Abstract
The crystallographic and microstructural parameters of plasma sprayed pure zirconia powders were studied by X-ray and neutron powder diffraction. A significant influence of the flow rate of the quenching gas on the phase composition (the tetragonal to monoclinic ratio varied between 0.6 and 3.5) and on the micro-structure was observed, while structural parameters of both phases of all investigated samples remained essentially unchanged and were close to those reported in the literature. These results do not support the concept of a critical particle size effect as a stabilizing factor for the tetragonal phase. A transition from a tetragonal to a monoclinic phase was observed without any measurable change in the crystallite sizes by heating at 845‡C. A very high background on the neutron powder patterns may have been caused by the presence of pores in the samples.
Similar content being viewed by others
References
R. C. Garvie, J. Phys. Chem. 82 (1978) 218.
R. Srinivasan, L. Rice and B. H. Davis, J. Amer. Ceram. Soc. 73 (1990) 3528.
E. D. Morgan, Comm. Amer. Ceram. Soc. 67 (1984) 204.
“Advances in ceramics, vol. 12, science and technology of ZrO2, II”, edited by N. Claussen, M. Rühle and A.H. Heuer (The American Ceramic Society, Columbus, OH, 1984).
G. Teufer, Acta Crystallog. 15 (1962) 1187.
J. D. McCullough and K. N. Trueblood, Acta Crystallog. 12 (1959) 507.
D. K. Smith and H. W. Newkirk, Acta Crystallog. 18 (1965) 983.
C. J. Howard, R. J. Hill and B. E. Reichert, Acta Crystallog. B44 (1988) 116.
L. Lutterotti and P. Scardi, J. Appl. Crystallog. 23 (1990) 246.
F. Frey, H. Boysen and T. Vogt, Acta Crystallog. B46 (1990) 724.
H. Boysen, F. Frey and T. Vogt, Acta Crystallog. B47 (1991) 881.
j. p. grabis, j. k. vaivads, A. A. bernans and t. n. millers, Izv. AN Latv. SSR, Ser. khim. 131 (1981) (in Russian).
I. V. Uvarova, D. S. Arensburger, G. A. Bokan, Z. A. Vasilevskaia and Z. A. Vitijaz, Poroshkovaja metalurgija 219 (1981) 60 (in Russian).
“GSAS generalized structure analysis”, edited by A. C. LARSON and R. B. VON DREELE (Los Alamos National Laboratory, 1988).
P. Thompson, D. E. Cox and J. B. Hastings, J. Appl. Crystallog. 20 (1987) 79.
W. I. F. David, J. Appl. Crystallog. 19 (1986) 63.
G. Caglioti, A. Paoletti and F. P. Ricci, Nucl. Instrum. Methods 35 (1958) 223.
Th. De Keijser, J. I. Langford, E. J. Mittemeijer and A. B. P. Vogels, J. Appl. Crystallog. 15 (1982) 308.
J. I. Langford, J. Appl. Crystallog. 11 (1978) 10.
B. E. Warren and B. L. Averbach, J. Appl. Phys. 2 (1950) 89.
P. A. Evans, R. Stivens and J. G. P. Binner, Br. Ceram. Trans. J. 83 (1984) 39.
J. Adam and M. D. Rogers, Acta Crystallog. 12 (1959) 951.
R. Srinivasan, B. H. Davis, B. H. Cavin and C. R. Hubbard, J. Amer. Ceram. Soc. 75 (1992) 1217.
w. lengauer and p. ettmayer, High temperature — high pressure (1990) 13.
H. Boysen, J. Appl. Crystallog. 18 (1985) 320.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bondars, B., Heidemane, G., Grabis, J. et al. Powder diffraction investigations of plasma sprayed zirconia. Journal of Materials Science 30, 1621–1625 (1995). https://doi.org/10.1007/BF00375275
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00375275