Abstract
The shear strength (τ) of overlap shear test pieces made by solid state diffusion bonding or by machining thin (2.5 or 4 mm thick) Al-Li 8090 alloy sheet has been determined for various overlap lengths (/). When / < 3 mm, τ was independent of / and equal to 188 to 202 MPa for the bonded joint and 199 to 209 MPa for the base metal sheet. The lower mean shear strength of the bonded joint was caused by the lower resistance of intergranular fracture in the planar grain boundary at the bond interface. The bond strengths were, however, greater than those previously reported for joints in 8090 alloy made by solid-state or liquid-phase diffusion bonding and about a factor of 7 greater than those for adhesive bonded joints.
Similar content being viewed by others
References
H. E. Friedrich, R. Furlan andM. Kullick, in “Superplasticity and Superplastic Forming” edited by C. H. Hamilton and N. F. Paton (TMS, 1988) p. 649.
D. Stephen, “Designing with Titanium” (Institute of Metals, London, 1986) p. 108.
P. G. Partridge, J. Harvey andD. V. Dunford, AGARD Conference on Advanced Joining of Aerospace Metallic Materials, No. 398 September 1985, p. 8–1.
D. V. Dunford andP. G. Partridge, in “Proceedings of the International Symposium on Superplasticity in Aerospace — Aluminium”, Cranfield, UK (SIS, Cranfield 1985) p. 257.
P. G. Partridge, AGARD Lecture Series on Superplasticity, No. 154, September 1987, p. 5–1.
J. Pilling andN. Ridley,Mater. Sci. Engng 3 (1987) 353.
T. D. Byun andP. Yavari, “Welding Bonding and Fastening”, NASA Publication 2387 (NASA, 1984) p. 23.
J. Kennedy, in “Superplasticity and Superplastic Forming”, edited by C. H. Hamilton and N. F. Paton (TMS, 1988) p. 523.
P. G. Partridge andD. V. Dunford,J. Mater. Sci. 22 (1987) 1597.
C. J. Peel, B. Evans andD. S. McDarmaid,Metals Mater. August (1987) 449.
P. G. Partridge, International Materials Review, 1990, Vol. 35, No. 1, p. 37.
J. Pilling, in “Superplasticity and Superplastic Forming”, edited by C. H. Hamilton and N. F. Paton (TMS, 1988) 475.
M. R. Edwards, E. Klinklin andV. E. Stoneham, “Weldability of Aluminium — Lithium Alloys”, RMCS Technical Note MTG 1450/7 Final Report, June 1989.
E. R. Maddrell, R. A. Ricks andE. R. Wallach, in “5th International Conference on Al-Li Alloys”, edited by T. H. Sanders and E. A. Starke (Materials and Component Engineering, Publications Ltd, Birmingham, 1989) p. 451.
R. A. Ricks, P. J. Winkler, H. Stoklossa andR. Grimes,ibid. P. 441.
D. V. Dunford andP. G. Partridge,J. Mater. Sci. (1990) in press.
Idem, to be published.
J. Harvey, P. G. Partridge andC. L. Snooke,J. Mater. Sci. 20 (1985) 1009.
A. J. Kinloch,ibid. 17 (1982) 617.
L. J. Hart-Smith, “Delamination and Debonding of Materials” ASTM STP 876 (American Society for Testing and Materials, Philadelphia, Pennsylvania, 1985) p. 238.
D. J. Arrowsmith, A. W. Clifford, D. A. Moth andR. J. Davies, in “3rd International Conference on Al-Li Alloys”, (Institute of Metals, London, 1986) p. 143.
ASM, “Source Book on Selection and Fabrication of Aluminium Alloys” (ASM, 1978) p. 1.
D. Dew-Hughes, E. Creed andW. S. Miller,Mater. Sci. Tech. 4 (1988) 106.
K. T. V. Rao, W. Yu andR. O. Ritchie,Met. Trans. 19A (1988) 549.
W. S. Miller, M. D. Thomas, D. J. Lloyd andD. Creber, in “3rd International Conference on Al-Li Alloys” (Institute of Metals, London, 1986) p. 584.
A. F. Smith, AGARD Conference Proceedings No. 444, New Light Alloys (1988) p. 19.
K. V. Jata andE. A. Starke,Scripta Metall. 22 (1988) 1553.
D. V. Dunford, C. G. Gilmore andP. G. Partridge, in “Proceedings of International Conference on Diffusion Bonding”, Cranfield, UK (SIS, Cranfield, 1987) p. 143.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dunford, D.V., Partridge, P.G. Strength and fracture behaviour of diffusion-bonded joints in Al-Li (8090) alloy. J Mater Sci 25, 4957–4964 (1990). https://doi.org/10.1007/BF00580113
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00580113