1986) 930.
Digital Instruments, Inc. Nanoscope III Command Reference Manual, Version 3.0 (December 21, 1993) p. 35.
J. B. PETHICA and W. C. OLIVER,Physica Scripta T19 (1987) 61.
R. J. ALBALAK and E. L. THOMAS,J. Polym. Sci. Polym. Phys. Edn 31 (1993) 37.
Idem., ibid. 32 (1994) 341.
J. T. CHEN, E. L. THOMAS, C. K. OBER and S. S. HWANG,Macromolecules 28 (1995) 1688.
R. J. ALBALAK, unpublished work.
Idem., Polymer 35 (1994) 4115.
B. MAXWELL,J. Polym. Sci. 20 (1956) 551.
W. LETHERSICH,Brit. J. Appl. Phys. 1 (1950) 294.
H. WRIGHT, C. S. N. FARADAY, E. F. T. WHITE and L. R. G. TRELOAR,J. Phys. D: Appl. Phys. 4 (1971) 2002.
C. CRETON, E. J. KRAMER, C.-Y. HUI and H. R. BROWN,Macromolecules 25 (1992) 3075.
G. COULON, T. P. RUSSELL, V. R. DELINE and P. F. GREEN,ibid. 22 (1989) 2581.
T. P. RUSSELL, A. M. MAYES and M. S. KUNZ,“Ordering in macromolecular systems”, edited by A. Teramoto, M. Kobayashi and T. Norisuje (Springer-Verlag, Berlin, 1994) p. 217.
M. N. BERGER,J. Macromol. Sci.-Revs. Macromol. Chem. C9 (1973) 269.
A. I. BUR and L. I. FETTERS,Chem. Revs. 76 (1976) 727.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chen, J.T., Thomas, E.L. The use of force modulation microscopy to investigate block copolymer morphology. J Mater Sci 31, 2531–2538 (1996). https://doi.org/10.1007/BF00687278
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00687278